- W3133465166 abstract "The present study evaluated CFRP and SPCC hybrid laminates by combined experimental and simulation analysis. The results showed that the strength of hybrid laminate [SPCC/[0]n]S increased more than 100% from 1000 MPa (0.5 mm thickness) compared to 2000 MPa (2 mm thickness). Moreover, by setting the volume fraction of hybrid laminates, the strength can increase from under 500 MPa to more than 3000 MPa with a minimum changed in strain performance. In other results, the effect of temperature differences during the manufacturing process is investigated. The analysis related to the operational temperature that used different material combinations was also evaluated. The band of temperature is varying from as high as 45 °C to as low as −45 °C. The outcomes demonstrate that the range of maximum strain of laminate from 45 °C to −45 °C can up to 0.1% of strain. Further analysis with a comparison regarding the angle effect of hybrid laminates with residual compressive stress and the curing temperature was also evaluated. The waviness trend shows higher when the temperature is set higher, and vice versa. The experimental results indicate good agreement with simulation results. Moreover, the analysis based on cost assessment was included and compared with other mechanical properties." @default.
- W3133465166 created "2021-03-01" @default.
- W3133465166 creator A5032140853 @default.
- W3133465166 creator A5059502977 @default.
- W3133465166 date "2021-05-01" @default.
- W3133465166 modified "2023-10-02" @default.
- W3133465166 title "Experimental and numerical analysis of CFRP-SPCC hybrid laminates for automotive and structural applications with cost analysis assessment" @default.
- W3133465166 cites W1778002070 @default.
- W3133465166 cites W190203132 @default.
- W3133465166 cites W2002337658 @default.
- W3133465166 cites W2013598542 @default.
- W3133465166 cites W2019650856 @default.
- W3133465166 cites W2049756826 @default.
- W3133465166 cites W2056406701 @default.
- W3133465166 cites W2057073075 @default.
- W3133465166 cites W2073082009 @default.
- W3133465166 cites W2099079993 @default.
- W3133465166 cites W2152698831 @default.
- W3133465166 cites W2323092461 @default.
- W3133465166 cites W2342521513 @default.
- W3133465166 cites W2370999869 @default.
- W3133465166 cites W2420613912 @default.
- W3133465166 cites W2591958438 @default.
- W3133465166 cites W2605036234 @default.
- W3133465166 cites W2755645881 @default.
- W3133465166 cites W2767788747 @default.
- W3133465166 cites W2783470494 @default.
- W3133465166 cites W2889433051 @default.
- W3133465166 cites W2897750568 @default.
- W3133465166 cites W2919165349 @default.
- W3133465166 cites W2920959188 @default.
- W3133465166 cites W2923052517 @default.
- W3133465166 cites W2935478696 @default.
- W3133465166 cites W2940028176 @default.
- W3133465166 cites W2944544663 @default.
- W3133465166 cites W2954568984 @default.
- W3133465166 cites W2981914195 @default.
- W3133465166 cites W2983885359 @default.
- W3133465166 cites W2990051486 @default.
- W3133465166 cites W2999139758 @default.
- W3133465166 cites W2999398113 @default.
- W3133465166 cites W3000741808 @default.
- W3133465166 cites W3001741485 @default.
- W3133465166 cites W4244649830 @default.
- W3133465166 doi "https://doi.org/10.1016/j.compstruct.2021.113707" @default.
- W3133465166 hasPublicationYear "2021" @default.
- W3133465166 type Work @default.
- W3133465166 sameAs 3133465166 @default.
- W3133465166 citedByCount "24" @default.
- W3133465166 countsByYear W31334651662021 @default.
- W3133465166 countsByYear W31334651662022 @default.
- W3133465166 countsByYear W31334651662023 @default.
- W3133465166 crossrefType "journal-article" @default.
- W3133465166 hasAuthorship W3133465166A5032140853 @default.
- W3133465166 hasAuthorship W3133465166A5059502977 @default.
- W3133465166 hasConcept C132976073 @default.
- W3133465166 hasConcept C159985019 @default.
- W3133465166 hasConcept C192562407 @default.
- W3133465166 hasConcept C20965850 @default.
- W3133465166 hasConcept C2777701225 @default.
- W3133465166 hasConcept C37292000 @default.
- W3133465166 hasConcept C65590680 @default.
- W3133465166 hasConceptScore W3133465166C132976073 @default.
- W3133465166 hasConceptScore W3133465166C159985019 @default.
- W3133465166 hasConceptScore W3133465166C192562407 @default.
- W3133465166 hasConceptScore W3133465166C20965850 @default.
- W3133465166 hasConceptScore W3133465166C2777701225 @default.
- W3133465166 hasConceptScore W3133465166C37292000 @default.
- W3133465166 hasConceptScore W3133465166C65590680 @default.
- W3133465166 hasLocation W31334651661 @default.
- W3133465166 hasOpenAccess W3133465166 @default.
- W3133465166 hasPrimaryLocation W31334651661 @default.
- W3133465166 hasRelatedWork W1992869483 @default.
- W3133465166 hasRelatedWork W2004362670 @default.
- W3133465166 hasRelatedWork W2078945242 @default.
- W3133465166 hasRelatedWork W2350972785 @default.
- W3133465166 hasRelatedWork W2389140591 @default.
- W3133465166 hasRelatedWork W3087783407 @default.
- W3133465166 hasRelatedWork W3172622391 @default.
- W3133465166 hasRelatedWork W3212773040 @default.
- W3133465166 hasRelatedWork W4245667518 @default.
- W3133465166 hasRelatedWork W4320034603 @default.
- W3133465166 hasVolume "263" @default.
- W3133465166 isParatext "false" @default.
- W3133465166 isRetracted "false" @default.
- W3133465166 magId "3133465166" @default.
- W3133465166 workType "article" @default.