- W3169750051 abstract "TiAl matrix composites reinforced with graphene oxide (GO) were prepared by powder metallurgy technology. The graphene oxide plates were added into TiAl powder by ultrasonic dispersion and milling, and then, shaped by Hot Isostatic Pressing (HIPing). Microstructures of the composites were characterized by using scanning electron microscopy (SEM) and transmission electron microscopy (TEM). X-ray photoelectron spectroscopy (XPS) as well as Raman spectrum were conducted on the composite powder. The thermal and mechanical properties were tested on the TiAl matrix composites. The results show that the compression strength and heat conductivity of the composites can be improved distinctly at both room temperature and high temperature. The heat conductivity coefficient can reach to above 23 W/m K, and the compressive strength can reach to 1700 MPa at room temperature. GO was homogeneously dispersed into TiAl matrix in the form of random film with the diameter less than 10 μm. The minimum thickness of the GO film is about 5 nm. However, The GO does not well represent thermodynamically stable reinforcement at high temperatures, GO existed not only in the form of graphene but also a certain amount of Ti3AlC, and its size is about 2 μm rather than nanoscale, which can decrease the ductile reinforcement of GO in the TiAl matrix." @default.
- W3169750051 created "2021-06-22" @default.
- W3169750051 creator A5008695150 @default.
- W3169750051 creator A5037739851 @default.
- W3169750051 creator A5079566041 @default.
- W3169750051 creator A5085894372 @default.
- W3169750051 creator A5088316890 @default.
- W3169750051 date "2021-05-28" @default.
- W3169750051 modified "2023-09-26" @default.
- W3169750051 title "Microstructure Characterization and Properties of Graphene Oxide-Reinforced TiAl Matrix Composites" @default.
- W3169750051 cites W1989751498 @default.
- W3169750051 cites W1990571935 @default.
- W3169750051 cites W2157780288 @default.
- W3169750051 cites W2331559844 @default.
- W3169750051 cites W2552296683 @default.
- W3169750051 cites W2611593266 @default.
- W3169750051 cites W2902687790 @default.
- W3169750051 doi "https://doi.org/10.3390/met11060883" @default.
- W3169750051 hasPublicationYear "2021" @default.
- W3169750051 type Work @default.
- W3169750051 sameAs 3169750051 @default.
- W3169750051 citedByCount "13" @default.
- W3169750051 countsByYear W31697500512022 @default.
- W3169750051 countsByYear W31697500512023 @default.
- W3169750051 crossrefType "journal-article" @default.
- W3169750051 hasAuthorship W3169750051A5008695150 @default.
- W3169750051 hasAuthorship W3169750051A5037739851 @default.
- W3169750051 hasAuthorship W3169750051A5079566041 @default.
- W3169750051 hasAuthorship W3169750051A5085894372 @default.
- W3169750051 hasAuthorship W3169750051A5088316890 @default.
- W3169750051 hasBestOaLocation W31697500511 @default.
- W3169750051 hasConcept C104779481 @default.
- W3169750051 hasConcept C120665830 @default.
- W3169750051 hasConcept C121332964 @default.
- W3169750051 hasConcept C127413603 @default.
- W3169750051 hasConcept C159985019 @default.
- W3169750051 hasConcept C171250308 @default.
- W3169750051 hasConcept C175708663 @default.
- W3169750051 hasConcept C191897082 @default.
- W3169750051 hasConcept C192562407 @default.
- W3169750051 hasConcept C26771246 @default.
- W3169750051 hasConcept C2776578615 @default.
- W3169750051 hasConcept C2779851234 @default.
- W3169750051 hasConcept C2780036946 @default.
- W3169750051 hasConcept C30080830 @default.
- W3169750051 hasConcept C40003534 @default.
- W3169750051 hasConcept C42360764 @default.
- W3169750051 hasConcept C7794659 @default.
- W3169750051 hasConcept C87976508 @default.
- W3169750051 hasConceptScore W3169750051C104779481 @default.
- W3169750051 hasConceptScore W3169750051C120665830 @default.
- W3169750051 hasConceptScore W3169750051C121332964 @default.
- W3169750051 hasConceptScore W3169750051C127413603 @default.
- W3169750051 hasConceptScore W3169750051C159985019 @default.
- W3169750051 hasConceptScore W3169750051C171250308 @default.
- W3169750051 hasConceptScore W3169750051C175708663 @default.
- W3169750051 hasConceptScore W3169750051C191897082 @default.
- W3169750051 hasConceptScore W3169750051C192562407 @default.
- W3169750051 hasConceptScore W3169750051C26771246 @default.
- W3169750051 hasConceptScore W3169750051C2776578615 @default.
- W3169750051 hasConceptScore W3169750051C2779851234 @default.
- W3169750051 hasConceptScore W3169750051C2780036946 @default.
- W3169750051 hasConceptScore W3169750051C30080830 @default.
- W3169750051 hasConceptScore W3169750051C40003534 @default.
- W3169750051 hasConceptScore W3169750051C42360764 @default.
- W3169750051 hasConceptScore W3169750051C7794659 @default.
- W3169750051 hasConceptScore W3169750051C87976508 @default.
- W3169750051 hasIssue "6" @default.
- W3169750051 hasLocation W31697500511 @default.
- W3169750051 hasLocation W31697500512 @default.
- W3169750051 hasOpenAccess W3169750051 @default.
- W3169750051 hasPrimaryLocation W31697500511 @default.
- W3169750051 hasRelatedWork W2003154400 @default.
- W3169750051 hasRelatedWork W2005496670 @default.
- W3169750051 hasRelatedWork W2021473652 @default.
- W3169750051 hasRelatedWork W2068113961 @default.
- W3169750051 hasRelatedWork W2352533232 @default.
- W3169750051 hasRelatedWork W2379855728 @default.
- W3169750051 hasRelatedWork W2809525502 @default.
- W3169750051 hasRelatedWork W2951609152 @default.
- W3169750051 hasRelatedWork W3205547254 @default.
- W3169750051 hasRelatedWork W4226076254 @default.
- W3169750051 hasVolume "11" @default.
- W3169750051 isParatext "false" @default.
- W3169750051 isRetracted "false" @default.
- W3169750051 magId "3169750051" @default.
- W3169750051 workType "article" @default.