- W3089523712 abstract "Laser beam welding (LBW) had been successfully applied to the welding of Ti–6Al–4V plates by wire arc additive manufacturing. The effects of solution treatment on microstructure, tensile properties, and microhardness after LBW in different deposition directions were studied. When the wire speeding was 3 m/min and travel speed was 0.36 m/min, the difference in mechanical properties was related to the anisotropy of the microstructure. The long columnar grain along the building direction could provide an α path with a large aspect ratio and high elongation. More grain boundaries are present along the scanning direction than in others, showing high strength. The microstructure of the as-deposited condition mainly consists of coarse prior-β grains, partial basket-weave structure, and numerous martensite α′ phase. In LBW without solution treatment, the microstructure of the welds mainly consists of a large amount of martensite α′ and a small amount of basket-weave structure. The weld had high strength and hardness. The tensile strength was between 930 and 970 MPa. The hardness was between 415 and 456 HV. The elongation ranged from 5% to 7%. Afterwards, the temperature was maintained at 870 °C for 2 h, cooled to 600 °C in the furnace for 1 h, and finally air cooled to room temperature. The martensite α′ was almost completely transformed into platelet α. The microstructure of the welds mainly consists of partial β grains, thimbleful martensite α′, and a large of α path. The strength and hardness of the welds were reduced. The tensile strength is between 910 and 950 MPa. The hardness was between 398 and 445 HV. However, the elongation was significantly improved, and the elongation ranged from 10% to 12%." @default.
- W3089523712 created "2020-10-08" @default.
- W3089523712 creator A5006111313 @default.
- W3089523712 creator A5011914647 @default.
- W3089523712 creator A5042151372 @default.
- W3089523712 creator A5051273638 @default.
- W3089523712 creator A5091090518 @default.
- W3089523712 date "2020-09-30" @default.
- W3089523712 modified "2023-10-16" @default.
- W3089523712 title "Effects of Solution Treatment on Laser Welding of Ti–6Al–4V Alloy Plate Produced through Wire Arc Additive Manufacturing" @default.
- W3089523712 cites W1711375714 @default.
- W3089523712 cites W1974232778 @default.
- W3089523712 cites W1977420648 @default.
- W3089523712 cites W1977753660 @default.
- W3089523712 cites W2039986872 @default.
- W3089523712 cites W2048312493 @default.
- W3089523712 cites W2058491844 @default.
- W3089523712 cites W2073458383 @default.
- W3089523712 cites W2076582893 @default.
- W3089523712 cites W2082888867 @default.
- W3089523712 cites W2123511994 @default.
- W3089523712 cites W2147248770 @default.
- W3089523712 cites W2250232696 @default.
- W3089523712 cites W2324854349 @default.
- W3089523712 cites W2354100427 @default.
- W3089523712 cites W2531143389 @default.
- W3089523712 cites W2605549397 @default.
- W3089523712 cites W2736312043 @default.
- W3089523712 cites W2762864287 @default.
- W3089523712 cites W2770181615 @default.
- W3089523712 cites W2776655424 @default.
- W3089523712 cites W2791393720 @default.
- W3089523712 cites W2792714161 @default.
- W3089523712 cites W2801166441 @default.
- W3089523712 cites W2884635314 @default.
- W3089523712 cites W2905717179 @default.
- W3089523712 cites W2917320168 @default.
- W3089523712 cites W3013794055 @default.
- W3089523712 cites W2068459595 @default.
- W3089523712 doi "https://doi.org/10.3390/met10101310" @default.
- W3089523712 hasPublicationYear "2020" @default.
- W3089523712 type Work @default.
- W3089523712 sameAs 3089523712 @default.
- W3089523712 citedByCount "2" @default.
- W3089523712 countsByYear W30895237122021 @default.
- W3089523712 countsByYear W30895237122023 @default.
- W3089523712 crossrefType "journal-article" @default.
- W3089523712 hasAuthorship W3089523712A5006111313 @default.
- W3089523712 hasAuthorship W3089523712A5011914647 @default.
- W3089523712 hasAuthorship W3089523712A5042151372 @default.
- W3089523712 hasAuthorship W3089523712A5051273638 @default.
- W3089523712 hasAuthorship W3089523712A5091090518 @default.
- W3089523712 hasBestOaLocation W30895237121 @default.
- W3089523712 hasConcept C112950240 @default.
- W3089523712 hasConcept C159985019 @default.
- W3089523712 hasConcept C165720898 @default.
- W3089523712 hasConcept C18747287 @default.
- W3089523712 hasConcept C191897082 @default.
- W3089523712 hasConcept C192562407 @default.
- W3089523712 hasConcept C19474535 @default.
- W3089523712 hasConcept C2780026712 @default.
- W3089523712 hasConcept C33947775 @default.
- W3089523712 hasConcept C87976508 @default.
- W3089523712 hasConceptScore W3089523712C112950240 @default.
- W3089523712 hasConceptScore W3089523712C159985019 @default.
- W3089523712 hasConceptScore W3089523712C165720898 @default.
- W3089523712 hasConceptScore W3089523712C18747287 @default.
- W3089523712 hasConceptScore W3089523712C191897082 @default.
- W3089523712 hasConceptScore W3089523712C192562407 @default.
- W3089523712 hasConceptScore W3089523712C19474535 @default.
- W3089523712 hasConceptScore W3089523712C2780026712 @default.
- W3089523712 hasConceptScore W3089523712C33947775 @default.
- W3089523712 hasConceptScore W3089523712C87976508 @default.
- W3089523712 hasFunder F4320335833 @default.
- W3089523712 hasIssue "10" @default.
- W3089523712 hasLocation W30895237121 @default.
- W3089523712 hasOpenAccess W3089523712 @default.
- W3089523712 hasPrimaryLocation W30895237121 @default.
- W3089523712 hasRelatedWork W1979107336 @default.
- W3089523712 hasRelatedWork W1987487801 @default.
- W3089523712 hasRelatedWork W1988943651 @default.
- W3089523712 hasRelatedWork W2348697288 @default.
- W3089523712 hasRelatedWork W2349027603 @default.
- W3089523712 hasRelatedWork W2368738051 @default.
- W3089523712 hasRelatedWork W2369154548 @default.
- W3089523712 hasRelatedWork W2371235204 @default.
- W3089523712 hasRelatedWork W4211100724 @default.
- W3089523712 hasRelatedWork W4240267549 @default.
- W3089523712 hasVolume "10" @default.
- W3089523712 isParatext "false" @default.
- W3089523712 isRetracted "false" @default.
- W3089523712 magId "3089523712" @default.
- W3089523712 workType "article" @default.