- W3200119685 abstract "The process of synthesis of vanadium pentoxide nanobelts by hydrothermal method using intensive stirring of a suspension of V2O5 powder in aqueous NaCl solution was studied. The peculiarity of the hydrothermal method of synthesis of single-crystal V2O5 nanobelts is its ecological safety and high efficiency in terms of large-scale production by simple intensive mixing of the suspension of V2O5 powder in aqueous NaCl solution. No other specific conditions are required for the growth of nanostructures in this approach. Preparation of the suspension was as follows: 2 moles of NaCl was dissolved in 150 ml of distilled water, then 10 g of commercial V2O5 powder with particle sizes in the range from 10-100 μm was added. For the synthesis of V2O5 nanobelts, the test suspension was subjected to intensive mechanical stirring. During mixing, the temperature, pH of the solution, the viscosity of the test suspension were measured. The synthesized nanobelts were investigated by scanning electron microscopy (SEM) and X-ray diffractometry.The technological possibility of application the hydrothermal method in combination with intensive mechanical stirring of the solution for the synthesis of vanadium pentoxide nanobelts from powder with a particle size of 10-100 μm was confirmed. The characteristic feature of the process of structural transformation of particles into V2O5 nanobelts is the reduction in pH of the solution, which can be used as an indicative integral characteristic of the rate of synthesis of vanadium pentoxide nanobelts in industrial production.The important factors that can critically affect the process of hydrothermal synthesis of nanostructures during intensive mixing are the composition of the suspension, its temperature, mixing speed. The investigation of the influence of these factors will be carried out in the following works." @default.
- W3200119685 created "2021-09-27" @default.
- W3200119685 creator A5002209009 @default.
- W3200119685 creator A5013456980 @default.
- W3200119685 creator A5070832914 @default.
- W3200119685 date "2020-01-01" @default.
- W3200119685 modified "2023-09-25" @default.
- W3200119685 title "ГІДРОТЕРМІЧНИЙ МЕТОД СИНТЕЗУ НАНОПОЯСКІВ ОКСИДУ ВАНАДІЮ V2O5 ПРИ ІНТЕНСИВНОМУ ПЕРЕМІШУВАННІ" @default.
- W3200119685 cites W2013209195 @default.
- W3200119685 cites W2020046447 @default.
- W3200119685 cites W2122727913 @default.
- W3200119685 cites W2136119351 @default.
- W3200119685 cites W2289781493 @default.
- W3200119685 hasPublicationYear "2020" @default.
- W3200119685 type Work @default.
- W3200119685 sameAs 3200119685 @default.
- W3200119685 citedByCount "0" @default.
- W3200119685 crossrefType "journal-article" @default.
- W3200119685 hasAuthorship W3200119685A5002209009 @default.
- W3200119685 hasAuthorship W3200119685A5013456980 @default.
- W3200119685 hasAuthorship W3200119685A5070832914 @default.
- W3200119685 hasConcept C105341887 @default.
- W3200119685 hasConcept C107054158 @default.
- W3200119685 hasConcept C111368507 @default.
- W3200119685 hasConcept C121332964 @default.
- W3200119685 hasConcept C127313418 @default.
- W3200119685 hasConcept C127413603 @default.
- W3200119685 hasConcept C153294291 @default.
- W3200119685 hasConcept C156622251 @default.
- W3200119685 hasConcept C159985019 @default.
- W3200119685 hasConcept C178790620 @default.
- W3200119685 hasConcept C184651966 @default.
- W3200119685 hasConcept C185592680 @default.
- W3200119685 hasConcept C187530423 @default.
- W3200119685 hasConcept C191897082 @default.
- W3200119685 hasConcept C192562407 @default.
- W3200119685 hasConcept C202444582 @default.
- W3200119685 hasConcept C26771246 @default.
- W3200119685 hasConcept C2776871784 @default.
- W3200119685 hasConcept C2778517922 @default.
- W3200119685 hasConcept C2779429693 @default.
- W3200119685 hasConcept C2780162846 @default.
- W3200119685 hasConcept C33923547 @default.
- W3200119685 hasConcept C42360764 @default.
- W3200119685 hasConcept C43617362 @default.
- W3200119685 hasConcept C504678139 @default.
- W3200119685 hasConcept C5961521 @default.
- W3200119685 hasConceptScore W3200119685C105341887 @default.
- W3200119685 hasConceptScore W3200119685C107054158 @default.
- W3200119685 hasConceptScore W3200119685C111368507 @default.
- W3200119685 hasConceptScore W3200119685C121332964 @default.
- W3200119685 hasConceptScore W3200119685C127313418 @default.
- W3200119685 hasConceptScore W3200119685C127413603 @default.
- W3200119685 hasConceptScore W3200119685C153294291 @default.
- W3200119685 hasConceptScore W3200119685C156622251 @default.
- W3200119685 hasConceptScore W3200119685C159985019 @default.
- W3200119685 hasConceptScore W3200119685C178790620 @default.
- W3200119685 hasConceptScore W3200119685C184651966 @default.
- W3200119685 hasConceptScore W3200119685C185592680 @default.
- W3200119685 hasConceptScore W3200119685C187530423 @default.
- W3200119685 hasConceptScore W3200119685C191897082 @default.
- W3200119685 hasConceptScore W3200119685C192562407 @default.
- W3200119685 hasConceptScore W3200119685C202444582 @default.
- W3200119685 hasConceptScore W3200119685C26771246 @default.
- W3200119685 hasConceptScore W3200119685C2776871784 @default.
- W3200119685 hasConceptScore W3200119685C2778517922 @default.
- W3200119685 hasConceptScore W3200119685C2779429693 @default.
- W3200119685 hasConceptScore W3200119685C2780162846 @default.
- W3200119685 hasConceptScore W3200119685C33923547 @default.
- W3200119685 hasConceptScore W3200119685C42360764 @default.
- W3200119685 hasConceptScore W3200119685C43617362 @default.
- W3200119685 hasConceptScore W3200119685C504678139 @default.
- W3200119685 hasConceptScore W3200119685C5961521 @default.
- W3200119685 hasIssue "1" @default.
- W3200119685 hasLocation W32001196851 @default.
- W3200119685 hasOpenAccess W3200119685 @default.
- W3200119685 hasPrimaryLocation W32001196851 @default.
- W3200119685 hasVolume "1" @default.
- W3200119685 isParatext "false" @default.
- W3200119685 isRetracted "false" @default.
- W3200119685 magId "3200119685" @default.
- W3200119685 workType "article" @default.