• W3135766886 abstract "Abstract Al 2 O 3 @CaCO 3 aggregates were prepared by impregnating corundum aggregates (particle sizes with 3‐1 and 5‐3 mm) in precursor solutions (Calcium hydrogen citrate, CaHC 6 H 5 O 7 ) followed by heat treatment at 430°C. The phase composition and microstructure of the coatings were characterized via X‐ray diffraction and scanning electron microscope, respectively. The novel aggregates were used in Al 2 O 3 ‐MgO castables. The effects of the Al 2 O 3 @CaCO 3 aggregates on the physical properties and thermal shock resistance (TSR) of castables were investigated. The results show that uniform CaCO 3 coating of aggregates (C15) with thickness about 10 µm can be attained when the concentration of Ca 2+ in solution was 0.15 mol L −1 . There was a strong bonding between the aggregates and coating that was constituted by particles with size about 0.2 µm. Both improving physical and TSR properties of the castables are related with the unique layer structure, calcium hexaluminate (CA 6 ) layer in‐situ formed at the aggregate‐matrix interface, of added Al 2 O 3 @CaCO 3 aggregates. There is a mass of multi‐deflection of cracks along with the CA 6 layer which consumes more fracture surface energy. The castables with C15 exhibit optimal TSR and the residual strength ratio after the thermal shock test is 29.5%, which is 12.8% higher than the castables with corundum aggregates." @default.
• W3135766886 created "2021-03-15" @default.
• W3135766886 creator A5005988997 @default.
• W3135766886 creator A5009975007 @default.
• W3135766886 creator A5029477125 @default.
• W3135766886 creator A5060497481 @default.
• W3135766886 creator A5075594387 @default.
• W3135766886 creator A5078936716 @default.
• W3135766886 creator A5079027605 @default.
• W3135766886 date "2021-04-17" @default.
• W3135766886 modified "2023-10-17" @default.
• W3135766886 title "Preparation of Al₂O₃@CaCO₃ aggregates and its effects on the thermal shock resistance of Al₂O₃‐MgO castables" @default.
• W3135766886 cites W1662202094 @default.
• W3135766886 cites W1969027244 @default.
• W3135766886 cites W1986101489 @default.
• W3135766886 cites W1988520560 @default.
• W3135766886 cites W1994688305 @default.
• W3135766886 cites W1999225745 @default.
• W3135766886 cites W2002208127 @default.
• W3135766886 cites W2004306671 @default.
• W3135766886 cites W2034060281 @default.
• W3135766886 cites W2044403699 @default.
• W3135766886 cites W2046477349 @default.
• W3135766886 cites W2047646669 @default.
• W3135766886 cites W2049582094 @default.
• W3135766886 cites W2059402680 @default.
• W3135766886 cites W2079198044 @default.
• W3135766886 cites W2085519654 @default.
• W3135766886 cites W2104115092 @default.
• W3135766886 cites W2125595177 @default.
• W3135766886 cites W2171787540 @default.
• W3135766886 cites W2302412746 @default.
• W3135766886 cites W2460700625 @default.
• W3135766886 cites W2577082987 @default.
• W3135766886 cites W2620993502 @default.
• W3135766886 cites W2732902352 @default.
• W3135766886 cites W2793858903 @default.
• W3135766886 cites W2799596492 @default.
• W3135766886 cites W2800250980 @default.
• W3135766886 cites W2803339393 @default.
• W3135766886 cites W2884214646 @default.
• W3135766886 cites W2885020869 @default.
• W3135766886 cites W2891740191 @default.
• W3135766886 cites W2922728161 @default.
• W3135766886 cites W2944277742 @default.
• W3135766886 cites W2981441418 @default.
• W3135766886 cites W2981811192 @default.
• W3135766886 cites W2990811285 @default.
• W3135766886 cites W2996833580 @default.
• W3135766886 cites W2999004598 @default.
• W3135766886 cites W3023320585 @default.
• W3135766886 cites W3033152608 @default.
• W3135766886 cites W2066315848 @default.
• W3135766886 doi "https://doi.org/10.1111/ijac.13745" @default.
• W3135766886 hasPublicationYear "2021" @default.
• W3135766886 type Work @default.
• W3135766886 sameAs 3135766886 @default.
• W3135766886 citedByCount "1" @default.
• W3135766886 countsByYear W31357668862023 @default.
• W3135766886 crossrefType "journal-article" @default.
• W3135766886 hasAuthorship W3135766886A5005988997 @default.
• W3135766886 hasAuthorship W3135766886A5009975007 @default.
• W3135766886 hasAuthorship W3135766886A5029477125 @default.
• W3135766886 hasAuthorship W3135766886A5060497481 @default.
• W3135766886 hasAuthorship W3135766886A5075594387 @default.
• W3135766886 hasAuthorship W3135766886A5078936716 @default.
• W3135766886 hasAuthorship W3135766886A5079027605 @default.
• W3135766886 hasConcept C127413603 @default.
• W3135766886 hasConcept C159985019 @default.
• W3135766886 hasConcept C176177977 @default.
• W3135766886 hasConcept C185592680 @default.
• W3135766886 hasConcept C187530423 @default.
• W3135766886 hasConcept C192562407 @default.
• W3135766886 hasConcept C199289684 @default.
• W3135766886 hasConcept C26771246 @default.
• W3135766886 hasConcept C2777519835 @default.
• W3135766886 hasConcept C2781448156 @default.
• W3135766886 hasConcept C42360764 @default.
• W3135766886 hasConcept C87976508 @default.
• W3135766886 hasConceptScore W3135766886C127413603 @default.
• W3135766886 hasConceptScore W3135766886C159985019 @default.
• W3135766886 hasConceptScore W3135766886C176177977 @default.
• W3135766886 hasConceptScore W3135766886C185592680 @default.
• W3135766886 hasConceptScore W3135766886C187530423 @default.
• W3135766886 hasConceptScore W3135766886C192562407 @default.
• W3135766886 hasConceptScore W3135766886C199289684 @default.
• W3135766886 hasConceptScore W3135766886C26771246 @default.
• W3135766886 hasConceptScore W3135766886C2777519835 @default.
• W3135766886 hasConceptScore W3135766886C2781448156 @default.
• W3135766886 hasConceptScore W3135766886C42360764 @default.
• W3135766886 hasConceptScore W3135766886C87976508 @default.
• W3135766886 hasFunder F4320321001 @default.
• W3135766886 hasIssue "4" @default.
• W3135766886 hasLocation W31357668861 @default.
• W3135766886 hasOpenAccess W3135766886 @default.
• W3135766886 hasPrimaryLocation W31357668861 @default.
• W3135766886 hasRelatedWork W2034517149 @default.
• W3135766886 hasRelatedWork W2051157305 @default.

• next