- W3141305998 abstract "La-Ba co-modified alumina was prepared from two kinds of pseudo boehmite and HNO_3 as peptizer by peptizing method.The structure and surface property of the alumina were characterized by XRD,BET surface area analyzer,NH_3-temperature programmed desorpfion and NO_2-temperature programmed desorption technology.XRD results showed thatγ-Al_2O_3 phase existed in all the modified alumina samples after calcination at 1273 K.A little BaCO_3 was generated when content of BaO was increased to 14%(w).BET results showed that both of 5%(w) La_2O_3- modified and 5% La_2O_3-8%BaO co-modified alumina (Ba-8) samples exhibited larger specific surface area and pore volume after calcination at 1273 K.N_2 adsorption and desorption isotherms of all alumina exhibited that their surface pore structure was slit-shape and ink-shape pores,pore diameter distribution of Ba-8 was broader and centered between 5 and 10 nm,and other samples centered at 10 nm.NH_3-TPD results indicated that the larger the BaO doping concentration,the less the acidic amount was.At the same time,surface acidity of alumina apparently became weak. NO_2-TPD results showed that BaO doped alumina adsorbed more NO_2 than La_2O_3 doped,sample Ba-8 adsorbed the most NO_2.As sample Ba-8 simultaneously exhibited good textural properties,proper surface acidic amount,acidity and stronger NO_2 adsorption capacity,it had the best catalytic performance when it was used as catalyst carder.The temperatures of light-off and complete conversion of C_3H_3 were 526 K and 593 K,respectively." @default.
- W3141305998 created "2021-04-13" @default.
- W3141305998 creator A5063496433 @default.
- W3141305998 date "2007-01-01" @default.
- W3141305998 modified "2023-09-25" @default.
- W3141305998 title "Performance of La-Ba Co-modified Alumina Prepared by Peptizing Method" @default.
- W3141305998 hasPublicationYear "2007" @default.
- W3141305998 type Work @default.
- W3141305998 sameAs 3141305998 @default.
- W3141305998 citedByCount "0" @default.
- W3141305998 crossrefType "journal-article" @default.
- W3141305998 hasAuthorship W3141305998A5063496433 @default.
- W3141305998 hasConcept C113196181 @default.
- W3141305998 hasConcept C147789679 @default.
- W3141305998 hasConcept C150394285 @default.
- W3141305998 hasConcept C150581940 @default.
- W3141305998 hasConcept C159985019 @default.
- W3141305998 hasConcept C161790260 @default.
- W3141305998 hasConcept C162711632 @default.
- W3141305998 hasConcept C178790620 @default.
- W3141305998 hasConcept C185592680 @default.
- W3141305998 hasConcept C192562407 @default.
- W3141305998 hasConcept C199289684 @default.
- W3141305998 hasConcept C2777882336 @default.
- W3141305998 hasConcept C27923307 @default.
- W3141305998 hasConcept C43617362 @default.
- W3141305998 hasConcept C44280652 @default.
- W3141305998 hasConcept C49040817 @default.
- W3141305998 hasConcept C513153333 @default.
- W3141305998 hasConcept C57863236 @default.
- W3141305998 hasConcept C7082614 @default.
- W3141305998 hasConceptScore W3141305998C113196181 @default.
- W3141305998 hasConceptScore W3141305998C147789679 @default.
- W3141305998 hasConceptScore W3141305998C150394285 @default.
- W3141305998 hasConceptScore W3141305998C150581940 @default.
- W3141305998 hasConceptScore W3141305998C159985019 @default.
- W3141305998 hasConceptScore W3141305998C161790260 @default.
- W3141305998 hasConceptScore W3141305998C162711632 @default.
- W3141305998 hasConceptScore W3141305998C178790620 @default.
- W3141305998 hasConceptScore W3141305998C185592680 @default.
- W3141305998 hasConceptScore W3141305998C192562407 @default.
- W3141305998 hasConceptScore W3141305998C199289684 @default.
- W3141305998 hasConceptScore W3141305998C2777882336 @default.
- W3141305998 hasConceptScore W3141305998C27923307 @default.
- W3141305998 hasConceptScore W3141305998C43617362 @default.
- W3141305998 hasConceptScore W3141305998C44280652 @default.
- W3141305998 hasConceptScore W3141305998C49040817 @default.
- W3141305998 hasConceptScore W3141305998C513153333 @default.
- W3141305998 hasConceptScore W3141305998C57863236 @default.
- W3141305998 hasConceptScore W3141305998C7082614 @default.
- W3141305998 hasLocation W31413059981 @default.
- W3141305998 hasOpenAccess W3141305998 @default.
- W3141305998 hasPrimaryLocation W31413059981 @default.
- W3141305998 hasRelatedWork W1528502073 @default.
- W3141305998 hasRelatedWork W1671738336 @default.
- W3141305998 hasRelatedWork W2011472670 @default.
- W3141305998 hasRelatedWork W2064454806 @default.
- W3141305998 hasRelatedWork W2079015535 @default.
- W3141305998 hasRelatedWork W2097054466 @default.
- W3141305998 hasRelatedWork W2108631129 @default.
- W3141305998 hasRelatedWork W2153943021 @default.
- W3141305998 hasRelatedWork W2243630300 @default.
- W3141305998 hasRelatedWork W2364302005 @default.
- W3141305998 hasRelatedWork W2366906336 @default.
- W3141305998 hasRelatedWork W2377911686 @default.
- W3141305998 hasRelatedWork W2384236222 @default.
- W3141305998 hasRelatedWork W2385321669 @default.
- W3141305998 hasRelatedWork W2389124045 @default.
- W3141305998 hasRelatedWork W2526087824 @default.
- W3141305998 hasRelatedWork W2559992677 @default.
- W3141305998 hasRelatedWork W2942849095 @default.
- W3141305998 hasRelatedWork W2951603662 @default.
- W3141305998 hasRelatedWork W2462339643 @default.
- W3141305998 isParatext "false" @default.
- W3141305998 isRetracted "false" @default.
- W3141305998 magId "3141305998" @default.
- W3141305998 workType "article" @default.