- W3119443645 abstract "Lead-free ferroelectric BCZT ((Ba0.85Ca0.15)(Ti0.9Zr0.1)O3) films with thickness ~ 750 nm were deposited on Si/SiO2/TiO2/Pt (1 0 0) substrates using polyvinyl pyrrolidone modified chemical solution. BCZT films crystallized at 800 °C showed better electrical and mechanical properties as compared to the films crystallized at 700 °C. The BCZT films crystallized at 800 °C exhibited maximum polarization of 58 µC/cm2 and energy storage density of 27.53 J/cm3. Furthermore, these films displayed extremely low dielectric loss and leakage current densities. The dielectric loss varied from 0.005 to 0.026 in measured frequency range: 3 kHz to 500 kHz. Hardness and elastic modulus values calculated from nanoindentaion measurements of the 700 °C annealed film were 5.2 ± 0.3 GPa and 87.3 ± 2.6 GPa respectively. The same for the 800 °C annealed film were 3.9 ± 1.02 GPa and 227 ± 28 GPa respectively. The higher values of elastic modulus of the 800 °C annealed film could be correlated to the microstructure of the film." @default.
- W3119443645 created "2021-01-18" @default.
- W3119443645 creator A5022727233 @default.
- W3119443645 creator A5047150626 @default.
- W3119443645 creator A5047443680 @default.
- W3119443645 creator A5066554974 @default.
- W3119443645 creator A5075678132 @default.
- W3119443645 date "2021-03-01" @default.
- W3119443645 modified "2023-10-16" @default.
- W3119443645 title "Ferroelectric and nano-mechanical properties of the chemical solution deposited lead-free BCZT films" @default.
- W3119443645 cites W1876611095 @default.
- W3119443645 cites W1967110057 @default.
- W3119443645 cites W1973634915 @default.
- W3119443645 cites W1974340702 @default.
- W3119443645 cites W1990425363 @default.
- W3119443645 cites W1992206315 @default.
- W3119443645 cites W2000601457 @default.
- W3119443645 cites W2000828375 @default.
- W3119443645 cites W2002316964 @default.
- W3119443645 cites W2031750630 @default.
- W3119443645 cites W2033879012 @default.
- W3119443645 cites W2040237037 @default.
- W3119443645 cites W2047542304 @default.
- W3119443645 cites W2050933675 @default.
- W3119443645 cites W2054445416 @default.
- W3119443645 cites W2059929984 @default.
- W3119443645 cites W2086933933 @default.
- W3119443645 cites W2087735078 @default.
- W3119443645 cites W2095672668 @default.
- W3119443645 cites W2102479576 @default.
- W3119443645 cites W2103286753 @default.
- W3119443645 cites W2134795691 @default.
- W3119443645 cites W2137667074 @default.
- W3119443645 cites W2148822556 @default.
- W3119443645 cites W2149218247 @default.
- W3119443645 cites W2165860870 @default.
- W3119443645 cites W2204572701 @default.
- W3119443645 cites W2572393558 @default.
- W3119443645 cites W2802097152 @default.
- W3119443645 cites W2805400282 @default.
- W3119443645 cites W2885716202 @default.
- W3119443645 cites W2943238428 @default.
- W3119443645 cites W2979992981 @default.
- W3119443645 cites W3140341656 @default.
- W3119443645 doi "https://doi.org/10.1016/j.mseb.2020.115037" @default.
- W3119443645 hasPublicationYear "2021" @default.
- W3119443645 type Work @default.
- W3119443645 sameAs 3119443645 @default.
- W3119443645 citedByCount "2" @default.
- W3119443645 countsByYear W31194436452022 @default.
- W3119443645 countsByYear W31194436452023 @default.
- W3119443645 crossrefType "journal-article" @default.
- W3119443645 hasAuthorship W3119443645A5022727233 @default.
- W3119443645 hasAuthorship W3119443645A5047150626 @default.
- W3119443645 hasAuthorship W3119443645A5047443680 @default.
- W3119443645 hasAuthorship W3119443645A5066554974 @default.
- W3119443645 hasAuthorship W3119443645A5075678132 @default.
- W3119443645 hasConcept C133386390 @default.
- W3119443645 hasConcept C159985019 @default.
- W3119443645 hasConcept C192562407 @default.
- W3119443645 hasConcept C193867417 @default.
- W3119443645 hasConcept C2777855556 @default.
- W3119443645 hasConcept C2780357685 @default.
- W3119443645 hasConcept C43486711 @default.
- W3119443645 hasConcept C49040817 @default.
- W3119443645 hasConcept C79090758 @default.
- W3119443645 hasConcept C87976508 @default.
- W3119443645 hasConcept C91066073 @default.
- W3119443645 hasConceptScore W3119443645C133386390 @default.
- W3119443645 hasConceptScore W3119443645C159985019 @default.
- W3119443645 hasConceptScore W3119443645C192562407 @default.
- W3119443645 hasConceptScore W3119443645C193867417 @default.
- W3119443645 hasConceptScore W3119443645C2777855556 @default.
- W3119443645 hasConceptScore W3119443645C2780357685 @default.
- W3119443645 hasConceptScore W3119443645C43486711 @default.
- W3119443645 hasConceptScore W3119443645C49040817 @default.
- W3119443645 hasConceptScore W3119443645C79090758 @default.
- W3119443645 hasConceptScore W3119443645C87976508 @default.
- W3119443645 hasConceptScore W3119443645C91066073 @default.
- W3119443645 hasLocation W31194436451 @default.
- W3119443645 hasOpenAccess W3119443645 @default.
- W3119443645 hasPrimaryLocation W31194436451 @default.
- W3119443645 hasRelatedWork W1495947988 @default.
- W3119443645 hasRelatedWork W1978368497 @default.
- W3119443645 hasRelatedWork W1979981191 @default.
- W3119443645 hasRelatedWork W1993148241 @default.
- W3119443645 hasRelatedWork W1994753809 @default.
- W3119443645 hasRelatedWork W2010390859 @default.
- W3119443645 hasRelatedWork W2011411333 @default.
- W3119443645 hasRelatedWork W2043673973 @default.
- W3119443645 hasRelatedWork W2049363578 @default.
- W3119443645 hasRelatedWork W2364566157 @default.
- W3119443645 hasVolume "265" @default.
- W3119443645 isParatext "false" @default.
- W3119443645 isRetracted "false" @default.
- W3119443645 magId "3119443645" @default.
- W3119443645 workType "article" @default.