- W3114271323 abstract "In friction stir welding process, shoulder diameter of stirring tool plays an important role. The role is to provide enough soften region along the process to produce a good quality of weldment. In this work, three variations of stirring tool shoulder diameter are produced which are stirring tool 1 (16mm), stirring tool 2 (20mm), and stirring tool 3 (24mm). Reconfigured milling machine (Cheng Yin – CY-GH 260) is used to performed friction stir welding process using the fabricated stirring tool. The stirring tools are made of H13 steel (chromium-molybdenum) with constant pin height of 3mm, and pin diameter of 5mm. Welding parameter used are 1270 RPM for rotating speed and 248 mm/min for welding speed. Then, all stirring tools are used to joined two similar plates AA 6061 with butt joint. The surface quality is determined from physical appearance, surface roughness, and welding strength of AA 6061 welded samples using fabricated strring tools (16mm, 20mm, and 24mm). From the result, smallest diameter stirring tool 1 (16mm) produced the best surface quality of weldment. Stirring tool 1 produced a free defect sample, smoothest surface with surface roughness value of 1.92 µm, and highest welding strength (119.28 MPa). However, the wear rate of the stirring tool 1 is the highest recorded from the stirring tool 1 material deposited at the sample." @default.
- W3114271323 created "2021-01-05" @default.
- W3114271323 creator A5030349075 @default.
- W3114271323 creator A5044002945 @default.
- W3114271323 creator A5047144963 @default.
- W3114271323 creator A5078514846 @default.
- W3114271323 date "2020-12-18" @default.
- W3114271323 modified "2023-09-26" @default.
- W3114271323 title "Effect of tool shoulder diameters on surface quality of friction stir welded joints of aluminum alloy 6061" @default.
- W3114271323 cites W1999654508 @default.
- W3114271323 cites W2768958666 @default.
- W3114271323 doi "https://doi.org/10.1088/1757-899x/932/1/012114" @default.
- W3114271323 hasPublicationYear "2020" @default.
- W3114271323 type Work @default.
- W3114271323 sameAs 3114271323 @default.
- W3114271323 citedByCount "0" @default.
- W3114271323 crossrefType "journal-article" @default.
- W3114271323 hasAuthorship W3114271323A5030349075 @default.
- W3114271323 hasAuthorship W3114271323A5044002945 @default.
- W3114271323 hasAuthorship W3114271323A5047144963 @default.
- W3114271323 hasAuthorship W3114271323A5078514846 @default.
- W3114271323 hasBestOaLocation W31142713231 @default.
- W3114271323 hasConcept C107365816 @default.
- W3114271323 hasConcept C127413603 @default.
- W3114271323 hasConcept C159985019 @default.
- W3114271323 hasConcept C191897082 @default.
- W3114271323 hasConcept C192562407 @default.
- W3114271323 hasConcept C19474535 @default.
- W3114271323 hasConcept C2780026712 @default.
- W3114271323 hasConcept C40367268 @default.
- W3114271323 hasConcept C513153333 @default.
- W3114271323 hasConcept C71039073 @default.
- W3114271323 hasConcept C78519656 @default.
- W3114271323 hasConcept C81063470 @default.
- W3114271323 hasConcept C94870803 @default.
- W3114271323 hasConceptScore W3114271323C107365816 @default.
- W3114271323 hasConceptScore W3114271323C127413603 @default.
- W3114271323 hasConceptScore W3114271323C159985019 @default.
- W3114271323 hasConceptScore W3114271323C191897082 @default.
- W3114271323 hasConceptScore W3114271323C192562407 @default.
- W3114271323 hasConceptScore W3114271323C19474535 @default.
- W3114271323 hasConceptScore W3114271323C2780026712 @default.
- W3114271323 hasConceptScore W3114271323C40367268 @default.
- W3114271323 hasConceptScore W3114271323C513153333 @default.
- W3114271323 hasConceptScore W3114271323C71039073 @default.
- W3114271323 hasConceptScore W3114271323C78519656 @default.
- W3114271323 hasConceptScore W3114271323C81063470 @default.
- W3114271323 hasConceptScore W3114271323C94870803 @default.
- W3114271323 hasLocation W31142713231 @default.
- W3114271323 hasOpenAccess W3114271323 @default.
- W3114271323 hasPrimaryLocation W31142713231 @default.
- W3114271323 hasRelatedWork W2388650043 @default.
- W3114271323 hasRelatedWork W2394025433 @default.
- W3114271323 hasRelatedWork W2417394184 @default.
- W3114271323 hasRelatedWork W2921021964 @default.
- W3114271323 hasRelatedWork W2948469762 @default.
- W3114271323 hasRelatedWork W2990398083 @default.
- W3114271323 hasRelatedWork W2998563097 @default.
- W3114271323 hasRelatedWork W3048615399 @default.
- W3114271323 hasRelatedWork W4220664133 @default.
- W3114271323 hasRelatedWork W4360951528 @default.
- W3114271323 hasVolume "932" @default.
- W3114271323 isParatext "false" @default.
- W3114271323 isRetracted "false" @default.
- W3114271323 magId "3114271323" @default.
- W3114271323 workType "article" @default.