- W3150756379 abstract "The thermal expansion, thermal stability and bending strength of aluminumtitanate (AT)-mullite composites prepared from synthesized AT, Newzealand kaolin and aluminum hydroxide were investigated. The results obtained are summarized as follows; (1) The average linear thermal expansion coefficient from 100° to 1100°C increased slightly with increasing amount of AT up to 50wt%, and decreased with further increase in the amount of AT, approaching to be value of fired AT. The average linear thermal expansion coefficients from 1100° to 1400°C in heating and from 1400°C to the turning point in the cooling stage increased monotonously with increasing AT content. (2) The degree of thermal expansion hysteresis decreased with decreasing amount of AT. (3) The bending strength of the composites containing 10-30wt% AT was the highest, and decreased with further increase in the amount of AT. (4) The decomposition of AT in the composites was restrained almost completely." @default.
- W3150756379 created "2021-04-13" @default.
- W3150756379 creator A5009904425 @default.
- W3150756379 creator A5036096581 @default.
- W3150756379 creator A5064460740 @default.
- W3150756379 creator A5066284189 @default.
- W3150756379 creator A5089584902 @default.
- W3150756379 date "1987-01-01" @default.
- W3150756379 modified "2023-10-17" @default.
- W3150756379 title "Thermal and mechanical properties of aluminumtitanate-mullite composites (part 1)" @default.
- W3150756379 doi "https://doi.org/10.1016/0267-3762(87)90010-5" @default.
- W3150756379 hasPublicationYear "1987" @default.
- W3150756379 type Work @default.
- W3150756379 sameAs 3150756379 @default.
- W3150756379 citedByCount "0" @default.
- W3150756379 crossrefType "journal-article" @default.
- W3150756379 hasAuthorship W3150756379A5009904425 @default.
- W3150756379 hasAuthorship W3150756379A5036096581 @default.
- W3150756379 hasAuthorship W3150756379A5064460740 @default.
- W3150756379 hasAuthorship W3150756379A5066284189 @default.
- W3150756379 hasAuthorship W3150756379A5089584902 @default.
- W3150756379 hasConcept C121332964 @default.
- W3150756379 hasConcept C134132462 @default.
- W3150756379 hasConcept C153294291 @default.
- W3150756379 hasConcept C159985019 @default.
- W3150756379 hasConcept C192562407 @default.
- W3150756379 hasConcept C204530211 @default.
- W3150756379 hasConcept C2781436864 @default.
- W3150756379 hasConceptScore W3150756379C121332964 @default.
- W3150756379 hasConceptScore W3150756379C134132462 @default.
- W3150756379 hasConceptScore W3150756379C153294291 @default.
- W3150756379 hasConceptScore W3150756379C159985019 @default.
- W3150756379 hasConceptScore W3150756379C192562407 @default.
- W3150756379 hasConceptScore W3150756379C204530211 @default.
- W3150756379 hasConceptScore W3150756379C2781436864 @default.
- W3150756379 hasIssue "3" @default.
- W3150756379 hasLocation W31507563791 @default.
- W3150756379 hasOpenAccess W3150756379 @default.
- W3150756379 hasPrimaryLocation W31507563791 @default.
- W3150756379 hasRelatedWork W1964125561 @default.
- W3150756379 hasRelatedWork W1992399540 @default.
- W3150756379 hasRelatedWork W2021807975 @default.
- W3150756379 hasRelatedWork W2059382639 @default.
- W3150756379 hasRelatedWork W2074697892 @default.
- W3150756379 hasRelatedWork W2315466714 @default.
- W3150756379 hasRelatedWork W2371400253 @default.
- W3150756379 hasRelatedWork W3150626555 @default.
- W3150756379 hasRelatedWork W4234216116 @default.
- W3150756379 hasRelatedWork W4244960656 @default.
- W3150756379 hasVolume "3" @default.
- W3150756379 isParatext "false" @default.
- W3150756379 isRetracted "false" @default.
- W3150756379 magId "3150756379" @default.
- W3150756379 workType "article" @default.