- W3175993805 abstract "• Inconel 625 filling powders with different amounts of pure Zr addition are used to braze SiC ceramic. Sound SiC joints are obtained at 1400 °C. • Zr is beneficial in suppressing the formation of graphite, which is a mechanically detrimental product of the reaction between Ni and SiC. When Zr addition reaches 40 wt%, the interface shows no sign of graphite. • Thermodynamic calculations prove that Zr’s activity surpasses that of Ni as the Zr content increases. Zr replaces Ni as the dominating element that reacts with SiC. A dense and consecutive ZrC layer is thus formed along the interface. • The room-temperature shear strength of the SiC joint with no graphite reaches 81.97 MPa, which is almost three times higher than that of the joint with graphite. Ni-based alloys are believed to be the most suitable brazing fillers for SiC ceramic application in a nuclear environment. However, graphite, which severely deteriorates the mechanical property of the joint, is inevitable when Ni reacts with SiC. In this paper, Different amounts of Zr powders are mixed with Inconel 625 powders to braze SiC at 1400 °C. When Zr addition reaches 40 wt%, the brazed seam confirms the absence of graphite. This research proves that Zr can avoid the graphite’s formation by suppressing Ni’s activity. The room-temperature shear strength of the joint with graphite’s absence is tested to be 81.97 MPa, which is almost three times higher than that of the joint with graphite. The interfacial reaction process and mechanism of the SiC joint are investigated and explained in this paper using thermodynamic calculations." @default.
- W3175993805 created "2021-07-05" @default.
- W3175993805 creator A5000228596 @default.
- W3175993805 creator A5003268372 @default.
- W3175993805 creator A5003718473 @default.
- W3175993805 creator A5021384155 @default.
- W3175993805 creator A5021431031 @default.
- W3175993805 creator A5023077332 @default.
- W3175993805 creator A5030942549 @default.
- W3175993805 creator A5031810848 @default.
- W3175993805 creator A5037308528 @default.
- W3175993805 creator A5043175040 @default.
- W3175993805 creator A5046404461 @default.
- W3175993805 creator A5081675173 @default.
- W3175993805 creator A5082451281 @default.
- W3175993805 creator A5082744526 @default.
- W3175993805 creator A5083732534 @default.
- W3175993805 date "2021-10-01" @default.
- W3175993805 modified "2023-09-29" @default.
- W3175993805 title "Effect of Zr addition on the interfacial reaction of the SiC joint brazed by Inconel 625 powder filler" @default.
- W3175993805 cites W1964148171 @default.
- W3175993805 cites W1972505988 @default.
- W3175993805 cites W1976127026 @default.
- W3175993805 cites W1989352328 @default.
- W3175993805 cites W1990047663 @default.
- W3175993805 cites W1990553775 @default.
- W3175993805 cites W2001321788 @default.
- W3175993805 cites W2001594745 @default.
- W3175993805 cites W2004417702 @default.
- W3175993805 cites W2005898093 @default.
- W3175993805 cites W2013874931 @default.
- W3175993805 cites W2015266446 @default.
- W3175993805 cites W2018204398 @default.
- W3175993805 cites W2027286886 @default.
- W3175993805 cites W2030694313 @default.
- W3175993805 cites W2036284301 @default.
- W3175993805 cites W2036299379 @default.
- W3175993805 cites W2050464153 @default.
- W3175993805 cites W2059784933 @default.
- W3175993805 cites W2068605235 @default.
- W3175993805 cites W2077709560 @default.
- W3175993805 cites W2082134476 @default.
- W3175993805 cites W2083245968 @default.
- W3175993805 cites W2088295058 @default.
- W3175993805 cites W2096643764 @default.
- W3175993805 cites W2097288984 @default.
- W3175993805 cites W2102915553 @default.
- W3175993805 cites W2233058752 @default.
- W3175993805 cites W2303671982 @default.
- W3175993805 cites W2355588736 @default.
- W3175993805 cites W2432637342 @default.
- W3175993805 cites W2468511959 @default.
- W3175993805 cites W2596279022 @default.
- W3175993805 cites W2611801927 @default.
- W3175993805 cites W2795785313 @default.
- W3175993805 cites W2805406418 @default.
- W3175993805 cites W2828126308 @default.
- W3175993805 cites W2900525266 @default.
- W3175993805 cites W2908091334 @default.
- W3175993805 cites W2911229266 @default.
- W3175993805 cites W2921864163 @default.
- W3175993805 cites W2945424403 @default.
- W3175993805 cites W2977606141 @default.
- W3175993805 cites W2983722967 @default.
- W3175993805 cites W2984696978 @default.
- W3175993805 cites W3004963709 @default.
- W3175993805 cites W3027187396 @default.
- W3175993805 cites W3044267890 @default.
- W3175993805 cites W3045383778 @default.
- W3175993805 cites W3049267054 @default.
- W3175993805 cites W3084472817 @default.
- W3175993805 cites W3092087435 @default.
- W3175993805 cites W3135650874 @default.
- W3175993805 cites W47193935 @default.
- W3175993805 doi "https://doi.org/10.1016/j.jeurceramsoc.2021.06.047" @default.
- W3175993805 hasPublicationYear "2021" @default.
- W3175993805 type Work @default.
- W3175993805 sameAs 3175993805 @default.
- W3175993805 citedByCount "8" @default.
- W3175993805 countsByYear W31759938052021 @default.
- W3175993805 countsByYear W31759938052022 @default.
- W3175993805 countsByYear W31759938052023 @default.
- W3175993805 crossrefType "journal-article" @default.
- W3175993805 hasAuthorship W3175993805A5000228596 @default.
- W3175993805 hasAuthorship W3175993805A5003268372 @default.
- W3175993805 hasAuthorship W3175993805A5003718473 @default.
- W3175993805 hasAuthorship W3175993805A5021384155 @default.
- W3175993805 hasAuthorship W3175993805A5021431031 @default.
- W3175993805 hasAuthorship W3175993805A5023077332 @default.
- W3175993805 hasAuthorship W3175993805A5030942549 @default.
- W3175993805 hasAuthorship W3175993805A5031810848 @default.
- W3175993805 hasAuthorship W3175993805A5037308528 @default.
- W3175993805 hasAuthorship W3175993805A5043175040 @default.
- W3175993805 hasAuthorship W3175993805A5046404461 @default.
- W3175993805 hasAuthorship W3175993805A5081675173 @default.
- W3175993805 hasAuthorship W3175993805A5082451281 @default.
- W3175993805 hasAuthorship W3175993805A5082744526 @default.
- W3175993805 hasAuthorship W3175993805A5083732534 @default.