- W3093767059 endingPage "3138" @default.
- W3093767059 startingPage "3135" @default.
- W3093767059 abstract "Using High Energy ball milling, the particle size of average 80 µm and 25 µm, 40 wt% Ni-Fe alloy powder was produced by mechanical alloying respectively. For different time intervals of 16, 32 and 64 hrs, at room temperature, high energy planetary ball milling was done. On “DR.SINTER.LABTM (SPS 5155) machine” spark plasma sintering (SPS) was performed. At constant temperature and pressure of 650 °C and 30Mpa respectively, all samples were sintered. The research is applied on same alloy, as milling hour increases, porosity increases and densification decreases of the samples, this is because of some reasons that are “increase in the surface area of the milled nanopowder (i.e. Reduction of particle size), low green body density of long milling powders by agglomeration of powders and oxidation of powders during a milling process”. As milling hour increases, for perfect densification, more temperature and pressure is needed. In 16 h of milling 85.4% densification was achieved." @default.
- W3093767059 created "2020-10-29" @default.
- W3093767059 creator A5037138959 @default.
- W3093767059 creator A5062966435 @default.
- W3093767059 date "2021-01-01" @default.
- W3093767059 modified "2023-09-25" @default.
- W3093767059 title "A study on factors affecting the densification ofspark plasma sintered ball milled 40 wt% Ni-Fe nanopowder" @default.
- W3093767059 cites W1504211442 @default.
- W3093767059 cites W1662175451 @default.
- W3093767059 cites W1988589367 @default.
- W3093767059 cites W2002613545 @default.
- W3093767059 cites W2034889023 @default.
- W3093767059 cites W2054707738 @default.
- W3093767059 cites W2065441148 @default.
- W3093767059 cites W2149060538 @default.
- W3093767059 cites W2157309158 @default.
- W3093767059 cites W2397975515 @default.
- W3093767059 cites W2515963323 @default.
- W3093767059 cites W2775958948 @default.
- W3093767059 cites W2904533270 @default.
- W3093767059 cites W2965504132 @default.
- W3093767059 cites W2966584813 @default.
- W3093767059 cites W2981995391 @default.
- W3093767059 cites W2986421671 @default.
- W3093767059 cites W2991231499 @default.
- W3093767059 doi "https://doi.org/10.1016/j.matpr.2020.09.027" @default.
- W3093767059 hasPublicationYear "2021" @default.
- W3093767059 type Work @default.
- W3093767059 sameAs 3093767059 @default.
- W3093767059 citedByCount "2" @default.
- W3093767059 countsByYear W30937670592023 @default.
- W3093767059 crossrefType "journal-article" @default.
- W3093767059 hasAuthorship W3093767059A5037138959 @default.
- W3093767059 hasAuthorship W3093767059A5062966435 @default.
- W3093767059 hasConcept C127413603 @default.
- W3093767059 hasConcept C131850264 @default.
- W3093767059 hasConcept C132186339 @default.
- W3093767059 hasConcept C159985019 @default.
- W3093767059 hasConcept C187530423 @default.
- W3093767059 hasConcept C191897082 @default.
- W3093767059 hasConcept C192562407 @default.
- W3093767059 hasConcept C2776014600 @default.
- W3093767059 hasConcept C2777581544 @default.
- W3093767059 hasConcept C2780026712 @default.
- W3093767059 hasConcept C42360764 @default.
- W3093767059 hasConcept C6648577 @default.
- W3093767059 hasConceptScore W3093767059C127413603 @default.
- W3093767059 hasConceptScore W3093767059C131850264 @default.
- W3093767059 hasConceptScore W3093767059C132186339 @default.
- W3093767059 hasConceptScore W3093767059C159985019 @default.
- W3093767059 hasConceptScore W3093767059C187530423 @default.
- W3093767059 hasConceptScore W3093767059C191897082 @default.
- W3093767059 hasConceptScore W3093767059C192562407 @default.
- W3093767059 hasConceptScore W3093767059C2776014600 @default.
- W3093767059 hasConceptScore W3093767059C2777581544 @default.
- W3093767059 hasConceptScore W3093767059C2780026712 @default.
- W3093767059 hasConceptScore W3093767059C42360764 @default.
- W3093767059 hasConceptScore W3093767059C6648577 @default.
- W3093767059 hasLocation W30937670591 @default.
- W3093767059 hasOpenAccess W3093767059 @default.
- W3093767059 hasPrimaryLocation W30937670591 @default.
- W3093767059 hasRelatedWork W1965572746 @default.
- W3093767059 hasRelatedWork W2031122028 @default.
- W3093767059 hasRelatedWork W2058545557 @default.
- W3093767059 hasRelatedWork W2062064674 @default.
- W3093767059 hasRelatedWork W2089315512 @default.
- W3093767059 hasRelatedWork W2097829472 @default.
- W3093767059 hasRelatedWork W2245602275 @default.
- W3093767059 hasRelatedWork W2547539111 @default.
- W3093767059 hasRelatedWork W2902107089 @default.
- W3093767059 hasRelatedWork W4319067266 @default.
- W3093767059 hasVolume "37" @default.
- W3093767059 isParatext "false" @default.
- W3093767059 isRetracted "false" @default.
- W3093767059 magId "3093767059" @default.
- W3093767059 workType "article" @default.