- W3131408352 abstract "A comparative study of metal removal in ferric chloride solution has been completed. The purpose of this study is the effect of acid solution cause material removal of various types of metals such as steel, iron, aluminum and tin. Previously this plate had been prepared by determine the dimensions of the plate size, plate mass and ensuring the plate surface is flat. After that, the plates were immersed in ferric chloride solution with a solution percentage of 27% gram / ml in water for 2 hours. Metal plates had been cleaned and dried and then carried out post-immersion measurements for plate mass, plate dimensions, solution temperature and the acidity of the solution. The result of measurement show the metal plates of steel, iron, aluminum and tin have removed material with a depth of 0.350 mm; 0.550 mm; 0.5625 mm and 0.665 mm. The mass lost after immersion in ferric chloride solution was 2.2 g; 3.9 g; 3.6 g and 7.6 g. Through Faraday's Law, it has been found that the calculation of the material removal rate (MRR) is 0.140 cm3/hour; 0.252 cm3/hour; 0.667 cm3/hour and 0.659 cm3/hour. This has shown the acid solution can remove the metal surface,when the density of the metal is large, material removal rate is low. Therefore, further studies are needed to observe the presence of impurities in the plate and the surface roughness of the metal plate after immersion." @default.
- W3131408352 created "2021-03-01" @default.
- W3131408352 creator A5076906280 @default.
- W3131408352 date "2021-02-14" @default.
- W3131408352 modified "2023-09-26" @default.
- W3131408352 title "PERBANDINGAN KEDALAMAN PENGIKISAN LOGAM DALAM LARUTAN FERI KLORIDA" @default.
- W3131408352 doi "https://doi.org/10.22373/crc.v5i1.8472" @default.
- W3131408352 hasPublicationYear "2021" @default.
- W3131408352 type Work @default.
- W3131408352 sameAs 3131408352 @default.
- W3131408352 citedByCount "0" @default.
- W3131408352 crossrefType "journal-article" @default.
- W3131408352 hasAuthorship W3131408352A5076906280 @default.
- W3131408352 hasBestOaLocation W31314083521 @default.
- W3131408352 hasConcept C113196181 @default.
- W3131408352 hasConcept C116628846 @default.
- W3131408352 hasConcept C13965031 @default.
- W3131408352 hasConcept C159985019 @default.
- W3131408352 hasConcept C178790620 @default.
- W3131408352 hasConcept C185592680 @default.
- W3131408352 hasConcept C191897082 @default.
- W3131408352 hasConcept C192562407 @default.
- W3131408352 hasConcept C2778695967 @default.
- W3131408352 hasConcept C2780534640 @default.
- W3131408352 hasConcept C43617362 @default.
- W3131408352 hasConcept C513153333 @default.
- W3131408352 hasConcept C525849907 @default.
- W3131408352 hasConcept C544153396 @default.
- W3131408352 hasConcept C71987851 @default.
- W3131408352 hasConceptScore W3131408352C113196181 @default.
- W3131408352 hasConceptScore W3131408352C116628846 @default.
- W3131408352 hasConceptScore W3131408352C13965031 @default.
- W3131408352 hasConceptScore W3131408352C159985019 @default.
- W3131408352 hasConceptScore W3131408352C178790620 @default.
- W3131408352 hasConceptScore W3131408352C185592680 @default.
- W3131408352 hasConceptScore W3131408352C191897082 @default.
- W3131408352 hasConceptScore W3131408352C192562407 @default.
- W3131408352 hasConceptScore W3131408352C2778695967 @default.
- W3131408352 hasConceptScore W3131408352C2780534640 @default.
- W3131408352 hasConceptScore W3131408352C43617362 @default.
- W3131408352 hasConceptScore W3131408352C513153333 @default.
- W3131408352 hasConceptScore W3131408352C525849907 @default.
- W3131408352 hasConceptScore W3131408352C544153396 @default.
- W3131408352 hasConceptScore W3131408352C71987851 @default.
- W3131408352 hasLocation W31314083521 @default.
- W3131408352 hasOpenAccess W3131408352 @default.
- W3131408352 hasPrimaryLocation W31314083521 @default.
- W3131408352 hasRelatedWork W10194799 @default.
- W3131408352 hasRelatedWork W1171662 @default.
- W3131408352 hasRelatedWork W14835697 @default.
- W3131408352 hasRelatedWork W14877814 @default.
- W3131408352 hasRelatedWork W1532551 @default.
- W3131408352 hasRelatedWork W2390660 @default.
- W3131408352 hasRelatedWork W3992793 @default.
- W3131408352 hasRelatedWork W6836937 @default.
- W3131408352 hasRelatedWork W7995941 @default.
- W3131408352 hasRelatedWork W17429724 @default.
- W3131408352 isParatext "false" @default.
- W3131408352 isRetracted "false" @default.
- W3131408352 magId "3131408352" @default.
- W3131408352 workType "article" @default.