• W3199472013 abstract "Corrosion resistance of 3004 and 4044 aluminium alloys (3004Al and 4044Al) in neutral chloride (0.5%–4.5% concentration), sulphate (0.00625M-0.1 M concentration), and chloride-sulphate (0.00625 M H2SO4/0.5%–4.5% chloride concentration) solutions was studied with potentiodynamic polarization, open circuit potential, cyclic polarization, and optical microscopy. Results show 4044Al exhibited higher resistance to general corrosion while 3004Al was more resistant to localized corrosion. Corrosion of 4044Al decreases with increase in chloride concentration while 3004 Al increases. Corrosion rate values for 3004Al and 4044Al in sulphate solution were generally similar between 0.061–0.395 mm y−1 and 0.168–0.213 mm y−1, respectively. In chloride-sulphate solution, corrosion rate of 3004Al increased from 0.130 mm y−1 to 1.563 mm y−1 at peak chloride concentration whereas the corrosion rate of 4044Al is near constant. The passive film on 4044Al is found to weaken significantly with increase in chloride concentration. Passivation values varied from 0.39 V at 0.5% chloride concentration to 0.01 V at 4.5% concentration while the potential at which stable pitting occurred increased. The passivation range values for 3004Al are relatively stable with respect to chloride concentration. Results from cyclic polarization experiments show the deterioration rate of both alloys in NaCl solution is subject to chloride concentration. The results show the alloys corrode at all NaCl concentrations (0.5%–4.5%) with the lowest pitting corrosion risk in 0.5% and 1.5%NaCl solutions. The highest pitting corrosion risk of the alloys occurred in 3.5% NaCl solution. Significant localized morphological deterioration is visible throughout the entirety of 4044Al relative to the adjacent Al alloy matrix compared to total surface deterioration on 3004Al." @default.
• W3199472013 created "2021-09-27" @default.
• W3199472013 creator A5001051741 @default.
• W3199472013 creator A5079510843 @default.
• W3199472013 date "2021-09-01" @default.
• W3199472013 modified "2023-10-16" @default.
• W3199472013 title "Corrosion resistance and passivation behavior of 3004 AlMnMg and 4044AlSi aluminum alloys in acid-chloride electrolytes" @default.
• W3199472013 cites W1594528531 @default.
• W3199472013 cites W1967389466 @default.
• W3199472013 cites W1968381698 @default.
• W3199472013 cites W1985075987 @default.
• W3199472013 cites W1985361360 @default.
• W3199472013 cites W1988752021 @default.
• W3199472013 cites W1990316701 @default.
• W3199472013 cites W1990612746 @default.
• W3199472013 cites W1992135514 @default.
• W3199472013 cites W1992202775 @default.
• W3199472013 cites W1995352535 @default.
• W3199472013 cites W2001940016 @default.
• W3199472013 cites W2004378618 @default.
• W3199472013 cites W2008243856 @default.
• W3199472013 cites W2009788042 @default.
• W3199472013 cites W2009992595 @default.
• W3199472013 cites W2014947339 @default.
• W3199472013 cites W2018731801 @default.
• W3199472013 cites W2019993071 @default.
• W3199472013 cites W2026936061 @default.
• W3199472013 cites W2031960988 @default.
• W3199472013 cites W2032725519 @default.
• W3199472013 cites W2042226266 @default.
• W3199472013 cites W2047342168 @default.
• W3199472013 cites W2048115472 @default.
• W3199472013 cites W2049523656 @default.
• W3199472013 cites W2053469781 @default.
• W3199472013 cites W2059986171 @default.
• W3199472013 cites W2062681410 @default.
• W3199472013 cites W2078051427 @default.
• W3199472013 cites W2085646742 @default.
• W3199472013 cites W2093935410 @default.
• W3199472013 cites W2094942962 @default.
• W3199472013 cites W2108493994 @default.
• W3199472013 cites W2161630654 @default.
• W3199472013 cites W2268495580 @default.
• W3199472013 cites W2315355831 @default.
• W3199472013 cites W2499031847 @default.
• W3199472013 cites W2546732810 @default.
• W3199472013 cites W2555246931 @default.
• W3199472013 cites W2580753261 @default.
• W3199472013 cites W2618562181 @default.
• W3199472013 cites W2751970733 @default.
• W3199472013 cites W2792022241 @default.
• W3199472013 cites W2801253966 @default.
• W3199472013 cites W282317399 @default.
• W3199472013 cites W2883214426 @default.
• W3199472013 cites W2895997574 @default.
• W3199472013 cites W2902208091 @default.
• W3199472013 cites W2909323802 @default.
• W3199472013 cites W2914691214 @default.
• W3199472013 cites W2930893867 @default.
• W3199472013 cites W2952404234 @default.
• W3199472013 cites W2952689643 @default.
• W3199472013 cites W2972331377 @default.
• W3199472013 cites W2980307977 @default.
• W3199472013 cites W3004396254 @default.
• W3199472013 cites W3017262071 @default.
• W3199472013 cites W3024076648 @default.
• W3199472013 cites W3114427865 @default.
• W3199472013 cites W34307164 @default.
• W3199472013 cites W4212902233 @default.
• W3199472013 cites W618189179 @default.
• W3199472013 doi "https://doi.org/10.1088/2053-1591/ac286b" @default.
• W3199472013 hasPublicationYear "2021" @default.
• W3199472013 type Work @default.
• W3199472013 sameAs 3199472013 @default.
• W3199472013 citedByCount "3" @default.
• W3199472013 countsByYear W31994720132022 @default.
• W3199472013 crossrefType "journal-article" @default.
• W3199472013 hasAuthorship W3199472013A5001051741 @default.
• W3199472013 hasAuthorship W3199472013A5079510843 @default.
• W3199472013 hasBestOaLocation W31994720131 @default.
• W3199472013 hasConcept C147789679 @default.
• W3199472013 hasConcept C159985019 @default.
• W3199472013 hasConcept C17525397 @default.
• W3199472013 hasConcept C179104552 @default.
• W3199472013 hasConcept C185592680 @default.
• W3199472013 hasConcept C191897082 @default.
• W3199472013 hasConcept C192562407 @default.
• W3199472013 hasConcept C205049153 @default.
• W3199472013 hasConcept C20625102 @default.
• W3199472013 hasConcept C2778695967 @default.
• W3199472013 hasConcept C2779227376 @default.
• W3199472013 hasConcept C2779720300 @default.
• W3199472013 hasConcept C33574316 @default.
• W3199472013 hasConcept C513153333 @default.
• W3199472013 hasConcept C68801617 @default.
• W3199472013 hasConceptScore W3199472013C147789679 @default.
• W3199472013 hasConceptScore W3199472013C159985019 @default.
• W3199472013 hasConceptScore W3199472013C17525397 @default.

• next