- W3211636701 abstract "Abstract Melt-grown alumina-based composites are receiving increasing attention due to their potential for aerospace applications; however, the rapid preparation of high-performance components remains a challenge. Herein, a novel route for 3D printing dense (< 99.4%) high-performance melt-grown alumina-mullite/glass composites using directed laser deposition (DLD) is proposed. Key issues on the composites, including phase composition, microstructure formation/evolution, densification, and mechanical properties, are systematically investigated. The toughening and strengthening mechanisms are analyzed using classical fracture mechanics, Griffith strength theory, and solid/glass interface infiltration theory. It is demonstrated that the composites are composed of corundum, mullite, and glass, or corundum and glass. With the increase of alumina content in the initial powder, corundum grains gradually evolve from near-equiaxed dendrite to columnar dendrite and cellular structures due to the weakening of constitutional undercooling and small nucleation undercooling. The microhardness and fracture toughness are the highest at 92.5 mol% alumina, with 18.39±0.38 GPa and 3.07±0.13 MPa·m 1/2 , respectively. The maximum strength is 310.1±36.5 MPa at 95 mol% alumina. Strength enhancement is attributed to the improved densification due to the trace silica doping and the relief of residual stresses. The method unravels the potential of preparing dense high-performance melt-grown alumina-based composites by the DLD technology." @default.
- W3211636701 created "2021-11-22" @default.
- W3211636701 creator A5028747870 @default.
- W3211636701 creator A5043008399 @default.
- W3211636701 creator A5054625300 @default.
- W3211636701 creator A5079888913 @default.
- W3211636701 creator A5089303903 @default.
- W3211636701 date "2021-11-12" @default.
- W3211636701 modified "2023-10-17" @default.
- W3211636701 title "Microstructure and mechanical properties of melt-grown alumina-mullite/glass composites fabricated by directed laser deposition" @default.
- W3211636701 cites W1133639075 @default.
- W3211636701 cites W1526849346 @default.
- W3211636701 cites W1540032842 @default.
- W3211636701 cites W1965513801 @default.
- W3211636701 cites W1970102204 @default.
- W3211636701 cites W1976178500 @default.
- W3211636701 cites W1976597500 @default.
- W3211636701 cites W1979834963 @default.
- W3211636701 cites W1981074402 @default.
- W3211636701 cites W1985955705 @default.
- W3211636701 cites W1986428572 @default.
- W3211636701 cites W1989292230 @default.
- W3211636701 cites W1991935965 @default.
- W3211636701 cites W1998111134 @default.
- W3211636701 cites W1998237538 @default.
- W3211636701 cites W2015142022 @default.
- W3211636701 cites W2021458386 @default.
- W3211636701 cites W2025326631 @default.
- W3211636701 cites W2026188314 @default.
- W3211636701 cites W2026198704 @default.
- W3211636701 cites W2030457024 @default.
- W3211636701 cites W2031363439 @default.
- W3211636701 cites W2038704895 @default.
- W3211636701 cites W2039672144 @default.
- W3211636701 cites W2043044642 @default.
- W3211636701 cites W2048166598 @default.
- W3211636701 cites W2050107758 @default.
- W3211636701 cites W2053976177 @default.
- W3211636701 cites W2054960563 @default.
- W3211636701 cites W2055955464 @default.
- W3211636701 cites W2059987727 @default.
- W3211636701 cites W2064458709 @default.
- W3211636701 cites W2067014378 @default.
- W3211636701 cites W2067618673 @default.
- W3211636701 cites W2067618681 @default.
- W3211636701 cites W2077867065 @default.
- W3211636701 cites W2089587327 @default.
- W3211636701 cites W2089762728 @default.
- W3211636701 cites W2107023154 @default.
- W3211636701 cites W2117371631 @default.
- W3211636701 cites W2118586342 @default.
- W3211636701 cites W2118812023 @default.
- W3211636701 cites W2119965251 @default.
- W3211636701 cites W2130496912 @default.
- W3211636701 cites W2131451096 @default.
- W3211636701 cites W2131471121 @default.
- W3211636701 cites W2134778396 @default.
- W3211636701 cites W2146649272 @default.
- W3211636701 cites W2147699377 @default.
- W3211636701 cites W2160746590 @default.
- W3211636701 cites W2171675640 @default.
- W3211636701 cites W2268907602 @default.
- W3211636701 cites W2532553392 @default.
- W3211636701 cites W2559263076 @default.
- W3211636701 cites W2766106893 @default.
- W3211636701 cites W2778826446 @default.
- W3211636701 cites W2800271586 @default.
- W3211636701 cites W2800930531 @default.
- W3211636701 cites W2868155450 @default.
- W3211636701 cites W2884074740 @default.
- W3211636701 cites W2901378615 @default.
- W3211636701 cites W2921864163 @default.
- W3211636701 cites W2924410638 @default.
- W3211636701 cites W2945968583 @default.
- W3211636701 cites W2963351988 @default.
- W3211636701 cites W2964344211 @default.
- W3211636701 cites W2981971355 @default.
- W3211636701 cites W2994044580 @default.
- W3211636701 cites W3009539038 @default.
- W3211636701 cites W3014713008 @default.
- W3211636701 cites W3017570993 @default.
- W3211636701 cites W3020763515 @default.
- W3211636701 cites W3025304030 @default.
- W3211636701 cites W3036872151 @default.
- W3211636701 cites W3090120030 @default.
- W3211636701 cites W3094598295 @default.
- W3211636701 cites W3095726773 @default.
- W3211636701 cites W3096621499 @default.
- W3211636701 cites W3110189425 @default.
- W3211636701 cites W3126509770 @default.
- W3211636701 cites W4214736987 @default.
- W3211636701 cites W619095108 @default.
- W3211636701 cites W2025667793 @default.
- W3211636701 doi "https://doi.org/10.1007/s40145-021-0518-6" @default.
- W3211636701 hasPublicationYear "2021" @default.
- W3211636701 type Work @default.
- W3211636701 sameAs 3211636701 @default.
- W3211636701 citedByCount "15" @default.