- W3198710603 endingPage "10" @default.
- W3198710603 startingPage "1" @default.
- W3198710603 abstract "PLA-PBAT was melt blended using Twin screw compounding extruder in three ratios (60:40, 50:50, 40:60%) with EGMA as compatibilizer (2.5 wt%). Tubular blown films were made using a tubular blown film extruder. In one formulation (50:50%) micro ZnO 1% was also included. The PLA-PBAT blends were tested for their mechanical, thermal, optical and physical properties. Due to ductility/flexibility of PBAT, tensile strength in machine direction (M/D) decreases with increasing PBAT concentration. However, in the transverse direction (T/D) the tensile strength increases with increase in PBAT concentration. Tear strength results show maximum strength in proportion of 50:50 in both machine and transverse direction. The PLA-PBAT 50:50 % blend filled with ZnO 1% has higher tear strength in both machine and transverse direction. Improvement in the dart impact strength was observed. Luminious transmittance was increased, MFI increased with increase in PBAT composition. Water vapour transmission rate was not decreased by increasing PBAT content since PBAT has slightly higher gas permeability than that of PLA. A complete biodegradation (100%) of PLA/PBAT blend was achieved in all PLA-PBAT blends and with micro ZnO, because of high biodegradability nature of PLA and PBAT polyesters. The test was done up to 210 days in soil burial method." @default.
- W3198710603 created "2021-09-13" @default.
- W3198710603 creator A5021210808 @default.
- W3198710603 creator A5022697931 @default.
- W3198710603 creator A5033450940 @default.
- W3198710603 creator A5036723630 @default.
- W3198710603 creator A5037687575 @default.
- W3198710603 creator A5050556990 @default.
- W3198710603 creator A5087046006 @default.
- W3198710603 date "2021-06-23" @default.
- W3198710603 modified "2023-09-27" @default.
- W3198710603 title "Studies on mechanical, optical and barrier properties of biodegradable PLA-PBAT blend film with EGMA compatibilizer and micro ZnO" @default.
- W3198710603 hasPublicationYear "2021" @default.
- W3198710603 type Work @default.
- W3198710603 sameAs 3198710603 @default.
- W3198710603 citedByCount "0" @default.
- W3198710603 crossrefType "journal-article" @default.
- W3198710603 hasAuthorship W3198710603A5021210808 @default.
- W3198710603 hasAuthorship W3198710603A5022697931 @default.
- W3198710603 hasAuthorship W3198710603A5033450940 @default.
- W3198710603 hasAuthorship W3198710603A5036723630 @default.
- W3198710603 hasAuthorship W3198710603A5037687575 @default.
- W3198710603 hasAuthorship W3198710603A5050556990 @default.
- W3198710603 hasAuthorship W3198710603A5087046006 @default.
- W3198710603 hasConcept C102267420 @default.
- W3198710603 hasConcept C112950240 @default.
- W3198710603 hasConcept C149912024 @default.
- W3198710603 hasConcept C150493377 @default.
- W3198710603 hasConcept C159985019 @default.
- W3198710603 hasConcept C163936134 @default.
- W3198710603 hasConcept C192562407 @default.
- W3198710603 hasConcept C207673951 @default.
- W3198710603 hasConcept C2776512210 @default.
- W3198710603 hasConcept C49040817 @default.
- W3198710603 hasConcept C97103648 @default.
- W3198710603 hasConceptScore W3198710603C102267420 @default.
- W3198710603 hasConceptScore W3198710603C112950240 @default.
- W3198710603 hasConceptScore W3198710603C149912024 @default.
- W3198710603 hasConceptScore W3198710603C150493377 @default.
- W3198710603 hasConceptScore W3198710603C159985019 @default.
- W3198710603 hasConceptScore W3198710603C163936134 @default.
- W3198710603 hasConceptScore W3198710603C192562407 @default.
- W3198710603 hasConceptScore W3198710603C207673951 @default.
- W3198710603 hasConceptScore W3198710603C2776512210 @default.
- W3198710603 hasConceptScore W3198710603C49040817 @default.
- W3198710603 hasConceptScore W3198710603C97103648 @default.
- W3198710603 hasIssue "2" @default.
- W3198710603 hasLocation W31987106031 @default.
- W3198710603 hasOpenAccess W3198710603 @default.
- W3198710603 hasPrimaryLocation W31987106031 @default.
- W3198710603 hasRelatedWork W1506042191 @default.
- W3198710603 hasRelatedWork W2023002187 @default.
- W3198710603 hasRelatedWork W2028931352 @default.
- W3198710603 hasRelatedWork W2155477859 @default.
- W3198710603 hasRelatedWork W2218753886 @default.
- W3198710603 hasRelatedWork W2225509088 @default.
- W3198710603 hasRelatedWork W2307151318 @default.
- W3198710603 hasRelatedWork W2374023185 @default.
- W3198710603 hasRelatedWork W2592693423 @default.
- W3198710603 hasRelatedWork W2609772865 @default.
- W3198710603 hasRelatedWork W2952984436 @default.
- W3198710603 hasRelatedWork W3000694926 @default.
- W3198710603 hasRelatedWork W3007020756 @default.
- W3198710603 hasRelatedWork W3012505294 @default.
- W3198710603 hasRelatedWork W3049538915 @default.
- W3198710603 hasRelatedWork W3106850736 @default.
- W3198710603 hasRelatedWork W3112325187 @default.
- W3198710603 hasRelatedWork W3136258400 @default.
- W3198710603 hasRelatedWork W3176555881 @default.
- W3198710603 hasRelatedWork W3204388395 @default.
- W3198710603 hasVolume "6" @default.
- W3198710603 isParatext "false" @default.
- W3198710603 isRetracted "false" @default.
- W3198710603 magId "3198710603" @default.
- W3198710603 workType "article" @default.