- W3128011662 abstract "OBJECTIVE The aim of the present study was to evaluate the effect of different pHs (4.4, 5.4, 6.4, 7.4, 8.4, and 9.4) and three different particle sizes of bismuth oxide on diametral tensile strength (DTS) of white Mineral Trioxide Aggregate (WMTA). METHODS Thirty cylindrical moulds were divided into six groups of five; WMTA was mixed, placed inside the moulds, and wrapped in pieces of gauze soaked in synthetic tissue fluid (STF) with pH values of either 4.4, 5.4, 6.4, 7.4, 8.4, 9.4. For bismuth oxide, eighteen similar molds were divided into three groups of six (n=6). Then bismuth oxide with three particle sizes, including fine (120 nm), medium (200 nm), and coarse (10 μm), were provided and added to the Portland cement, which did not have any bismuth oxide to create WMTA. Then WMTA was mixed, placed inside cylindrical molds. After incubation at 95% humidity for 48 hours, samples were subjected to DTS testing by an Instron Universal testing machine with a crosshead speed of 1 mm/min. Then, one sample from each group was subjected to scanning electron microscope (SEM) analysis. Data were analysed by ANOVA and Tukey tests (α=0.05). RESULTS The comparison of DTS in pH groups were: 8.4>7.4>9.4>6.4>5.4>4.4 (P medium particles > coarse particles (P<0.05). Acidic pH, negatively affected the distribution of Ca2+ and Si4+ ions, while bismuth oxide with fine particles enhanced it. CONCLUSION Acidic pH can decline the DTS of MTA significantly. However, reducing the particle size of bismuth oxide can increase the DTS of MTA significantly." @default.
- W3128011662 created "2021-02-15" @default.
- W3128011662 creator A5006095966 @default.
- W3128011662 creator A5033297443 @default.
- W3128011662 creator A5042494399 @default.
- W3128011662 creator A5044634660 @default.
- W3128011662 creator A5070001356 @default.
- W3128011662 date "2021-01-01" @default.
- W3128011662 modified "2023-09-24" @default.
- W3128011662 title "The pH and Bismuth Oxide Particle Size Can Affect Diametral Tensile Strength of Mineral Trioxide Aggregate" @default.
- W3128011662 doi "https://doi.org/10.14744/eej.2021.27136" @default.
- W3128011662 hasPubMedCentralId "https://www.ncbi.nlm.nih.gov/pmc/articles/8461494" @default.
- W3128011662 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/34047298" @default.
- W3128011662 hasPublicationYear "2021" @default.
- W3128011662 type Work @default.
- W3128011662 sameAs 3128011662 @default.
- W3128011662 citedByCount "1" @default.
- W3128011662 countsByYear W31280116622022 @default.
- W3128011662 crossrefType "journal-article" @default.
- W3128011662 hasAuthorship W3128011662A5006095966 @default.
- W3128011662 hasAuthorship W3128011662A5033297443 @default.
- W3128011662 hasAuthorship W3128011662A5042494399 @default.
- W3128011662 hasAuthorship W3128011662A5044634660 @default.
- W3128011662 hasAuthorship W3128011662A5070001356 @default.
- W3128011662 hasBestOaLocation W31280116622 @default.
- W3128011662 hasConcept C112950240 @default.
- W3128011662 hasConcept C127413603 @default.
- W3128011662 hasConcept C159985019 @default.
- W3128011662 hasConcept C187530423 @default.
- W3128011662 hasConcept C191897082 @default.
- W3128011662 hasConcept C192562407 @default.
- W3128011662 hasConcept C199343813 @default.
- W3128011662 hasConcept C2776432453 @default.
- W3128011662 hasConcept C2777090975 @default.
- W3128011662 hasConcept C42360764 @default.
- W3128011662 hasConcept C4679612 @default.
- W3128011662 hasConcept C533668322 @default.
- W3128011662 hasConcept C71924100 @default.
- W3128011662 hasConceptScore W3128011662C112950240 @default.
- W3128011662 hasConceptScore W3128011662C127413603 @default.
- W3128011662 hasConceptScore W3128011662C159985019 @default.
- W3128011662 hasConceptScore W3128011662C187530423 @default.
- W3128011662 hasConceptScore W3128011662C191897082 @default.
- W3128011662 hasConceptScore W3128011662C192562407 @default.
- W3128011662 hasConceptScore W3128011662C199343813 @default.
- W3128011662 hasConceptScore W3128011662C2776432453 @default.
- W3128011662 hasConceptScore W3128011662C2777090975 @default.
- W3128011662 hasConceptScore W3128011662C42360764 @default.
- W3128011662 hasConceptScore W3128011662C4679612 @default.
- W3128011662 hasConceptScore W3128011662C533668322 @default.
- W3128011662 hasConceptScore W3128011662C71924100 @default.
- W3128011662 hasLocation W31280116621 @default.
- W3128011662 hasLocation W31280116622 @default.
- W3128011662 hasLocation W31280116623 @default.
- W3128011662 hasOpenAccess W3128011662 @default.
- W3128011662 hasPrimaryLocation W31280116621 @default.
- W3128011662 hasRelatedWork W1975608897 @default.
- W3128011662 hasRelatedWork W2044949441 @default.
- W3128011662 hasRelatedWork W2089085266 @default.
- W3128011662 hasRelatedWork W2111421561 @default.
- W3128011662 hasRelatedWork W2229503843 @default.
- W3128011662 hasRelatedWork W2363203688 @default.
- W3128011662 hasRelatedWork W2795554382 @default.
- W3128011662 hasRelatedWork W3122552578 @default.
- W3128011662 hasRelatedWork W4281567869 @default.
- W3128011662 hasRelatedWork W4285731133 @default.
- W3128011662 isParatext "false" @default.
- W3128011662 isRetracted "false" @default.
- W3128011662 magId "3128011662" @default.
- W3128011662 workType "article" @default.