- W3205212445 abstract "The present work is conducted in two stages, first synthesizing ZnO and Al doped ZnO thin films on glass substrates by SILAR method and second, comparing their optical, structural and morphological information. 0.025 M Zinc ammoniac solutions were prepared using Zinc Chloride. In one sample solution Al doping was obtained by adding 1% Aluminum Chloride. At room temperature SILAR cycles of 50 dips were conducted separately for two samples and thus obtained samples were annealed at 450°C for two hours. Obtained ZnO film sample were marked as S1(Sample1) and AZO film as S2(Sample 2). Optical transmittance and absorbance of the prepared samples were revealed by investigating with UV- Visible spectrometer. The transmittance of S1 was comparatively greater to that of S2, were absorbance was vice versa, which gives direct information regarding the increase in crystallinity of S2. The peak and average values of the samples were recorded. From X-ray diffraction, enhancement of intensity peaks was observed in S2 which shows the crystalline property in S2 surface. The lattice parameters were determined from it and ZnO hexagonal structures were identified. The grain size of the samples were calculated and compared. The surface analyses of the samples were provided by Scanning electron Microscope (SEM). Sample S1 was found to be smooth and uniform with good surface morphology whereas S2 was found to be rough and non-uniform. The grain size found to be decreasing in sample S2 compared to S1. So from the study it is confirmed that the grain size will decrease with Al doping but its concentration must be limited to lower values and also SILAR is found to be an effective method in preparing ZnO and Al doped ZnO thin films." @default.
- W3205212445 created "2021-10-25" @default.
- W3205212445 creator A5022835389 @default.
- W3205212445 creator A5031705228 @default.
- W3205212445 creator A5065432652 @default.
- W3205212445 creator A5068052792 @default.
- W3205212445 creator A5077885872 @default.
- W3205212445 date "2020-01-01" @default.
- W3205212445 modified "2023-09-27" @default.
- W3205212445 title "Characterization of ZnO and Al doped ZnO thin films prepared by SILAR method" @default.
- W3205212445 cites W1979590995 @default.
- W3205212445 cites W1988764200 @default.
- W3205212445 cites W2005654566 @default.
- W3205212445 cites W2007468754 @default.
- W3205212445 cites W2033160834 @default.
- W3205212445 cites W2045530011 @default.
- W3205212445 cites W2062475899 @default.
- W3205212445 cites W2088060382 @default.
- W3205212445 cites W2095389248 @default.
- W3205212445 cites W2154563667 @default.
- W3205212445 cites W2317632640 @default.
- W3205212445 doi "https://doi.org/10.1063/5.0030054" @default.
- W3205212445 hasPublicationYear "2020" @default.
- W3205212445 type Work @default.
- W3205212445 sameAs 3205212445 @default.
- W3205212445 citedByCount "0" @default.
- W3205212445 crossrefType "proceedings-article" @default.
- W3205212445 hasAuthorship W3205212445A5022835389 @default.
- W3205212445 hasAuthorship W3205212445A5031705228 @default.
- W3205212445 hasAuthorship W3205212445A5065432652 @default.
- W3205212445 hasAuthorship W3205212445A5068052792 @default.
- W3205212445 hasAuthorship W3205212445A5077885872 @default.
- W3205212445 hasConcept C113196181 @default.
- W3205212445 hasConcept C120665830 @default.
- W3205212445 hasConcept C121332964 @default.
- W3205212445 hasConcept C150493377 @default.
- W3205212445 hasConcept C159985019 @default.
- W3205212445 hasConcept C171250308 @default.
- W3205212445 hasConcept C185592680 @default.
- W3205212445 hasConcept C19067145 @default.
- W3205212445 hasConcept C191897082 @default.
- W3205212445 hasConcept C192191005 @default.
- W3205212445 hasConcept C192562407 @default.
- W3205212445 hasConcept C26771246 @default.
- W3205212445 hasConcept C43617362 @default.
- W3205212445 hasConcept C46275449 @default.
- W3205212445 hasConcept C49040817 @default.
- W3205212445 hasConcept C535196362 @default.
- W3205212445 hasConcept C57863236 @default.
- W3205212445 hasConcept C98015330 @default.
- W3205212445 hasConceptScore W3205212445C113196181 @default.
- W3205212445 hasConceptScore W3205212445C120665830 @default.
- W3205212445 hasConceptScore W3205212445C121332964 @default.
- W3205212445 hasConceptScore W3205212445C150493377 @default.
- W3205212445 hasConceptScore W3205212445C159985019 @default.
- W3205212445 hasConceptScore W3205212445C171250308 @default.
- W3205212445 hasConceptScore W3205212445C185592680 @default.
- W3205212445 hasConceptScore W3205212445C19067145 @default.
- W3205212445 hasConceptScore W3205212445C191897082 @default.
- W3205212445 hasConceptScore W3205212445C192191005 @default.
- W3205212445 hasConceptScore W3205212445C192562407 @default.
- W3205212445 hasConceptScore W3205212445C26771246 @default.
- W3205212445 hasConceptScore W3205212445C43617362 @default.
- W3205212445 hasConceptScore W3205212445C46275449 @default.
- W3205212445 hasConceptScore W3205212445C49040817 @default.
- W3205212445 hasConceptScore W3205212445C535196362 @default.
- W3205212445 hasConceptScore W3205212445C57863236 @default.
- W3205212445 hasConceptScore W3205212445C98015330 @default.
- W3205212445 hasLocation W32052124451 @default.
- W3205212445 hasOpenAccess W3205212445 @default.
- W3205212445 hasPrimaryLocation W32052124451 @default.
- W3205212445 hasRelatedWork W2017551786 @default.
- W3205212445 hasRelatedWork W2052710927 @default.
- W3205212445 hasRelatedWork W2095553506 @default.
- W3205212445 hasRelatedWork W2383217154 @default.
- W3205212445 hasRelatedWork W2389523700 @default.
- W3205212445 hasRelatedWork W2476235457 @default.
- W3205212445 hasRelatedWork W2720647270 @default.
- W3205212445 hasRelatedWork W3095711615 @default.
- W3205212445 hasRelatedWork W4200056847 @default.
- W3205212445 hasRelatedWork W4312793889 @default.
- W3205212445 isParatext "false" @default.
- W3205212445 isRetracted "false" @default.
- W3205212445 magId "3205212445" @default.
- W3205212445 workType "article" @default.