• W3107050004 abstract "Abstract The scope of work included the fabrication of ceramic-metal composites from the Al 2 O 3 -Cu and Al 2 O 3 -Cu-Mo and examining their microstructure and selected properties. The composites were fabricated by the slip casting method. The rheological behavior, microstructures, X-ray analysis, and mechanical properties were investigated. The rheological study demonstrated that all of the obtained slurries were non-Newtonian shear diluted fluids and stability on time. In both slurries, the flow limit is close to 0 Pa, which is very beneficial when casting the suspensions into molds. The X-ray analysis reveals Al 2 O 3 , Cu, and Mo phases in all specimens. No new phases were found in both types of composites after the sintering process. The results provided that the hardness for Al 2 O 3 -Cu-Mo composites was equal to 10.06 ± 0.49 GPa, while for Al 2 O 3 -Cu, it was equal to 6.81 ± 2.08 GPa. The K 1C values measured, with the use of Niihara equation, for composites with and without the addition of Mo were equal to 6.13 ± 0.62 MPa m 0.5 and 6.04 ± 0.55 MPa m 0.5 , respectively. It has been established that the mean specific wear rates of Al 2 O 3 -Cu and Al 2 O 3 -Cu-Mo samples were 0.35 × 10–5 ± 0.02 mm 3 N −1 m −1 and 0.22 × 10–5 ± 0.04 mm 3 N −1 m −1 , respectively. It was found that molybdenum addition improved wear resistance properties of the composites." @default.
• W3107050004 created "2020-12-07" @default.
• W3107050004 creator A5018706819 @default.
• W3107050004 creator A5056156856 @default.
• W3107050004 creator A5068280117 @default.
• W3107050004 creator A5069421138 @default.
• W3107050004 creator A5074299172 @default.
• W3107050004 date "2020-11-20" @default.
• W3107050004 modified "2023-10-06" @default.
• W3107050004 title "Investigation of microstructure and selected properties of Al2O3-Cu and Al2O3-Cu-Mo composites" @default.
• W3107050004 cites W197253224 @default.
• W3107050004 cites W1975089636 @default.
• W3107050004 cites W1980830965 @default.
• W3107050004 cites W1982145859 @default.
• W3107050004 cites W1984656329 @default.
• W3107050004 cites W1988772108 @default.
• W3107050004 cites W1997391465 @default.
• W3107050004 cites W2003983607 @default.
• W3107050004 cites W2005344676 @default.
• W3107050004 cites W2008142180 @default.
• W3107050004 cites W2019131424 @default.
• W3107050004 cites W2019932804 @default.
• W3107050004 cites W2029129551 @default.
• W3107050004 cites W2029228140 @default.
• W3107050004 cites W2031714287 @default.
• W3107050004 cites W2046658745 @default.
• W3107050004 cites W2048414782 @default.
• W3107050004 cites W2050147687 @default.
• W3107050004 cites W2053024757 @default.
• W3107050004 cites W2055955464 @default.
• W3107050004 cites W2070275972 @default.
• W3107050004 cites W2071182278 @default.
• W3107050004 cites W2084253272 @default.
• W3107050004 cites W2116673269 @default.
• W3107050004 cites W2203961583 @default.
• W3107050004 cites W2504484763 @default.
• W3107050004 cites W2552525793 @default.
• W3107050004 cites W2554708843 @default.
• W3107050004 cites W2561509057 @default.
• W3107050004 cites W2761744062 @default.
• W3107050004 cites W2770001698 @default.
• W3107050004 cites W2802095790 @default.
• W3107050004 cites W2803731308 @default.
• W3107050004 cites W2900280279 @default.
• W3107050004 cites W2903126590 @default.
• W3107050004 cites W2904147459 @default.
• W3107050004 cites W2948385740 @default.
• W3107050004 cites W2985412918 @default.
• W3107050004 cites W2985875729 @default.
• W3107050004 cites W3024083423 @default.
• W3107050004 cites W3035715929 @default.
• W3107050004 cites W3141452292 @default.
• W3107050004 cites W4210260839 @default.
• W3107050004 doi "https://doi.org/10.1007/s42114-020-00188-8" @default.
• W3107050004 hasPublicationYear "2020" @default.
• W3107050004 type Work @default.
• W3107050004 sameAs 3107050004 @default.
• W3107050004 citedByCount "6" @default.
• W3107050004 countsByYear W31070500042021 @default.
• W3107050004 countsByYear W31070500042022 @default.
• W3107050004 countsByYear W31070500042023 @default.
• W3107050004 crossrefType "journal-article" @default.
• W3107050004 hasAuthorship W3107050004A5018706819 @default.
• W3107050004 hasAuthorship W3107050004A5056156856 @default.
• W3107050004 hasAuthorship W3107050004A5068280117 @default.
• W3107050004 hasAuthorship W3107050004A5069421138 @default.
• W3107050004 hasAuthorship W3107050004A5074299172 @default.
• W3107050004 hasBestOaLocation W31070500041 @default.
• W3107050004 hasConcept C134132462 @default.
• W3107050004 hasConcept C136525101 @default.
• W3107050004 hasConcept C142724271 @default.
• W3107050004 hasConcept C159985019 @default.
• W3107050004 hasConcept C191897082 @default.
• W3107050004 hasConcept C192562407 @default.
• W3107050004 hasConcept C200990466 @default.
• W3107050004 hasConcept C204787440 @default.
• W3107050004 hasConcept C2777581544 @default.
• W3107050004 hasConcept C544778455 @default.
• W3107050004 hasConcept C56918372 @default.
• W3107050004 hasConcept C71924100 @default.
• W3107050004 hasConcept C87976508 @default.
• W3107050004 hasConcept C94293008 @default.
• W3107050004 hasConceptScore W3107050004C134132462 @default.
• W3107050004 hasConceptScore W3107050004C136525101 @default.
• W3107050004 hasConceptScore W3107050004C142724271 @default.
• W3107050004 hasConceptScore W3107050004C159985019 @default.
• W3107050004 hasConceptScore W3107050004C191897082 @default.
• W3107050004 hasConceptScore W3107050004C192562407 @default.
• W3107050004 hasConceptScore W3107050004C200990466 @default.
• W3107050004 hasConceptScore W3107050004C204787440 @default.
• W3107050004 hasConceptScore W3107050004C2777581544 @default.
• W3107050004 hasConceptScore W3107050004C544778455 @default.
• W3107050004 hasConceptScore W3107050004C56918372 @default.
• W3107050004 hasConceptScore W3107050004C71924100 @default.
• W3107050004 hasConceptScore W3107050004C87976508 @default.
• W3107050004 hasConceptScore W3107050004C94293008 @default.
• W3107050004 hasFunder F4320321042 @default.
• W3107050004 hasFunder F4320322650 @default.

• next