• W3206678461 abstract "This study aimed to determine the effects of three different varnish materials (containing casein phosphopeptide-amorphous calcium phosphate, nano-hydroxyapatite, and fluoride) on enamel. Thirty-three extracted human third molars were used for specimen preparation. These were demineralized using phosphoric acid. Three experimental groups (n = 11) were treated with 3M™ Clinpro™ White Varnish, MI Varnish®, and Megasonex® toothpaste, respectively, every twenty-four hours for fourteen days. Analysis of the microhardness of the specimens' enamel surfaces was carried out via the Vickers method, and by scanning electron microscopy/energy dispersive X-ray spectroscopy (SEM/EDS). Analysis was performed at three stages: at baseline value, after demineralization, and after the period of remineralization. Data were subjected to Scheffe's post hoc test. The mean microhardness values (HV0.1) obtained for the group of samples treated with MI Varnish® were higher compared with the other two groups (p = 0.001 for both comparisons), while the first and third groups did not differ significantly from each other (p = 0.97). SEM analysis showed uneven patterns and porosities on all samples tested. EDS results showed an increase in the mineral content of the examined samples, with the highest mineral content observed in the MI Varnish® group. It can be concluded that MI Varnish® use has a better remineralization effect on enamel than the other two materials." @default.
• W3206678461 created "2021-10-25" @default.
• W3206678461 creator A5040247626 @default.
• W3206678461 creator A5044105460 @default.
• W3206678461 creator A5049777001 @default.
• W3206678461 creator A5053335019 @default.
• W3206678461 date "2021-10-13" @default.
• W3206678461 modified "2023-10-18" @default.
• W3206678461 title "The Effects of Three Remineralizing Agents on the Microhardness and Chemical Composition of Demineralized Enamel" @default.
• W3206678461 cites W1487763461 @default.
• W3206678461 cites W1597218655 @default.
• W3206678461 cites W1940195802 @default.
• W3206678461 cites W1964881720 @default.
• W3206678461 cites W1965580842 @default.
• W3206678461 cites W1969801112 @default.
• W3206678461 cites W1972842035 @default.
• W3206678461 cites W1975828730 @default.
• W3206678461 cites W1979830028 @default.
• W3206678461 cites W1982614104 @default.
• W3206678461 cites W1994704698 @default.
• W3206678461 cites W2001963118 @default.
• W3206678461 cites W2011973192 @default.
• W3206678461 cites W2068318216 @default.
• W3206678461 cites W2093730592 @default.
• W3206678461 cites W2098660565 @default.
• W3206678461 cites W2111293504 @default.
• W3206678461 cites W2128301110 @default.
• W3206678461 cites W2132481404 @default.
• W3206678461 cites W2133054532 @default.
• W3206678461 cites W2144173061 @default.
• W3206678461 cites W2162729216 @default.
• W3206678461 cites W2169324675 @default.
• W3206678461 cites W2598313162 @default.
• W3206678461 cites W2617866445 @default.
• W3206678461 cites W2619751992 @default.
• W3206678461 cites W2754384683 @default.
• W3206678461 cites W2897307448 @default.
• W3206678461 cites W2897797060 @default.
• W3206678461 cites W2972329229 @default.
• W3206678461 cites W2973054411 @default.
• W3206678461 cites W2975576639 @default.
• W3206678461 cites W2991424733 @default.
• W3206678461 cites W2991927756 @default.
• W3206678461 cites W2994480330 @default.
• W3206678461 cites W2995375655 @default.
• W3206678461 cites W3035905460 @default.
• W3206678461 cites W3038990927 @default.
• W3206678461 cites W3137545886 @default.
• W3206678461 cites W4293628210 @default.
• W3206678461 doi "https://doi.org/10.3390/ma14206051" @default.
• W3206678461 hasPubMedCentralId "https://www.ncbi.nlm.nih.gov/pmc/articles/8537823" @default.
• W3206678461 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/34683643" @default.
• W3206678461 hasPublicationYear "2021" @default.
• W3206678461 type Work @default.
• W3206678461 sameAs 3206678461 @default.
• W3206678461 citedByCount "8" @default.
• W3206678461 countsByYear W32066784612022 @default.
• W3206678461 countsByYear W32066784612023 @default.
• W3206678461 crossrefType "journal-article" @default.
• W3206678461 hasAuthorship W3206678461A5040247626 @default.
• W3206678461 hasAuthorship W3206678461A5044105460 @default.
• W3206678461 hasAuthorship W3206678461A5049777001 @default.
• W3206678461 hasAuthorship W3206678461A5053335019 @default.
• W3206678461 hasBestOaLocation W32066784611 @default.
• W3206678461 hasConcept C13965031 @default.
• W3206678461 hasConcept C148318117 @default.
• W3206678461 hasConcept C156887251 @default.
• W3206678461 hasConcept C159985019 @default.
• W3206678461 hasConcept C165720898 @default.
• W3206678461 hasConcept C179104552 @default.
• W3206678461 hasConcept C185592680 @default.
• W3206678461 hasConcept C191897082 @default.
• W3206678461 hasConcept C192562407 @default.
• W3206678461 hasConcept C199343813 @default.
• W3206678461 hasConcept C202271784 @default.
• W3206678461 hasConcept C26771246 @default.
• W3206678461 hasConcept C2776052348 @default.
• W3206678461 hasConcept C2776622989 @default.
• W3206678461 hasConcept C2777001299 @default.
• W3206678461 hasConcept C2780158840 @default.
• W3206678461 hasConcept C2780828025 @default.
• W3206678461 hasConcept C2781448156 @default.
• W3206678461 hasConcept C28667232 @default.
• W3206678461 hasConcept C519063684 @default.
• W3206678461 hasConcept C71924100 @default.
• W3206678461 hasConcept C87976508 @default.
• W3206678461 hasConceptScore W3206678461C13965031 @default.
• W3206678461 hasConceptScore W3206678461C148318117 @default.
• W3206678461 hasConceptScore W3206678461C156887251 @default.
• W3206678461 hasConceptScore W3206678461C159985019 @default.
• W3206678461 hasConceptScore W3206678461C165720898 @default.
• W3206678461 hasConceptScore W3206678461C179104552 @default.
• W3206678461 hasConceptScore W3206678461C185592680 @default.
• W3206678461 hasConceptScore W3206678461C191897082 @default.
• W3206678461 hasConceptScore W3206678461C192562407 @default.
• W3206678461 hasConceptScore W3206678461C199343813 @default.
• W3206678461 hasConceptScore W3206678461C202271784 @default.
• W3206678461 hasConceptScore W3206678461C26771246 @default.

• next