- W3134275793 abstract "In this work, BaTiO3 and Ba(MgxZr0.15Ti0.85-x)O3, (x = 0.005, 0.015, 0.025) ceramics were fabricated by a solid-state sintering route. All of the samples derived a single tetragonal perovskite structure. No significant impurity phases were indicated. A grain growth retardation phenomenon was observed. BaMg0.015Zr0.15Ti0.835O3 ceramics exhibited a maximum dielectric constant of 2010.18 at 102 Hz, showing a strong dependency on crystallite size (36.79 nm). The conductivity of the specimens was mainly due to polaron hopping, while the exponential conductivity factor ranged from 0.96123 to 1.00000. BaMg0.005Zr0.15Ti0.845O3 ceramics showed the lowest electrical resistivity (1.09 Ω-m at 102 Hz) due to its maximum grain size (873.72 nm). Although the complex impedance spectra was a straight line for BaTiO3 ceramics, it became a semicircle for Ba(MgxZr0.15Ti0.85-x)O3 ceramics exhibiting the presence of equal resistance into the grains and grain boundaries. The maximum remnant polarization (44.04 μC/cm2 for loop-5) with a coercive field of 1.67 kV/cm was observed into BaMg0.015Zr0.15Ti0.835O3 ceramics. The obtained optical band gap energy for BaTiO3 was 3.12 eV while the value for BaMg0.005Zr0.15Ti0.845O3, BaMg0.015Zr0.15Ti0.835O3, and BaMg0.025Zr0.15Ti0.825O3 ceramics were 3.10 eV, 3.06 eV and 3.23 eV respectively. Although BaMg0.015Zr0.15Ti0.835O3 ceramics demonstrated the extraordinary electrical and optical properties, the obtained results in BaMg0.005Zr0.15Ti0.845O3 specimens were satisfactory." @default.
- W3134275793 created "2021-03-15" @default.
- W3134275793 creator A5004348794 @default.
- W3134275793 creator A5036821657 @default.
- W3134275793 creator A5083457584 @default.
- W3134275793 creator A5084720851 @default.
- W3134275793 date "2021-06-01" @default.
- W3134275793 modified "2023-09-27" @default.
- W3134275793 title "Enhanced dielectric, ferroelectric and optical properties of Ba(Zr0.15Ti0.85)O3 ceramics incorporated with MgO" @default.
- W3134275793 cites W1913777984 @default.
- W3134275793 cites W1983150232 @default.
- W3134275793 cites W1985411038 @default.
- W3134275793 cites W1992174038 @default.
- W3134275793 cites W1992456606 @default.
- W3134275793 cites W1992774584 @default.
- W3134275793 cites W1999241407 @default.
- W3134275793 cites W2007109683 @default.
- W3134275793 cites W2011154106 @default.
- W3134275793 cites W2012901673 @default.
- W3134275793 cites W2022348818 @default.
- W3134275793 cites W2023165684 @default.
- W3134275793 cites W2035037381 @default.
- W3134275793 cites W2037771996 @default.
- W3134275793 cites W2052528601 @default.
- W3134275793 cites W2061082910 @default.
- W3134275793 cites W2067923693 @default.
- W3134275793 cites W2071901775 @default.
- W3134275793 cites W2072330913 @default.
- W3134275793 cites W2075795858 @default.
- W3134275793 cites W2077756429 @default.
- W3134275793 cites W2130392400 @default.
- W3134275793 cites W2135934271 @default.
- W3134275793 cites W2140620248 @default.
- W3134275793 cites W2152031732 @default.
- W3134275793 cites W2167590372 @default.
- W3134275793 cites W2227101482 @default.
- W3134275793 cites W2319943481 @default.
- W3134275793 cites W2516276296 @default.
- W3134275793 cites W2749254445 @default.
- W3134275793 cites W2767130926 @default.
- W3134275793 cites W2773981045 @default.
- W3134275793 cites W2792828446 @default.
- W3134275793 cites W2793582870 @default.
- W3134275793 cites W2799839914 @default.
- W3134275793 cites W2802747389 @default.
- W3134275793 cites W2882995569 @default.
- W3134275793 cites W2901974870 @default.
- W3134275793 cites W2950064756 @default.
- W3134275793 cites W3011782258 @default.
- W3134275793 cites W4244401340 @default.
- W3134275793 cites W828363751 @default.
- W3134275793 cites W980467359 @default.
- W3134275793 doi "https://doi.org/10.1016/j.rinma.2021.100176" @default.
- W3134275793 hasPublicationYear "2021" @default.
- W3134275793 type Work @default.
- W3134275793 sameAs 3134275793 @default.
- W3134275793 citedByCount "2" @default.
- W3134275793 countsByYear W31342757932022 @default.
- W3134275793 crossrefType "journal-article" @default.
- W3134275793 hasAuthorship W3134275793A5004348794 @default.
- W3134275793 hasAuthorship W3134275793A5036821657 @default.
- W3134275793 hasAuthorship W3134275793A5083457584 @default.
- W3134275793 hasAuthorship W3134275793A5084720851 @default.
- W3134275793 hasBestOaLocation W31342757931 @default.
- W3134275793 hasConcept C113196181 @default.
- W3134275793 hasConcept C115624301 @default.
- W3134275793 hasConcept C119599485 @default.
- W3134275793 hasConcept C121332964 @default.
- W3134275793 hasConcept C126530901 @default.
- W3134275793 hasConcept C127413603 @default.
- W3134275793 hasConcept C133386390 @default.
- W3134275793 hasConcept C134132462 @default.
- W3134275793 hasConcept C137637335 @default.
- W3134275793 hasConcept C159985019 @default.
- W3134275793 hasConcept C170751736 @default.
- W3134275793 hasConcept C181966813 @default.
- W3134275793 hasConcept C185592680 @default.
- W3134275793 hasConcept C191897082 @default.
- W3134275793 hasConcept C192191005 @default.
- W3134275793 hasConcept C192562407 @default.
- W3134275793 hasConcept C199289684 @default.
- W3134275793 hasConcept C26873012 @default.
- W3134275793 hasConcept C43617362 @default.
- W3134275793 hasConcept C47908070 @default.
- W3134275793 hasConcept C49040817 @default.
- W3134275793 hasConcept C69990965 @default.
- W3134275793 hasConcept C79090758 @default.
- W3134275793 hasConcept C8010536 @default.
- W3134275793 hasConcept C87976508 @default.
- W3134275793 hasConceptScore W3134275793C113196181 @default.
- W3134275793 hasConceptScore W3134275793C115624301 @default.
- W3134275793 hasConceptScore W3134275793C119599485 @default.
- W3134275793 hasConceptScore W3134275793C121332964 @default.
- W3134275793 hasConceptScore W3134275793C126530901 @default.
- W3134275793 hasConceptScore W3134275793C127413603 @default.
- W3134275793 hasConceptScore W3134275793C133386390 @default.
- W3134275793 hasConceptScore W3134275793C134132462 @default.
- W3134275793 hasConceptScore W3134275793C137637335 @default.