• W3191020487 abstract "A γ-analogue of the superalloy CMSX-4 that does not contain the strengthening γ′-phase and only consists of the γ-solid solution of nickel has been designed, solidified as single-crystals of different orientations, and tested under creep conditions in the temperature range between 1150 and 1288 °C. The tests have revealed a very high creep anisotropy of this alloy, as was previously found for CMSX-4 at supersolvus temperature of 1288 °C. This creep anisotropy could be explained by the dominance of 011111 octahedral slip. Furthermore, the analysis of the creep data has yielded a high value of the creep activation energy, Qc≈442 kJ/mol, which correlates with the high activation energy of Re diffusion in Ni. This supports the hypothesis that dislocation motion in the γ-matrix of Re-containing superalloys is controlled by the diffusion of the Re atoms segregating at the dislocation core. The Norton stress exponent n is close to 5, which is a typical value for pure metals and their alloys. The absence of γ′-reprecipitation after high-temperature creep tests facilitates microstructural investigations. It has been shown by EBSD that creep deformation results in an increasing misorientation of the existing low angle boundaries. In addition, according to TEM, new low angle boundaries appear due to reactions of the a/2011 mobile dislocations and knitting of new networks." @default.
• W3191020487 created "2021-08-16" @default.
• W3191020487 creator A5010858764 @default.
• W3191020487 creator A5021421592 @default.
• W3191020487 creator A5024016545 @default.
• W3191020487 creator A5025266023 @default.
• W3191020487 creator A5032350304 @default.
• W3191020487 creator A5035751725 @default.
• W3191020487 creator A5044210140 @default.
• W3191020487 creator A5057230512 @default.
• W3191020487 creator A5062118838 @default.
• W3191020487 creator A5087637649 @default.
• W3191020487 date "2021-09-01" @default.
• W3191020487 modified "2023-10-04" @default.
• W3191020487 title "Creep of single-crystals of nickel-base γ-alloy at temperatures between 1150 °C and 1288 °C" @default.
• W3191020487 cites W1966952174 @default.
• W3191020487 cites W1969813186 @default.
• W3191020487 cites W1974548207 @default.
• W3191020487 cites W1980442259 @default.
• W3191020487 cites W1984917316 @default.
• W3191020487 cites W1990660671 @default.
• W3191020487 cites W1997746364 @default.
• W3191020487 cites W2001118646 @default.
• W3191020487 cites W2032405077 @default.
• W3191020487 cites W2036597809 @default.
• W3191020487 cites W2042212987 @default.
• W3191020487 cites W2044945960 @default.
• W3191020487 cites W2045287719 @default.
• W3191020487 cites W2048365912 @default.
• W3191020487 cites W2053946317 @default.
• W3191020487 cites W2062895179 @default.
• W3191020487 cites W2064725405 @default.
• W3191020487 cites W2067007474 @default.
• W3191020487 cites W2067626964 @default.
• W3191020487 cites W2070016542 @default.
• W3191020487 cites W2075287230 @default.
• W3191020487 cites W2078493042 @default.
• W3191020487 cites W2094634959 @default.
• W3191020487 cites W2104196136 @default.
• W3191020487 cites W2109940155 @default.
• W3191020487 cites W2282123213 @default.
• W3191020487 cites W2621037646 @default.
• W3191020487 cites W2744263725 @default.
• W3191020487 cites W2807725877 @default.
• W3191020487 cites W2999366445 @default.
• W3191020487 cites W3021490342 @default.
• W3191020487 cites W3127043051 @default.
• W3191020487 cites W312878716 @default.
• W3191020487 doi "https://doi.org/10.1016/j.msea.2021.141880" @default.
• W3191020487 hasPublicationYear "2021" @default.
• W3191020487 type Work @default.
• W3191020487 sameAs 3191020487 @default.
• W3191020487 citedByCount "5" @default.
• W3191020487 countsByYear W31910204872021 @default.
• W3191020487 countsByYear W31910204872022 @default.
• W3191020487 countsByYear W31910204872023 @default.
• W3191020487 crossrefType "journal-article" @default.
• W3191020487 hasAuthorship W3191020487A5010858764 @default.
• W3191020487 hasAuthorship W3191020487A5021421592 @default.
• W3191020487 hasAuthorship W3191020487A5024016545 @default.
• W3191020487 hasAuthorship W3191020487A5025266023 @default.
• W3191020487 hasAuthorship W3191020487A5032350304 @default.
• W3191020487 hasAuthorship W3191020487A5035751725 @default.
• W3191020487 hasAuthorship W3191020487A5044210140 @default.
• W3191020487 hasAuthorship W3191020487A5057230512 @default.
• W3191020487 hasAuthorship W3191020487A5062118838 @default.
• W3191020487 hasAuthorship W3191020487A5087637649 @default.
• W3191020487 hasBestOaLocation W31910204872 @default.
• W3191020487 hasConcept C121332964 @default.
• W3191020487 hasConcept C149912024 @default.
• W3191020487 hasConcept C159122135 @default.
• W3191020487 hasConcept C159985019 @default.
• W3191020487 hasConcept C178790620 @default.
• W3191020487 hasConcept C185592680 @default.
• W3191020487 hasConcept C187059263 @default.
• W3191020487 hasConcept C191897082 @default.
• W3191020487 hasConcept C192562407 @default.
• W3191020487 hasConcept C195268267 @default.
• W3191020487 hasConcept C207055975 @default.
• W3191020487 hasConcept C2778117898 @default.
• W3191020487 hasConcept C2780026712 @default.
• W3191020487 hasConcept C27805521 @default.
• W3191020487 hasConcept C47908070 @default.
• W3191020487 hasConcept C504270822 @default.
• W3191020487 hasConcept C8010536 @default.
• W3191020487 hasConcept C81764414 @default.
• W3191020487 hasConcept C87976508 @default.
• W3191020487 hasConcept C95121573 @default.
• W3191020487 hasConcept C97355855 @default.
• W3191020487 hasConceptScore W3191020487C121332964 @default.
• W3191020487 hasConceptScore W3191020487C149912024 @default.
• W3191020487 hasConceptScore W3191020487C159122135 @default.
• W3191020487 hasConceptScore W3191020487C159985019 @default.
• W3191020487 hasConceptScore W3191020487C178790620 @default.
• W3191020487 hasConceptScore W3191020487C185592680 @default.
• W3191020487 hasConceptScore W3191020487C187059263 @default.
• W3191020487 hasConceptScore W3191020487C191897082 @default.
• W3191020487 hasConceptScore W3191020487C192562407 @default.

• next