- W3048997225 abstract "The influence of post-heat-treatment on the resulting microstructure and room-temperature fracture toughness (KIC) of Inconel 718 fabricated by laser solid forming (LSF), a kind of laser based directed-energy-deposition additive manufacturing technologies, is investigated. Detailed microstructure characterization was performed on as-fabricated and heat-treated samples using direct aging (DA), solution treatment plus aging (STA), homogenization plus STA (HSTA), respectively. The results indicate that as-fabricated sample mainly consists of γ columnar dendrites and a small quantity of (γ+Laves) eutectics in the interdendritic areas. After DA post-heat-treatment, the nonuniform γ′′/γ′ precipitates exist around Laves phases. After STA post-heat-treatment, the short-acicular δ-phases precipitate around/in the Laves phases, the micro-segregation reduces and the distribution of γ′′/γ′ precipitates in the dendrite arm is almost homogeneous. After HSTA post-heat-treatment, Laves phase mostly disappears, micro-segregation completely removes and the γ′′/γ′ precipitates (~30 nm) are distributed in bimodal recrystallized grains. The results of KIC testing indicate that as-fabricated sample possesses the lowest KIC mainly due to its lowest elastic modulus and yield strength. However, the KIC of DA sample (~89.8 MPam) is close to that of as-fabricated sample, mainly due to its low ductility and strain-hardening exponent. But, the KIC of STA and HSTA samples increases by ~55.8% and 90.8% compared with as-fabricated sample respectively, mainly because of the better performance in strength–plasticity of HSTA sample (~1114 MPa, ~26.1%). Particularly, the KIC of HSTA sample with bimodal grains is ~60 MPam higher than the lower limit of wrought IN718 (AMS 5662) and reaches ~164.1 MPam. There exists significant difference in the KIC fractographs of as-fabricated and heat-treated samples. Overall, this research illustrates that an appropriate post-heat-treatment possesses obvious toughening effect on the LSF Inconel 718 alloy." @default.
- W3048997225 created "2020-08-21" @default.
- W3048997225 creator A5001411043 @default.
- W3048997225 creator A5008175321 @default.
- W3048997225 creator A5013508138 @default.
- W3048997225 creator A5033064156 @default.
- W3048997225 creator A5033653310 @default.
- W3048997225 creator A5045099503 @default.
- W3048997225 creator A5051655382 @default.
- W3048997225 creator A5080669118 @default.
- W3048997225 date "2020-11-01" @default.
- W3048997225 modified "2023-10-15" @default.
- W3048997225 title "Influence of post-heat-treatment on the microstructure and fracture toughness properties of Inconel 718 fabricated with laser directed energy deposition additive manufacturing" @default.
- W3048997225 cites W1971091168 @default.
- W3048997225 cites W1986910123 @default.
- W3048997225 cites W1990559858 @default.
- W3048997225 cites W1994262782 @default.
- W3048997225 cites W2001507300 @default.
- W3048997225 cites W2004509699 @default.
- W3048997225 cites W2005070418 @default.
- W3048997225 cites W2011003161 @default.
- W3048997225 cites W2038751166 @default.
- W3048997225 cites W2062230795 @default.
- W3048997225 cites W2073528382 @default.
- W3048997225 cites W2074722818 @default.
- W3048997225 cites W2078790099 @default.
- W3048997225 cites W2089249846 @default.
- W3048997225 cites W2096331626 @default.
- W3048997225 cites W2326777963 @default.
- W3048997225 cites W2395360105 @default.
- W3048997225 cites W2408860057 @default.
- W3048997225 cites W2467559060 @default.
- W3048997225 cites W2503161491 @default.
- W3048997225 cites W2575378483 @default.
- W3048997225 cites W2608478959 @default.
- W3048997225 cites W2724418474 @default.
- W3048997225 cites W2759175412 @default.
- W3048997225 cites W2762367303 @default.
- W3048997225 cites W2766150348 @default.
- W3048997225 cites W2772221289 @default.
- W3048997225 cites W2774139035 @default.
- W3048997225 cites W2886436362 @default.
- W3048997225 cites W2897423593 @default.
- W3048997225 cites W2921054435 @default.
- W3048997225 cites W2945613921 @default.
- W3048997225 cites W643489657 @default.
- W3048997225 doi "https://doi.org/10.1016/j.msea.2020.140092" @default.
- W3048997225 hasPublicationYear "2020" @default.
- W3048997225 type Work @default.
- W3048997225 sameAs 3048997225 @default.
- W3048997225 citedByCount "59" @default.
- W3048997225 countsByYear W30489972252021 @default.
- W3048997225 countsByYear W30489972252022 @default.
- W3048997225 countsByYear W30489972252023 @default.
- W3048997225 crossrefType "journal-article" @default.
- W3048997225 hasAuthorship W3048997225A5001411043 @default.
- W3048997225 hasAuthorship W3048997225A5008175321 @default.
- W3048997225 hasAuthorship W3048997225A5013508138 @default.
- W3048997225 hasAuthorship W3048997225A5033064156 @default.
- W3048997225 hasAuthorship W3048997225A5033653310 @default.
- W3048997225 hasAuthorship W3048997225A5045099503 @default.
- W3048997225 hasAuthorship W3048997225A5051655382 @default.
- W3048997225 hasAuthorship W3048997225A5080669118 @default.
- W3048997225 hasConcept C159985019 @default.
- W3048997225 hasConcept C18168003 @default.
- W3048997225 hasConcept C191897082 @default.
- W3048997225 hasConcept C192562407 @default.
- W3048997225 hasConcept C27501479 @default.
- W3048997225 hasConcept C2776878729 @default.
- W3048997225 hasConcept C2778703219 @default.
- W3048997225 hasConcept C2780026712 @default.
- W3048997225 hasConcept C87976508 @default.
- W3048997225 hasConcept C97549433 @default.
- W3048997225 hasConceptScore W3048997225C159985019 @default.
- W3048997225 hasConceptScore W3048997225C18168003 @default.
- W3048997225 hasConceptScore W3048997225C191897082 @default.
- W3048997225 hasConceptScore W3048997225C192562407 @default.
- W3048997225 hasConceptScore W3048997225C27501479 @default.
- W3048997225 hasConceptScore W3048997225C2776878729 @default.
- W3048997225 hasConceptScore W3048997225C2778703219 @default.
- W3048997225 hasConceptScore W3048997225C2780026712 @default.
- W3048997225 hasConceptScore W3048997225C87976508 @default.
- W3048997225 hasConceptScore W3048997225C97549433 @default.
- W3048997225 hasFunder F4320321001 @default.
- W3048997225 hasFunder F4320335777 @default.
- W3048997225 hasLocation W30489972251 @default.
- W3048997225 hasOpenAccess W3048997225 @default.
- W3048997225 hasPrimaryLocation W30489972251 @default.
- W3048997225 hasRelatedWork W1995891606 @default.
- W3048997225 hasRelatedWork W2013585627 @default.
- W3048997225 hasRelatedWork W2058945371 @default.
- W3048997225 hasRelatedWork W2080116769 @default.
- W3048997225 hasRelatedWork W2106080380 @default.
- W3048997225 hasRelatedWork W2108165564 @default.
- W3048997225 hasRelatedWork W2146788481 @default.
- W3048997225 hasRelatedWork W2902987618 @default.
- W3048997225 hasRelatedWork W4210374666 @default.
- W3048997225 hasRelatedWork W4220757755 @default.