- W3148422015 abstract "The properties and structures of 3D-Cf/SiC composites prepared by rapid precursor infiltration pyrolysis process were studied.PCS solution was infiltrated into 3D-carbon fiber perform in vacuum,then these performs were dried at room temperature and pyrolyzed with three kinds of heating rate,3 900 min,1 500 min and 1 000 min respectively.The distinction of 3D-Cf/SiC samples fabricated at three kinds of heating rate was not obvious.Bending strength of sample at 1 000 min heating rate was 762.5 MPa,and a little better than the others.Three samples at various heating rate had similar micro-graph of fracture surface and fracture toughness.The research results show that mechanics performances of Cf/SiC composites did not decrease when heating rate was properly increased." @default.
- W3148422015 created "2021-04-13" @default.
- W3148422015 creator A5030690377 @default.
- W3148422015 date "2012-01-01" @default.
- W3148422015 modified "2023-09-27" @default.
- W3148422015 title "Effects of heating rate on properties and structures of 3D-Cf/SiC composites by PIP process" @default.
- W3148422015 hasPublicationYear "2012" @default.
- W3148422015 type Work @default.
- W3148422015 sameAs 3148422015 @default.
- W3148422015 citedByCount "0" @default.
- W3148422015 crossrefType "journal-article" @default.
- W3148422015 hasAuthorship W3148422015A5030690377 @default.
- W3148422015 hasConcept C127413603 @default.
- W3148422015 hasConcept C159985019 @default.
- W3148422015 hasConcept C192562407 @default.
- W3148422015 hasConcept C36759035 @default.
- W3148422015 hasConcept C42360764 @default.
- W3148422015 hasConcept C519885992 @default.
- W3148422015 hasConcept C97549433 @default.
- W3148422015 hasConcept C99595764 @default.
- W3148422015 hasConceptScore W3148422015C127413603 @default.
- W3148422015 hasConceptScore W3148422015C159985019 @default.
- W3148422015 hasConceptScore W3148422015C192562407 @default.
- W3148422015 hasConceptScore W3148422015C36759035 @default.
- W3148422015 hasConceptScore W3148422015C42360764 @default.
- W3148422015 hasConceptScore W3148422015C519885992 @default.
- W3148422015 hasConceptScore W3148422015C97549433 @default.
- W3148422015 hasConceptScore W3148422015C99595764 @default.
- W3148422015 hasLocation W31484220151 @default.
- W3148422015 hasOpenAccess W3148422015 @default.
- W3148422015 hasPrimaryLocation W31484220151 @default.
- W3148422015 hasRelatedWork W1984955996 @default.
- W3148422015 hasRelatedWork W1985995894 @default.
- W3148422015 hasRelatedWork W2031607405 @default.
- W3148422015 hasRelatedWork W2070507051 @default.
- W3148422015 hasRelatedWork W2349724315 @default.
- W3148422015 hasRelatedWork W2353468738 @default.
- W3148422015 hasRelatedWork W2355589448 @default.
- W3148422015 hasRelatedWork W2359106153 @default.
- W3148422015 hasRelatedWork W2368366282 @default.
- W3148422015 hasRelatedWork W2372621423 @default.
- W3148422015 hasRelatedWork W2376773650 @default.
- W3148422015 hasRelatedWork W2377616824 @default.
- W3148422015 hasRelatedWork W2380105150 @default.
- W3148422015 hasRelatedWork W2381265404 @default.
- W3148422015 hasRelatedWork W2389994660 @default.
- W3148422015 hasRelatedWork W2393028789 @default.
- W3148422015 hasRelatedWork W2394304129 @default.
- W3148422015 hasRelatedWork W2979090693 @default.
- W3148422015 hasRelatedWork W2979412735 @default.
- W3148422015 hasRelatedWork W940996165 @default.
- W3148422015 isParatext "false" @default.
- W3148422015 isRetracted "false" @default.
- W3148422015 magId "3148422015" @default.
- W3148422015 workType "article" @default.