- W3089707114 abstract "This research was aimed to do heat treatment of austemper carburization and investigate the effect of various cooling media on mechanical properties and microstructure of Cr-Mo alloy lateritic steel. Heat treatment was conducted to austenisation temperature at 950o C for 1 hour and austemper carburization at 400o C for 1 hour. Variation of cooling media included air blowing for 1 hour, water, and furnace cooling for 24 hours. Hardness and impact test were done using Hardness Rockwell and Charpy methods. Microstructure was observed using optical microscope. Fracture surface characterization was using SEM-EDX. The results showed the highest hardness of 65.48 HRC in sample that cooled by air blowing for 1 hour. The microstructure of this sample showed phases of ferrite, pearlite and martensite which causing higher hardness. The highest impact strength of 20 Joule took place in the furnace cooled sample. Characterization of the fracture surface using SEM-EDX showed dimple of ductile fractures.Penelitian ini bertujuan untuk melakukan proses perlakukan panas karburisasi austemper dan mempelajari pengaruh media pendinginan terhadap sifat mekanik dan struktur mikro baja laterit paduan Cr-Mo. Perlakuan panas yang dilakukan yaitu pemanasan sampel pada temperatur austenisasi (950o C) selama 1 jam dan proses karburisasi austemper dengan media serbuk arang halus pada temperatur 400o C selama 1 jam. Variasi pendinginan yang digunakan yaitu air blowing (semburan udara) selama 1 jam, air dan tungku selama 24 jam. Pengujian kekerasan dilakukan dengan metode Rockwell Hardness dan pengujian impak dilakukan dengan metode charpy. Karakterisasi struktur mikro dilakukan dengan proses metalografi dan mikroskop optik. Karakterisasi permukaan patahan pengujian impak dilakukan dengan SEM-EDX. Hasil penelitian ini menunjukkan nilai kekerasan tertinggi yaitu 65,48 HRC terjadi pada sampel dengan air blowing selama 1 jam. Struktur mikro sampel tersebut menunjukkan adanya fasa ferit, perlit dan martensit yang membuat sampel menjadi keras. Nilai kekuatan impak tertinggi sebesar 20 Joule terjadi pada sampel dengan pendinginan di dalam tungku selama 24 jam. Karakterisasi permukaan patahannya menggunakan SEM-EDX menunjukkan adanya dimple dari patah ulet." @default.
- W3089707114 created "2020-10-08" @default.
- W3089707114 creator A5014218705 @default.
- W3089707114 creator A5026565406 @default.
- W3089707114 creator A5030044968 @default.
- W3089707114 creator A5040919722 @default.
- W3089707114 creator A5060639139 @default.
- W3089707114 creator A5082497668 @default.
- W3089707114 creator A5087178589 @default.
- W3089707114 date "2020-06-30" @default.
- W3089707114 modified "2023-10-16" @default.
- W3089707114 title "Pengaruh Perlakuan Panas Karburisasi Austemper pada Baja Laterit Paduan Cr-Mo terhadap Sifat Mekanik dan Struktur Mikro" @default.
- W3089707114 doi "https://doi.org/10.37209/jtbbt.v10i1.165" @default.
- W3089707114 hasPublicationYear "2020" @default.
- W3089707114 type Work @default.
- W3089707114 sameAs 3089707114 @default.
- W3089707114 citedByCount "0" @default.
- W3089707114 crossrefType "journal-article" @default.
- W3089707114 hasAuthorship W3089707114A5014218705 @default.
- W3089707114 hasAuthorship W3089707114A5026565406 @default.
- W3089707114 hasAuthorship W3089707114A5030044968 @default.
- W3089707114 hasAuthorship W3089707114A5040919722 @default.
- W3089707114 hasAuthorship W3089707114A5060639139 @default.
- W3089707114 hasAuthorship W3089707114A5082497668 @default.
- W3089707114 hasAuthorship W3089707114A5087178589 @default.
- W3089707114 hasBestOaLocation W30897071141 @default.
- W3089707114 hasConcept C127205250 @default.
- W3089707114 hasConcept C159985019 @default.
- W3089707114 hasConcept C191897082 @default.
- W3089707114 hasConcept C192562407 @default.
- W3089707114 hasConcept C42698342 @default.
- W3089707114 hasConcept C87976508 @default.
- W3089707114 hasConcept C96606946 @default.
- W3089707114 hasConceptScore W3089707114C127205250 @default.
- W3089707114 hasConceptScore W3089707114C159985019 @default.
- W3089707114 hasConceptScore W3089707114C191897082 @default.
- W3089707114 hasConceptScore W3089707114C192562407 @default.
- W3089707114 hasConceptScore W3089707114C42698342 @default.
- W3089707114 hasConceptScore W3089707114C87976508 @default.
- W3089707114 hasConceptScore W3089707114C96606946 @default.
- W3089707114 hasLocation W30897071141 @default.
- W3089707114 hasOpenAccess W3089707114 @default.
- W3089707114 hasPrimaryLocation W30897071141 @default.
- W3089707114 hasRelatedWork W2297057 @default.
- W3089707114 hasRelatedWork W28928644 @default.
- W3089707114 hasRelatedWork W35003201 @default.
- W3089707114 hasRelatedWork W37094819 @default.
- W3089707114 hasRelatedWork W38553972 @default.
- W3089707114 hasRelatedWork W47755216 @default.
- W3089707114 hasRelatedWork W51334114 @default.
- W3089707114 hasRelatedWork W52188470 @default.
- W3089707114 hasRelatedWork W54160387 @default.
- W3089707114 hasRelatedWork W9862308 @default.
- W3089707114 isParatext "false" @default.
- W3089707114 isRetracted "false" @default.
- W3089707114 magId "3089707114" @default.
- W3089707114 workType "article" @default.