- W3092897462 abstract "The study was conducted to evaluate the impact toughness of flux-cored arc welded of SM570-TMC steel joint under different heat inputs, 0.9 kJ/mm (low heat input) and 1.6 kJ/mm (high heat input). Welding wire containing 0.4%Ni was selected on this experiment. Multi-pass welds were performed on SM570-TMC steel plate of 16 mm in thickness with a single V-groove butt joint on flat position (1G). The evaluation consists of observations on microstructure using an optical microscope and SEM-EDS, and mechanical properties including tensile, microhardness Vickers and Charpy V-notch (CVN) impact test at temperatures of 25, 0 and-20 °C. Results showed that the impact toughness of the base metal (BM) was higher than the weld metal (WM) at all test temperatures. Hardness and impact toughness of WM at low heat input was observed higher than when applied a high heat input. The welded samples at low and high heat inputs had high of tensile strength, and the fracture seemly occurs on the BM. Microstructure observation showed that at a high heat input, larger grains and microsegregation were observed. It might affect on decreasing their impact property." @default.
- W3092897462 created "2020-10-22" @default.
- W3092897462 creator A5046742355 @default.
- W3092897462 creator A5056770138 @default.
- W3092897462 creator A5065288547 @default.
- W3092897462 creator A5071582026 @default.
- W3092897462 creator A5089771346 @default.
- W3092897462 date "2020-10-01" @default.
- W3092897462 modified "2023-09-23" @default.
- W3092897462 title "Impact Toughness Characteristics of SM570-TMC Steel Joint Using Welding Wire Containing 0.4% Nickel at Different Level of Heat Input" @default.
- W3092897462 cites W1897817834 @default.
- W3092897462 cites W1976226533 @default.
- W3092897462 cites W1997250498 @default.
- W3092897462 cites W2056091752 @default.
- W3092897462 cites W2065925100 @default.
- W3092897462 cites W2083003417 @default.
- W3092897462 cites W2406863730 @default.
- W3092897462 cites W2789315330 @default.
- W3092897462 cites W2837879228 @default.
- W3092897462 cites W2891536558 @default.
- W3092897462 cites W2917266395 @default.
- W3092897462 cites W2964056621 @default.
- W3092897462 cites W889305082 @default.
- W3092897462 doi "https://doi.org/10.4028/www.scientific.net/kem.867.117" @default.
- W3092897462 hasPublicationYear "2020" @default.
- W3092897462 type Work @default.
- W3092897462 sameAs 3092897462 @default.
- W3092897462 citedByCount "2" @default.
- W3092897462 countsByYear W30928974622021 @default.
- W3092897462 crossrefType "journal-article" @default.
- W3092897462 hasAuthorship W3092897462A5046742355 @default.
- W3092897462 hasAuthorship W3092897462A5056770138 @default.
- W3092897462 hasAuthorship W3092897462A5065288547 @default.
- W3092897462 hasAuthorship W3092897462A5071582026 @default.
- W3092897462 hasAuthorship W3092897462A5089771346 @default.
- W3092897462 hasConcept C102267420 @default.
- W3092897462 hasConcept C112950240 @default.
- W3092897462 hasConcept C127205250 @default.
- W3092897462 hasConcept C127413603 @default.
- W3092897462 hasConcept C159985019 @default.
- W3092897462 hasConcept C165720898 @default.
- W3092897462 hasConcept C182508753 @default.
- W3092897462 hasConcept C18555067 @default.
- W3092897462 hasConcept C191897082 @default.
- W3092897462 hasConcept C192562407 @default.
- W3092897462 hasConcept C19474535 @default.
- W3092897462 hasConcept C40241539 @default.
- W3092897462 hasConcept C66938386 @default.
- W3092897462 hasConcept C87976508 @default.
- W3092897462 hasConcept C94870803 @default.
- W3092897462 hasConcept C99595764 @default.
- W3092897462 hasConceptScore W3092897462C102267420 @default.
- W3092897462 hasConceptScore W3092897462C112950240 @default.
- W3092897462 hasConceptScore W3092897462C127205250 @default.
- W3092897462 hasConceptScore W3092897462C127413603 @default.
- W3092897462 hasConceptScore W3092897462C159985019 @default.
- W3092897462 hasConceptScore W3092897462C165720898 @default.
- W3092897462 hasConceptScore W3092897462C182508753 @default.
- W3092897462 hasConceptScore W3092897462C18555067 @default.
- W3092897462 hasConceptScore W3092897462C191897082 @default.
- W3092897462 hasConceptScore W3092897462C192562407 @default.
- W3092897462 hasConceptScore W3092897462C19474535 @default.
- W3092897462 hasConceptScore W3092897462C40241539 @default.
- W3092897462 hasConceptScore W3092897462C66938386 @default.
- W3092897462 hasConceptScore W3092897462C87976508 @default.
- W3092897462 hasConceptScore W3092897462C94870803 @default.
- W3092897462 hasConceptScore W3092897462C99595764 @default.
- W3092897462 hasLocation W30928974621 @default.
- W3092897462 hasOpenAccess W3092897462 @default.
- W3092897462 hasPrimaryLocation W30928974621 @default.
- W3092897462 hasRelatedWork W2297057 @default.
- W3092897462 hasRelatedWork W25260731 @default.
- W3092897462 hasRelatedWork W30597469 @default.
- W3092897462 hasRelatedWork W40517357 @default.
- W3092897462 hasRelatedWork W41137717 @default.
- W3092897462 hasRelatedWork W47755216 @default.
- W3092897462 hasRelatedWork W47933584 @default.
- W3092897462 hasRelatedWork W50225239 @default.
- W3092897462 hasRelatedWork W53043644 @default.
- W3092897462 hasRelatedWork W52728044 @default.
- W3092897462 isParatext "false" @default.
- W3092897462 isRetracted "false" @default.
- W3092897462 magId "3092897462" @default.
- W3092897462 workType "article" @default.