• W3204237180 abstract "Micro-arc oxidation (MAO) ceramic coatings were prepared on porous AlSi10Mg selective laser-melted components to improve their corrosion property. The microstructure and composition of the coatings at different processing times were characterized via scanning electron microscopy, energy-dispersive spectroscopy , X-ray diffraction analysis, and X-ray photoelectron spectroscopy. Results showed that the diameter of micro-pores increased with an extension of treatment time, the porosity of coatings decreased from 6.24% to 0.85%. Thickness increased from 4.45 ± 0.01 μm to 15.20 ± 0.01 μm and surface roughness increased from 0.76 ± 0.01 μm to 5.41 ± 0.01 μm with increasing processing time. Meanwhile, the coatings were mostly composed of γ-Al 2 O 3 and trace amounts of α-Al 2 O 3 , Al 2 SiO 5 , AlPO 4 and WO 3 , the content of α-Al 2 O 3 was increased from 0.51% to 4.12%. Corrosion current density decreased from 2.213 e −5 A·cm −2 to 1.088 e −7 A·cm −2 . The polarization resistances R b were increased from 4.8 × 10 3 Ω·cm 2 to 2.6 × 10 5 Ω·cm 2 . The long term EIS results show that R b was 7.7 × 10 3 Ω·cm 2 after 3 weeks immersion, which show that the MAO coatings could provide good protection on AlSi10Mg alloy. The gas holes and defects of the SLM components were treated via MAO to form uniform MAO coatings on the surface of a sample, expanding the application range of selective laser-melted components in corrosive environments. • The gas holes in the SLM components were formed uniform MAO coatings. • Thickness, surface roughness increased with increasing processing time. • The coatings were mostly composed of γ-Al 2 O 3 , α-Al 2 O 3 , Al 2 SiO 5 , AlPO 4 , WO 3 . • The corrosion property of SLM sample was improved." @default.
• W3204237180 created "2021-10-11" @default.
• W3204237180 creator A5015751603 @default.
• W3204237180 creator A5018717863 @default.
• W3204237180 creator A5045000039 @default.
• W3204237180 creator A5046753327 @default.
• W3204237180 creator A5046834930 @default.
• W3204237180 creator A5067661498 @default.
• W3204237180 creator A5069768637 @default.
• W3204237180 date "2021-11-01" @default.
• W3204237180 modified "2023-09-26" @default.
• W3204237180 title "Growth characteristics and properties of micro-arc oxidation coatings on AlSi10Mg selective laser-melted components" @default.
• W3204237180 cites W1661604898 @default.
• W3204237180 cites W1968718744 @default.
• W3204237180 cites W2000450983 @default.
• W3204237180 cites W2018415549 @default.
• W3204237180 cites W2024308864 @default.
• W3204237180 cites W2031979751 @default.
• W3204237180 cites W2034099570 @default.
• W3204237180 cites W2053961256 @default.
• W3204237180 cites W2060928006 @default.
• W3204237180 cites W2200897650 @default.
• W3204237180 cites W2320027743 @default.
• W3204237180 cites W2729892130 @default.
• W3204237180 cites W2797339843 @default.
• W3204237180 cites W2804918031 @default.
• W3204237180 cites W2811030172 @default.
• W3204237180 cites W2885127638 @default.
• W3204237180 cites W2906821204 @default.
• W3204237180 cites W2909667680 @default.
• W3204237180 cites W2911753236 @default.
• W3204237180 cites W2923007684 @default.
• W3204237180 cites W2931028544 @default.
• W3204237180 cites W2934380160 @default.
• W3204237180 cites W2945214412 @default.
• W3204237180 cites W2947995430 @default.
• W3204237180 cites W2957890929 @default.
• W3204237180 cites W2960317155 @default.
• W3204237180 cites W2963347537 @default.
• W3204237180 cites W2964770265 @default.
• W3204237180 cites W2981669641 @default.
• W3204237180 cites W2982408926 @default.
• W3204237180 cites W2995563359 @default.
• W3204237180 cites W3005491093 @default.
• W3204237180 cites W3008654894 @default.
• W3204237180 cites W3012452335 @default.
• W3204237180 cites W3027673835 @default.
• W3204237180 cites W3031240002 @default.
• W3204237180 cites W3038111795 @default.
• W3204237180 cites W3092446203 @default.
• W3204237180 cites W3154454282 @default.
• W3204237180 cites W3159759022 @default.
• W3204237180 cites W3165056712 @default.
• W3204237180 cites W3187729231 @default.
• W3204237180 cites W3191289995 @default.
• W3204237180 cites W3201505248 @default.
• W3204237180 doi "https://doi.org/10.1016/j.surfcoat.2021.127765" @default.
• W3204237180 hasPublicationYear "2021" @default.
• W3204237180 type Work @default.
• W3204237180 sameAs 3204237180 @default.
• W3204237180 citedByCount "3" @default.
• W3204237180 countsByYear W32042371802022 @default.
• W3204237180 countsByYear W32042371802023 @default.
• W3204237180 crossrefType "journal-article" @default.
• W3204237180 hasAuthorship W3204237180A5015751603 @default.
• W3204237180 hasAuthorship W3204237180A5018717863 @default.
• W3204237180 hasAuthorship W3204237180A5045000039 @default.
• W3204237180 hasAuthorship W3204237180A5046753327 @default.
• W3204237180 hasAuthorship W3204237180A5046834930 @default.
• W3204237180 hasAuthorship W3204237180A5067661498 @default.
• W3204237180 hasAuthorship W3204237180A5069768637 @default.
• W3204237180 hasConcept C159985019 @default.
• W3204237180 hasConcept C191897082 @default.
• W3204237180 hasConcept C192562407 @default.
• W3204237180 hasConcept C2776797782 @default.
• W3204237180 hasConcept C3017923567 @default.
• W3204237180 hasConcept C87976508 @default.
• W3204237180 hasConceptScore W3204237180C159985019 @default.
• W3204237180 hasConceptScore W3204237180C191897082 @default.
• W3204237180 hasConceptScore W3204237180C192562407 @default.
• W3204237180 hasConceptScore W3204237180C2776797782 @default.
• W3204237180 hasConceptScore W3204237180C3017923567 @default.
• W3204237180 hasConceptScore W3204237180C87976508 @default.
• W3204237180 hasLocation W32042371801 @default.
• W3204237180 hasOpenAccess W3204237180 @default.
• W3204237180 hasPrimaryLocation W32042371801 @default.
• W3204237180 hasRelatedWork W1994103032 @default.
• W3204237180 hasRelatedWork W2051270029 @default.
• W3204237180 hasRelatedWork W2082293200 @default.
• W3204237180 hasRelatedWork W2137307547 @default.
• W3204237180 hasRelatedWork W2380293314 @default.
• W3204237180 hasRelatedWork W2943188944 @default.
• W3204237180 hasRelatedWork W3008690834 @default.
• W3204237180 hasRelatedWork W4242480814 @default.
• W3204237180 hasRelatedWork W4285802202 @default.
• W3204237180 hasRelatedWork W4317433637 @default.
• W3204237180 hasVolume "426" @default.
• W3204237180 isParatext "false" @default.

• next