- W3159657285 abstract "At present, cost-effective coatings that cause less pollution are in great demand; to decrease frictional losses, carbon-based hybrid composite coatings have been developed using a high-velocity oxy-fuel (HVOF) spray process. The microstructural, tribological, corrosion, and mechanical properties of these coatings have been evaluated using high-resolution X-ray diffraction (HRXRD), field emission scanning electron microscopy-Energy dispersive X-ray Spectroscopy (FESEM-EDS), Raman spectrum, Vickers micro-hardness tester, µ-360 cos(α) residual stress analyser, corrosion tester, and high temperature tribometer. The residual stress, corrosion and tribological behaviour at high temperatures were investigated using a pin-on-disc high-temperature tribometer. The tribological performance was evaluated using a high-temperature tribometer, and the experimental result shows that a coefficient of friction (COF) varies from 0.12 to 0.52, while wear results were in the range of 45 µm to 120 µm, as the test condition of temperature ranging from 50 °C to 350 °C, load from 60 N to 90 N and sliding velocity from 0.1 m/s to 0.4 m/s respectively. The experimental results of corrosion testing show that the mass loss decreases from 0.10 g to 0.04 g, when samples were dipped for 1 h; when the samples were dipped for 8 h, the mass loss of hybrid composite coating varied from 0.12 g to 0.045 g. The tribological test showed a 78.9 % increase in micro-hardness, a 78 % decrease in residual stress, and 60 % and 62.5 % decreases in mass loss due to corrosion at 1 h and 8 h, respectively, a 76.9 % decrease in COF and 62.5 % reduction in the wear at test condition of 350 ºC temperature, a sliding velocity of 0.4 m/s and 90 N load." @default.
- W3159657285 created "2021-05-10" @default.
- W3159657285 creator A5006191541 @default.
- W3159657285 creator A5023200172 @default.
- W3159657285 creator A5024527268 @default.
- W3159657285 date "2021-04-26" @default.
- W3159657285 modified "2023-10-14" @default.
- W3159657285 title "Residual, Corrosion & Tribological Behavior of HVOF Sprayed Sustainable Temperature-Dependent Carbon-Based Hybrid Composite Coating" @default.
- W3159657285 cites W1972199854 @default.
- W3159657285 cites W1992664938 @default.
- W3159657285 cites W2024266847 @default.
- W3159657285 cites W2025575577 @default.
- W3159657285 cites W2030977923 @default.
- W3159657285 cites W2053585689 @default.
- W3159657285 cites W2089415575 @default.
- W3159657285 cites W2089973178 @default.
- W3159657285 cites W2096039280 @default.
- W3159657285 cites W2116162163 @default.
- W3159657285 cites W2431939106 @default.
- W3159657285 cites W2469468663 @default.
- W3159657285 cites W2547037096 @default.
- W3159657285 cites W2606779835 @default.
- W3159657285 cites W2765467024 @default.
- W3159657285 cites W2791291144 @default.
- W3159657285 cites W2797194658 @default.
- W3159657285 cites W2802480363 @default.
- W3159657285 cites W2888943032 @default.
- W3159657285 cites W2893263380 @default.
- W3159657285 cites W2899842777 @default.
- W3159657285 cites W2942502542 @default.
- W3159657285 cites W2944156954 @default.
- W3159657285 cites W2944630823 @default.
- W3159657285 cites W2945032431 @default.
- W3159657285 cites W2969276942 @default.
- W3159657285 cites W2975323245 @default.
- W3159657285 cites W2982917952 @default.
- W3159657285 cites W2998997506 @default.
- W3159657285 cites W3006519600 @default.
- W3159657285 cites W3084032261 @default.
- W3159657285 cites W2113274198 @default.
- W3159657285 doi "https://doi.org/10.5545/sv-jme.2021.7101" @default.
- W3159657285 hasPublicationYear "2021" @default.
- W3159657285 type Work @default.
- W3159657285 sameAs 3159657285 @default.
- W3159657285 citedByCount "6" @default.
- W3159657285 countsByYear W31596572852021 @default.
- W3159657285 countsByYear W31596572852022 @default.
- W3159657285 crossrefType "journal-article" @default.
- W3159657285 hasAuthorship W3159657285A5006191541 @default.
- W3159657285 hasAuthorship W3159657285A5023200172 @default.
- W3159657285 hasAuthorship W3159657285A5024527268 @default.
- W3159657285 hasBestOaLocation W31596572851 @default.
- W3159657285 hasConcept C104779481 @default.
- W3159657285 hasConcept C149669645 @default.
- W3159657285 hasConcept C159985019 @default.
- W3159657285 hasConcept C162681261 @default.
- W3159657285 hasConcept C167310744 @default.
- W3159657285 hasConcept C191897082 @default.
- W3159657285 hasConcept C192562407 @default.
- W3159657285 hasConcept C20625102 @default.
- W3159657285 hasConcept C26771246 @default.
- W3159657285 hasConcept C2781448156 @default.
- W3159657285 hasConcept C37292000 @default.
- W3159657285 hasConceptScore W3159657285C104779481 @default.
- W3159657285 hasConceptScore W3159657285C149669645 @default.
- W3159657285 hasConceptScore W3159657285C159985019 @default.
- W3159657285 hasConceptScore W3159657285C162681261 @default.
- W3159657285 hasConceptScore W3159657285C167310744 @default.
- W3159657285 hasConceptScore W3159657285C191897082 @default.
- W3159657285 hasConceptScore W3159657285C192562407 @default.
- W3159657285 hasConceptScore W3159657285C20625102 @default.
- W3159657285 hasConceptScore W3159657285C26771246 @default.
- W3159657285 hasConceptScore W3159657285C2781448156 @default.
- W3159657285 hasConceptScore W3159657285C37292000 @default.
- W3159657285 hasLocation W31596572851 @default.
- W3159657285 hasLocation W31596572852 @default.
- W3159657285 hasLocation W31596572853 @default.
- W3159657285 hasOpenAccess W3159657285 @default.
- W3159657285 hasPrimaryLocation W31596572851 @default.
- W3159657285 hasRelatedWork W2057847 @default.
- W3159657285 hasRelatedWork W25427763 @default.
- W3159657285 hasRelatedWork W32048349 @default.
- W3159657285 hasRelatedWork W40563464 @default.
- W3159657285 hasRelatedWork W41634768 @default.
- W3159657285 hasRelatedWork W48613959 @default.
- W3159657285 hasRelatedWork W49602322 @default.
- W3159657285 hasRelatedWork W5279915 @default.
- W3159657285 hasRelatedWork W6806981 @default.
- W3159657285 hasRelatedWork W6954722 @default.
- W3159657285 isParatext "false" @default.
- W3159657285 isRetracted "false" @default.
- W3159657285 magId "3159657285" @default.
- W3159657285 workType "article" @default.