- W3087273573 abstract "This research presents an experimental study on the tribological behavior and plastic deformation layer response of quenched-tempered AISI 6150 steel and austempered AISI 6150 steel under sliding with a ball-on-disk type apparatus. Worn surfaces were analyzed by micro-hardness, 3D profilometer, microscopy and scanning electron microscope (SEM). The results showed that the disk surfaces were hardened after tribo-tests due to fresh-martensite formation caused by frictional heating/self-quenching during the sliding tests. The wear loss of the disk specimens was due to smearing plastic deformation resulting in material pile-up along the wear track and debris inside the wear track. The quenched-tempered disk specimens generated more debris than the austempered specimens. The greater amount of wear debris in the quench-tempered samples led to more severe contact stresses between the ball and disk samples which accelerated the smearing of material. As the tempering temperature increases, more cracks were observed for all quenched-tempered disk specimens. More voids and cracks was developed in the near surface region of tempered martensite leading to accelerated material loss through smearing and delamination. Also, more plate-like wear particles were observed on the disks of tempered martensite due to greater surface and subsurface crack fomation and propagation." @default.
- W3087273573 created "2020-09-25" @default.
- W3087273573 creator A5000815070 @default.
- W3087273573 creator A5010522561 @default.
- W3087273573 creator A5039049388 @default.
- W3087273573 creator A5040122877 @default.
- W3087273573 creator A5040167892 @default.
- W3087273573 creator A5077293556 @default.
- W3087273573 creator A5087214567 @default.
- W3087273573 creator A5087698403 @default.
- W3087273573 date "2020-11-01" @default.
- W3087273573 modified "2023-10-17" @default.
- W3087273573 title "Tribological behavior of heat treated AISI 6150 steel" @default.
- W3087273573 cites W1480401307 @default.
- W3087273573 cites W1968680345 @default.
- W3087273573 cites W1969964300 @default.
- W3087273573 cites W1976361340 @default.
- W3087273573 cites W1984021457 @default.
- W3087273573 cites W1985808849 @default.
- W3087273573 cites W1986958588 @default.
- W3087273573 cites W1988311718 @default.
- W3087273573 cites W1991000308 @default.
- W3087273573 cites W1991933602 @default.
- W3087273573 cites W1996052061 @default.
- W3087273573 cites W2005669970 @default.
- W3087273573 cites W2006933101 @default.
- W3087273573 cites W2008454565 @default.
- W3087273573 cites W2010076207 @default.
- W3087273573 cites W2014488765 @default.
- W3087273573 cites W2016561495 @default.
- W3087273573 cites W2024684843 @default.
- W3087273573 cites W2026922739 @default.
- W3087273573 cites W2028624510 @default.
- W3087273573 cites W2030569532 @default.
- W3087273573 cites W2041484056 @default.
- W3087273573 cites W2048130233 @default.
- W3087273573 cites W2050077967 @default.
- W3087273573 cites W2053426827 @default.
- W3087273573 cites W2053544746 @default.
- W3087273573 cites W2058233950 @default.
- W3087273573 cites W2060815927 @default.
- W3087273573 cites W2067387330 @default.
- W3087273573 cites W2074243338 @default.
- W3087273573 cites W2085003067 @default.
- W3087273573 cites W2117741290 @default.
- W3087273573 cites W2161214327 @default.
- W3087273573 cites W24202595 @default.
- W3087273573 cites W2547430932 @default.
- W3087273573 cites W2557509503 @default.
- W3087273573 cites W2769793059 @default.
- W3087273573 cites W2771840400 @default.
- W3087273573 cites W2896204693 @default.
- W3087273573 cites W2903741892 @default.
- W3087273573 cites W2972921251 @default.
- W3087273573 cites W2979871867 @default.
- W3087273573 cites W2985733336 @default.
- W3087273573 cites W2998760990 @default.
- W3087273573 cites W2999008053 @default.
- W3087273573 doi "https://doi.org/10.1016/j.jmrt.2020.08.089" @default.
- W3087273573 hasPublicationYear "2020" @default.
- W3087273573 type Work @default.
- W3087273573 sameAs 3087273573 @default.
- W3087273573 citedByCount "5" @default.
- W3087273573 countsByYear W30872735732021 @default.
- W3087273573 countsByYear W30872735732023 @default.
- W3087273573 crossrefType "journal-article" @default.
- W3087273573 hasAuthorship W3087273573A5000815070 @default.
- W3087273573 hasAuthorship W3087273573A5010522561 @default.
- W3087273573 hasAuthorship W3087273573A5039049388 @default.
- W3087273573 hasAuthorship W3087273573A5040122877 @default.
- W3087273573 hasAuthorship W3087273573A5040167892 @default.
- W3087273573 hasAuthorship W3087273573A5077293556 @default.
- W3087273573 hasAuthorship W3087273573A5087214567 @default.
- W3087273573 hasAuthorship W3087273573A5087698403 @default.
- W3087273573 hasBestOaLocation W30872735731 @default.
- W3087273573 hasConcept C121332964 @default.
- W3087273573 hasConcept C121745418 @default.
- W3087273573 hasConcept C159985019 @default.
- W3087273573 hasConcept C167310744 @default.
- W3087273573 hasConcept C18747287 @default.
- W3087273573 hasConcept C191897082 @default.
- W3087273573 hasConcept C192562407 @default.
- W3087273573 hasConcept C207948433 @default.
- W3087273573 hasConcept C26771246 @default.
- W3087273573 hasConcept C62520636 @default.
- W3087273573 hasConcept C71039073 @default.
- W3087273573 hasConcept C79261456 @default.
- W3087273573 hasConcept C87976508 @default.
- W3087273573 hasConcept C91881484 @default.
- W3087273573 hasConceptScore W3087273573C121332964 @default.
- W3087273573 hasConceptScore W3087273573C121745418 @default.
- W3087273573 hasConceptScore W3087273573C159985019 @default.
- W3087273573 hasConceptScore W3087273573C167310744 @default.
- W3087273573 hasConceptScore W3087273573C18747287 @default.
- W3087273573 hasConceptScore W3087273573C191897082 @default.
- W3087273573 hasConceptScore W3087273573C192562407 @default.
- W3087273573 hasConceptScore W3087273573C207948433 @default.
- W3087273573 hasConceptScore W3087273573C26771246 @default.