• W3134700577 abstract "In this paper, the microstructures, mechanical properties, and corrosion behavior of xTiB2/Al–9Si–3Cu-0.8Zn composites after T6 heat treatment were invested in detail through the combination of different technologies, including optical microscopy (OM), X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), tensile testing, corrosion testing, etc. The research results showed that the average size of the α-Al grains gradually decreased with the increase of TiB2 particles (TiB2p) content. In addition, there was a semi-coherent relationship between TiB2p and the α-Al matrix, and the nanoscale precipitates were identified as θ and θʹ phases by virtue of their crystal orientation relationship. Tensile testing results revealed that an increase in TiB2 content caused the elastic modulus, yield strength and tensile strength of the composites to increase and then decrease. And with a TiB2p content of 4 wt%, they reached 85.7 GPa, 360 MPa and 398 MPa, reflecting increases of 26.2%, 60.0%, and 30.9%, respectively. The contributions of thermal mismatch, grain boundary and Orowan strengthening mechanisms to the overall yield strength of the 4%TiB2/Al–9Si–3Cu–0.8Zn composite were 72.1, 3.8, and 35.6 MPa, respectively. Unfortunately, the corrosion resistance of xTiB2/Al–9Si–3Cu–0.8Zn composites gradually decreased with increasing TiB2p content. The corrosion morphology analysis indicated that the agglomeration of TiB2p and Si weakened the protection afforded by the oxide film, evolving into a point of nucleation for the subsequent corrosion reaction. Moreover, point–pair correlation was observed between the TiB2p and Al matrix, exacerbating the corrosion. The results implied that extra factors be considered in industrial application of TiB2 ceramic particles in a metallic system." @default.
• W3134700577 created "2021-03-15" @default.
• W3134700577 creator A5014249241 @default.
• W3134700577 creator A5043019475 @default.
• W3134700577 creator A5049199995 @default.
• W3134700577 creator A5052807371 @default.
• W3134700577 creator A5064906187 @default.
• W3134700577 date "2021-05-01" @default.
• W3134700577 modified "2023-10-16" @default.
• W3134700577 title "Investigate on the phase interfaces and performance evaluation of TiB2p/Al–Si–Cu–Zn (T6) composites" @default.
• W3134700577 cites W1768809741 @default.
• W3134700577 cites W1997981474 @default.
• W3134700577 cites W2011613789 @default.
• W3134700577 cites W2012692543 @default.
• W3134700577 cites W2030850606 @default.
• W3134700577 cites W2066759175 @default.
• W3134700577 cites W2068600858 @default.
• W3134700577 cites W2069386992 @default.
• W3134700577 cites W2135834532 @default.
• W3134700577 cites W2182721627 @default.
• W3134700577 cites W2197810634 @default.
• W3134700577 cites W2289997790 @default.
• W3134700577 cites W2461890763 @default.
• W3134700577 cites W2518545394 @default.
• W3134700577 cites W2528191610 @default.
• W3134700577 cites W2592489731 @default.
• W3134700577 cites W2605503884 @default.
• W3134700577 cites W2728999230 @default.
• W3134700577 cites W2747886696 @default.
• W3134700577 cites W2760744731 @default.
• W3134700577 cites W2792492831 @default.
• W3134700577 cites W2793367117 @default.
• W3134700577 cites W2793747686 @default.
• W3134700577 cites W2801979784 @default.
• W3134700577 cites W2809323754 @default.
• W3134700577 cites W2890837702 @default.
• W3134700577 cites W2902025479 @default.
• W3134700577 cites W2903715250 @default.
• W3134700577 cites W2907726984 @default.
• W3134700577 cites W2921108195 @default.
• W3134700577 cites W2950825468 @default.
• W3134700577 cites W2953260356 @default.
• W3134700577 cites W2958842195 @default.
• W3134700577 cites W2971781345 @default.
• W3134700577 cites W3004644594 @default.
• W3134700577 cites W3033953747 @default.
• W3134700577 cites W3080554826 @default.
• W3134700577 cites W3094160335 @default.
• W3134700577 cites W44076650 @default.
• W3134700577 doi "https://doi.org/10.1016/j.jmrt.2021.03.018" @default.
• W3134700577 hasPublicationYear "2021" @default.
• W3134700577 type Work @default.
• W3134700577 sameAs 3134700577 @default.
• W3134700577 citedByCount "8" @default.
• W3134700577 countsByYear W31347005772021 @default.
• W3134700577 countsByYear W31347005772022 @default.
• W3134700577 countsByYear W31347005772023 @default.
• W3134700577 crossrefType "journal-article" @default.
• W3134700577 hasAuthorship W3134700577A5014249241 @default.
• W3134700577 hasAuthorship W3134700577A5043019475 @default.
• W3134700577 hasAuthorship W3134700577A5049199995 @default.
• W3134700577 hasAuthorship W3134700577A5052807371 @default.
• W3134700577 hasAuthorship W3134700577A5064906187 @default.
• W3134700577 hasBestOaLocation W31347005771 @default.
• W3134700577 hasConcept C104779481 @default.
• W3134700577 hasConcept C112950240 @default.
• W3134700577 hasConcept C146088050 @default.
• W3134700577 hasConcept C159985019 @default.
• W3134700577 hasConcept C171250308 @default.
• W3134700577 hasConcept C178790620 @default.
• W3134700577 hasConcept C185592680 @default.
• W3134700577 hasConcept C192562407 @default.
• W3134700577 hasConcept C20625102 @default.
• W3134700577 hasConcept C26771246 @default.
• W3134700577 hasConcept C44280652 @default.
• W3134700577 hasConcept C47908070 @default.
• W3134700577 hasConcept C61048295 @default.
• W3134700577 hasConcept C87976508 @default.
• W3134700577 hasConceptScore W3134700577C104779481 @default.
• W3134700577 hasConceptScore W3134700577C112950240 @default.
• W3134700577 hasConceptScore W3134700577C146088050 @default.
• W3134700577 hasConceptScore W3134700577C159985019 @default.
• W3134700577 hasConceptScore W3134700577C171250308 @default.
• W3134700577 hasConceptScore W3134700577C178790620 @default.
• W3134700577 hasConceptScore W3134700577C185592680 @default.
• W3134700577 hasConceptScore W3134700577C192562407 @default.
• W3134700577 hasConceptScore W3134700577C20625102 @default.
• W3134700577 hasConceptScore W3134700577C26771246 @default.
• W3134700577 hasConceptScore W3134700577C44280652 @default.
• W3134700577 hasConceptScore W3134700577C47908070 @default.
• W3134700577 hasConceptScore W3134700577C61048295 @default.
• W3134700577 hasConceptScore W3134700577C87976508 @default.
• W3134700577 hasFunder F4320321001 @default.
• W3134700577 hasLocation W31347005771 @default.
• W3134700577 hasOpenAccess W3134700577 @default.
• W3134700577 hasPrimaryLocation W31347005771 @default.
• W3134700577 hasRelatedWork W1984931024 @default.
• W3134700577 hasRelatedWork W2033388865 @default.

• next