- W4200178051 abstract "In the present study, the stress corrosion cracking (SCC) behavior of ECAP Al5083 alloy was investigated in air as well as in 3.5 % NaCl solution using the slow strain rate tensile test (SSRT). The characteristics of grain boundary precipitates (GBPs), specifically the microchemistry of the SCC behavior of Al5083 alloys, both in as-received condition and when deformed by the ECAP process, were examined. The correlations between the SCC resistance and GBP microchemistry were examined. A microstructural evaluation was performed using an optical microscope. SCC tests were carried out using a universal tensile testing machine and the fracture surfaces were studied using scanning electron microscopy (SEM). A strain rate of 1×10-6 s-1 was applied for the SSRT. As the passes increased, the SCC susceptibility of the fine-grained ECAP Al5083 alloy also increased. Moreover, higher ultimate tensile strength and greater elongation were observed. This was due to grain refinement, high-density separations, and the expanded extent of high-density dislocations instigated by severe plastic deformation. Due to the high strength and elongation, the failure analysis showed a ductile mode of fracture. Electron backscattering diffraction (EBSD) analysis was performed to determine more clearly the nature of cracking. EBSD analysis showed that the crack propagation occurred in both transgranular and intergranular modes." @default.
- W4200178051 created "2021-12-31" @default.
- W4200178051 creator A5021543976 @default.
- W4200178051 creator A5041441970 @default.
- W4200178051 creator A5045185353 @default.
- W4200178051 creator A5083451939 @default.
- W4200178051 creator A5083771738 @default.
- W4200178051 date "2021-12-15" @default.
- W4200178051 modified "2023-09-26" @default.
- W4200178051 title "Stress Corrosion Cracking Behavior of Fine-Grained Al5083 Alloys Processed by Equal-Channel Angular Pressing (ECAP)" @default.
- W4200178051 cites W1963681996 @default.
- W4200178051 cites W1967868726 @default.
- W4200178051 cites W1971286923 @default.
- W4200178051 cites W1976096320 @default.
- W4200178051 cites W1983419415 @default.
- W4200178051 cites W1983932441 @default.
- W4200178051 cites W1984091151 @default.
- W4200178051 cites W1984831034 @default.
- W4200178051 cites W1985964361 @default.
- W4200178051 cites W1989898659 @default.
- W4200178051 cites W1992577817 @default.
- W4200178051 cites W1995153769 @default.
- W4200178051 cites W2001121353 @default.
- W4200178051 cites W2002798633 @default.
- W4200178051 cites W2007725785 @default.
- W4200178051 cites W2009995799 @default.
- W4200178051 cites W2014875592 @default.
- W4200178051 cites W2016492809 @default.
- W4200178051 cites W2023357572 @default.
- W4200178051 cites W2024338469 @default.
- W4200178051 cites W2035591537 @default.
- W4200178051 cites W2040395615 @default.
- W4200178051 cites W2042242555 @default.
- W4200178051 cites W2043645402 @default.
- W4200178051 cites W2044820251 @default.
- W4200178051 cites W2045568131 @default.
- W4200178051 cites W2046344036 @default.
- W4200178051 cites W2048533583 @default.
- W4200178051 cites W2051249309 @default.
- W4200178051 cites W2053207521 @default.
- W4200178051 cites W2054050242 @default.
- W4200178051 cites W2056071045 @default.
- W4200178051 cites W2058193930 @default.
- W4200178051 cites W2062510729 @default.
- W4200178051 cites W2063115418 @default.
- W4200178051 cites W2065843918 @default.
- W4200178051 cites W2071341316 @default.
- W4200178051 cites W2072924648 @default.
- W4200178051 cites W2077953383 @default.
- W4200178051 cites W2083317639 @default.
- W4200178051 cites W2087039924 @default.
- W4200178051 cites W2088046024 @default.
- W4200178051 cites W2090390955 @default.
- W4200178051 cites W2092167288 @default.
- W4200178051 cites W2093140392 @default.
- W4200178051 cites W2093842827 @default.
- W4200178051 cites W2103018933 @default.
- W4200178051 cites W2118158291 @default.
- W4200178051 cites W2121423834 @default.
- W4200178051 cites W2161630654 @default.
- W4200178051 cites W2163732611 @default.
- W4200178051 cites W2230298865 @default.
- W4200178051 cites W2296989457 @default.
- W4200178051 cites W2470415268 @default.
- W4200178051 cites W2472196133 @default.
- W4200178051 cites W2591576920 @default.
- W4200178051 cites W2734491109 @default.
- W4200178051 cites W2766232273 @default.
- W4200178051 cites W2801253966 @default.
- W4200178051 cites W2905516314 @default.
- W4200178051 cites W2906609347 @default.
- W4200178051 cites W2921807141 @default.
- W4200178051 cites W2956919146 @default.
- W4200178051 cites W2961262143 @default.
- W4200178051 cites W2970784384 @default.
- W4200178051 cites W579762698 @default.
- W4200178051 doi "https://doi.org/10.3390/molecules26247608" @default.
- W4200178051 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/34946692" @default.
- W4200178051 hasPublicationYear "2021" @default.
- W4200178051 type Work @default.
- W4200178051 citedByCount "2" @default.
- W4200178051 countsByYear W42001780512023 @default.
- W4200178051 crossrefType "journal-article" @default.
- W4200178051 hasAuthorship W4200178051A5021543976 @default.
- W4200178051 hasAuthorship W4200178051A5041441970 @default.
- W4200178051 hasAuthorship W4200178051A5045185353 @default.
- W4200178051 hasAuthorship W4200178051A5083451939 @default.
- W4200178051 hasAuthorship W4200178051A5083771738 @default.
- W4200178051 hasBestOaLocation W42001780511 @default.
- W4200178051 hasConcept C112950240 @default.
- W4200178051 hasConcept C149342994 @default.
- W4200178051 hasConcept C159985019 @default.
- W4200178051 hasConcept C182508753 @default.
- W4200178051 hasConcept C184102282 @default.
- W4200178051 hasConcept C191897082 @default.
- W4200178051 hasConcept C192562407 @default.
- W4200178051 hasConcept C26771246 @default.
- W4200178051 hasConcept C2778760603 @default.