- W417835 abstract "This report describes a research program to evaluate boride diffusion coatings for protection on Types 403 and 422 martensitic stainless steel turbine components against solid particle erosion. Several commercial coating vendors supplied stainless steel specimens with simple iron boride, chromium enriched iron boride, and silicon-enriched iron boride coatings. These specimens were characterized as to microstructure, composition, and hardness. They were then exposed in a stream of abrasive particulates at 1000{degrees}F and 500 ft/sec for up to 100 hours with intermediate specimen weighing and examination at 20 hour intervals. After the tests the microstructures and thickness of the remaining coating and substrate of each specimen were determined and measured. The tests showed that the chromium- and silicon-enriched iron boride coatings had erosion rates up to 2 to 4 times lower than those of simple iron borides. Coating microstructures was found to be an important factor influencing erosion resistance; while through thickness microcracking had no apparent effect on coating performance, fine networks of surface cracking were observed to make a coating much more susceptible to loss." @default.
- W417835 created "2016-06-24" @default.
- W417835 creator A5009965458 @default.
- W417835 creator A5021098452 @default.
- W417835 creator A5027787325 @default.
- W417835 creator A5057804767 @default.
- W417835 date "1991-11-01" @default.
- W417835 modified "2023-09-26" @default.
- W417835 title "Evaluation of boride diffusion coatings to alleviate erosion of steam turbine components" @default.
- W417835 hasPublicationYear "1991" @default.
- W417835 type Work @default.
- W417835 sameAs 417835 @default.
- W417835 citedByCount "0" @default.
- W417835 crossrefType "journal-article" @default.
- W417835 hasAuthorship W417835A5009965458 @default.
- W417835 hasAuthorship W417835A5021098452 @default.
- W417835 hasAuthorship W417835A5027787325 @default.
- W417835 hasAuthorship W417835A5057804767 @default.
- W417835 hasConcept C159985019 @default.
- W417835 hasConcept C191897082 @default.
- W417835 hasConcept C192562407 @default.
- W417835 hasConcept C2776723582 @default.
- W417835 hasConcept C2779249216 @default.
- W417835 hasConcept C2781448156 @default.
- W417835 hasConcept C87976508 @default.
- W417835 hasConceptScore W417835C159985019 @default.
- W417835 hasConceptScore W417835C191897082 @default.
- W417835 hasConceptScore W417835C192562407 @default.
- W417835 hasConceptScore W417835C2776723582 @default.
- W417835 hasConceptScore W417835C2779249216 @default.
- W417835 hasConceptScore W417835C2781448156 @default.
- W417835 hasConceptScore W417835C87976508 @default.
- W417835 hasLocation W4178351 @default.
- W417835 hasOpenAccess W417835 @default.
- W417835 hasPrimaryLocation W4178351 @default.
- W417835 hasRelatedWork W180526684 @default.
- W417835 hasRelatedWork W1978208714 @default.
- W417835 hasRelatedWork W1988771603 @default.
- W417835 hasRelatedWork W1998322767 @default.
- W417835 hasRelatedWork W2018827279 @default.
- W417835 hasRelatedWork W2034058536 @default.
- W417835 hasRelatedWork W203440062 @default.
- W417835 hasRelatedWork W2040474932 @default.
- W417835 hasRelatedWork W2042358411 @default.
- W417835 hasRelatedWork W2056616791 @default.
- W417835 hasRelatedWork W2082050318 @default.
- W417835 hasRelatedWork W2120624242 @default.
- W417835 hasRelatedWork W2274648075 @default.
- W417835 hasRelatedWork W2359746503 @default.
- W417835 hasRelatedWork W2389815413 @default.
- W417835 hasRelatedWork W2411567920 @default.
- W417835 hasRelatedWork W2470714367 @default.
- W417835 hasRelatedWork W2514731725 @default.
- W417835 hasRelatedWork W3169220068 @default.
- W417835 hasRelatedWork W2481431828 @default.
- W417835 isParatext "false" @default.
- W417835 isRetracted "false" @default.
- W417835 magId "417835" @default.
- W417835 workType "article" @default.