- W3094992479 endingPage "3252" @default.
- W3094992479 startingPage "3246" @default.
- W3094992479 abstract "For this research, wear and corrosion effects of a pure aluminium composite matrix reinforced with SiC and Spent catalyst were investigated. Pure aluminium reinforced with a specific weight percentage 2.5%, 5%, 7.5%, and 10% of 40 μm of spent catalyst particle size and 20 μm of SiC particle size with a stir casting process. The wear and corrosion rate was determined by using pin-on-disk and salt spray systems. In pin-on-disk, the sliding wear test with a uniform load of 10 N and constant sliding velocity 5 m/s were conducted for 10 min. Corrosion monitoring was conducted for 100 h in a salt spray bath. Wear loss with a uniform load of 10 N that was applied for both the metal matrix and the reinforced composites, and respective weight loss of composites was noted. Wear track of composite morphological characterization was done using a scanning electron microscope (SEM). Better wear and corrosion values have been obtained at 10 wt% silicon carbide and 10 wt% spent catalyst respectively. The result indicates that enhanced composites exhibit superior wear and corrosion compared to pure aluminium." @default.
- W3094992479 created "2020-11-09" @default.
- W3094992479 creator A5064715874 @default.
- W3094992479 creator A5091512238 @default.
- W3094992479 date "2021-01-01" @default.
- W3094992479 modified "2023-10-01" @default.
- W3094992479 title "Wear and corrosion behaviour on pure aluminium matrix reinforced with SiC and spent catalyst by using the stir casting method" @default.
- W3094992479 cites W2043698287 @default.
- W3094992479 cites W2136249094 @default.
- W3094992479 cites W2476345895 @default.
- W3094992479 cites W2790627549 @default.
- W3094992479 cites W2791033678 @default.
- W3094992479 cites W2797628889 @default.
- W3094992479 cites W2800591998 @default.
- W3094992479 cites W2806133058 @default.
- W3094992479 cites W2909609288 @default.
- W3094992479 cites W2948641342 @default.
- W3094992479 cites W2966039668 @default.
- W3094992479 cites W2968228511 @default.
- W3094992479 cites W2982351349 @default.
- W3094992479 cites W3012472708 @default.
- W3094992479 cites W3036237963 @default.
- W3094992479 cites W3145891179 @default.
- W3094992479 doi "https://doi.org/10.1016/j.matpr.2020.09.721" @default.
- W3094992479 hasPublicationYear "2021" @default.
- W3094992479 type Work @default.
- W3094992479 sameAs 3094992479 @default.
- W3094992479 citedByCount "5" @default.
- W3094992479 countsByYear W30949924792022 @default.
- W3094992479 countsByYear W30949924792023 @default.
- W3094992479 crossrefType "journal-article" @default.
- W3094992479 hasAuthorship W3094992479A5064715874 @default.
- W3094992479 hasAuthorship W3094992479A5091512238 @default.
- W3094992479 hasBestOaLocation W30949924791 @default.
- W3094992479 hasConcept C104779481 @default.
- W3094992479 hasConcept C111368507 @default.
- W3094992479 hasConcept C127313418 @default.
- W3094992479 hasConcept C127413603 @default.
- W3094992479 hasConcept C159985019 @default.
- W3094992479 hasConcept C16635281 @default.
- W3094992479 hasConcept C187530423 @default.
- W3094992479 hasConcept C191897082 @default.
- W3094992479 hasConcept C192562407 @default.
- W3094992479 hasConcept C20625102 @default.
- W3094992479 hasConcept C26771246 @default.
- W3094992479 hasConcept C2777925586 @default.
- W3094992479 hasConcept C2778517922 @default.
- W3094992479 hasConcept C2780722187 @default.
- W3094992479 hasConcept C42360764 @default.
- W3094992479 hasConcept C513153333 @default.
- W3094992479 hasConceptScore W3094992479C104779481 @default.
- W3094992479 hasConceptScore W3094992479C111368507 @default.
- W3094992479 hasConceptScore W3094992479C127313418 @default.
- W3094992479 hasConceptScore W3094992479C127413603 @default.
- W3094992479 hasConceptScore W3094992479C159985019 @default.
- W3094992479 hasConceptScore W3094992479C16635281 @default.
- W3094992479 hasConceptScore W3094992479C187530423 @default.
- W3094992479 hasConceptScore W3094992479C191897082 @default.
- W3094992479 hasConceptScore W3094992479C192562407 @default.
- W3094992479 hasConceptScore W3094992479C20625102 @default.
- W3094992479 hasConceptScore W3094992479C26771246 @default.
- W3094992479 hasConceptScore W3094992479C2777925586 @default.
- W3094992479 hasConceptScore W3094992479C2778517922 @default.
- W3094992479 hasConceptScore W3094992479C2780722187 @default.
- W3094992479 hasConceptScore W3094992479C42360764 @default.
- W3094992479 hasConceptScore W3094992479C513153333 @default.
- W3094992479 hasLocation W30949924791 @default.
- W3094992479 hasOpenAccess W3094992479 @default.
- W3094992479 hasPrimaryLocation W30949924791 @default.
- W3094992479 hasRelatedWork W1982666628 @default.
- W3094992479 hasRelatedWork W1985012163 @default.
- W3094992479 hasRelatedWork W2039464635 @default.
- W3094992479 hasRelatedWork W2046746716 @default.
- W3094992479 hasRelatedWork W2063778609 @default.
- W3094992479 hasRelatedWork W2314034157 @default.
- W3094992479 hasRelatedWork W2570482905 @default.
- W3094992479 hasRelatedWork W3020764549 @default.
- W3094992479 hasRelatedWork W3097783663 @default.
- W3094992479 hasRelatedWork W4206845333 @default.
- W3094992479 hasVolume "38" @default.
- W3094992479 isParatext "false" @default.
- W3094992479 isRetracted "false" @default.
- W3094992479 magId "3094992479" @default.
- W3094992479 workType "article" @default.