• W3141998052 abstract "Abstract Corrosion of I‐shaped steel in the primary support of the subsea tunnel is inevitable due to high chloride ion content, which will weaken the bond performance between concrete and I‐shaped steel, resulting in a reduction in the service time of the subsea tunnel. Based on Xiang'an subsea tunnel, the bond–slip behavior between concrete and corroded I‐shaped steel was studied by the accelerated corrosion tests and push‐out tests, the experimental results indicated that: (1) The cracks of experimental specimens could be divided into two main forms: splitting failure (corrosion rate less than 5.79%); spalling failure (corrosion rate more than 5.79%). (2) A three‐stage bond‐slip law for concrete and corroded I‐shaped steel was proposed, and the formulae for calculating the bond strength were established. Furthermore, the degradation process of bond‐slip caused by corrosion was analyzed by energy principle and damage mechanics. Based on energy principle, it found that the elastic energy stored in the interface increased before the peak point of bond‐slip curve and decreased after the peak point, while the dissipated energy in the interface always increased with slip value. Finally, the interface relative damage variable was defined based on secant line anti‐sliding modulus and slip equivalent principle. The interface damage development process can be divided into three stages: initial damage, rapid damage development, and slow damage accumulation." @default.
• W3141998052 created "2021-04-13" @default.
• W3141998052 creator A5005349362 @default.
• W3141998052 creator A5036927186 @default.
• W3141998052 creator A5043473466 @default.
• W3141998052 creator A5053980584 @default.
• W3141998052 creator A5063601357 @default.
• W3141998052 date "2021-03-31" @default.
• W3141998052 modified "2023-10-16" @default.
• W3141998052 title "Experimental research and mechanical analysis on the <scp>bond‐slip</scp> behavior between concrete and corroded I‐shaped steel" @default.
• W3141998052 cites W1042018764 @default.
• W3141998052 cites W1976272328 @default.
• W3141998052 cites W1996543498 @default.
• W3141998052 cites W2007686945 @default.
• W3141998052 cites W2048600130 @default.
• W3141998052 cites W2059892830 @default.
• W3141998052 cites W2252632525 @default.
• W3141998052 cites W2442794422 @default.
• W3141998052 cites W2481538167 @default.
• W3141998052 cites W2506475292 @default.
• W3141998052 cites W2566357376 @default.
• W3141998052 cites W2593991188 @default.
• W3141998052 cites W2601973179 @default.
• W3141998052 cites W2660696438 @default.
• W3141998052 cites W2755015655 @default.
• W3141998052 cites W2788956088 @default.
• W3141998052 cites W2800236220 @default.
• W3141998052 cites W2901478223 @default.
• W3141998052 cites W2904672824 @default.
• W3141998052 cites W2922751275 @default.
• W3141998052 cites W2929667290 @default.
• W3141998052 cites W2936380460 @default.
• W3141998052 cites W2972007666 @default.
• W3141998052 cites W2972469488 @default.
• W3141998052 cites W2985609001 @default.
• W3141998052 cites W2990684407 @default.
• W3141998052 cites W2994751997 @default.
• W3141998052 cites W3042592110 @default.
• W3141998052 cites W3096373499 @default.
• W3141998052 doi "https://doi.org/10.1002/suco.202000564" @default.
• W3141998052 hasPublicationYear "2021" @default.
• W3141998052 type Work @default.
• W3141998052 sameAs 3141998052 @default.
• W3141998052 citedByCount "4" @default.
• W3141998052 countsByYear W31419980522021 @default.
• W3141998052 countsByYear W31419980522022 @default.
• W3141998052 countsByYear W31419980522023 @default.
• W3141998052 crossrefType "journal-article" @default.
• W3141998052 hasAuthorship W3141998052A5005349362 @default.
• W3141998052 hasAuthorship W3141998052A5036927186 @default.
• W3141998052 hasAuthorship W3141998052A5043473466 @default.
• W3141998052 hasAuthorship W3141998052A5053980584 @default.
• W3141998052 hasAuthorship W3141998052A5063601357 @default.
• W3141998052 hasConcept C10138342 @default.
• W3141998052 hasConcept C103208741 @default.
• W3141998052 hasConcept C127413603 @default.
• W3141998052 hasConcept C146978453 @default.
• W3141998052 hasConcept C159985019 @default.
• W3141998052 hasConcept C162324750 @default.
• W3141998052 hasConcept C187320778 @default.
• W3141998052 hasConcept C191897082 @default.
• W3141998052 hasConcept C192562407 @default.
• W3141998052 hasConcept C195268267 @default.
• W3141998052 hasConcept C20625102 @default.
• W3141998052 hasConcept C2777737062 @default.
• W3141998052 hasConcept C64355373 @default.
• W3141998052 hasConcept C66938386 @default.
• W3141998052 hasConcept C69738904 @default.
• W3141998052 hasConceptScore W3141998052C10138342 @default.
• W3141998052 hasConceptScore W3141998052C103208741 @default.
• W3141998052 hasConceptScore W3141998052C127413603 @default.
• W3141998052 hasConceptScore W3141998052C146978453 @default.
• W3141998052 hasConceptScore W3141998052C159985019 @default.
• W3141998052 hasConceptScore W3141998052C162324750 @default.
• W3141998052 hasConceptScore W3141998052C187320778 @default.
• W3141998052 hasConceptScore W3141998052C191897082 @default.
• W3141998052 hasConceptScore W3141998052C192562407 @default.
• W3141998052 hasConceptScore W3141998052C195268267 @default.
• W3141998052 hasConceptScore W3141998052C20625102 @default.
• W3141998052 hasConceptScore W3141998052C2777737062 @default.
• W3141998052 hasConceptScore W3141998052C64355373 @default.
• W3141998052 hasConceptScore W3141998052C66938386 @default.
• W3141998052 hasConceptScore W3141998052C69738904 @default.
• W3141998052 hasFunder F4320321001 @default.
• W3141998052 hasIssue "4" @default.
• W3141998052 hasLocation W31419980521 @default.
• W3141998052 hasOpenAccess W3141998052 @default.
• W3141998052 hasPrimaryLocation W31419980521 @default.
• W3141998052 hasRelatedWork W2014507159 @default.
• W3141998052 hasRelatedWork W2043886955 @default.
• W3141998052 hasRelatedWork W2085096680 @default.
• W3141998052 hasRelatedWork W2610509641 @default.
• W3141998052 hasRelatedWork W2690336747 @default.
• W3141998052 hasRelatedWork W3097783663 @default.
• W3141998052 hasRelatedWork W3141998052 @default.
• W3141998052 hasRelatedWork W4294691170 @default.
• W3141998052 hasRelatedWork W4366262926 @default.
• W3141998052 hasRelatedWork W4382584963 @default.

• next