- W4200344680 abstract "One of the rivets connecting the frame and cover plate was broken unexpected in use. To analyze the fracture mode of this Al-Mg alloy pop rivet and prevent the similar events, scanning electron microscopy observation and chemical composition tests were carried out. Fatigue tests were performed to further find out the cause of failure of the Al-Mg alloy pop rivets. The failed rivets showed obvious fatigue fracture characteristics, whereas no corrosive medium could be tracked. The fatigue limit of Al-Mg alloy pop rivets was about 400 N. The stress concentration generated during riveting process and the maximum external forces beyond fatigue limit of aluminum rivets led to the initiation of plastic deformation zone. The low content of Mn and the possible existence of crevice between rivet core and rivet body may promote the initiation of plastic deformation zone. Under the action of continuous external load, the fatigue crack continued to expand, and finally caused the fracture of pop rivet. The effect of corrosive medium on cracking can be eliminated." @default.
- W4200344680 created "2021-12-31" @default.
- W4200344680 creator A5005056208 @default.
- W4200344680 creator A5008397133 @default.
- W4200344680 creator A5010394179 @default.
- W4200344680 creator A5020921140 @default.
- W4200344680 creator A5038061233 @default.
- W4200344680 creator A5047277220 @default.
- W4200344680 creator A5052830364 @default.
- W4200344680 creator A5056273715 @default.
- W4200344680 creator A5070159436 @default.
- W4200344680 creator A5081869027 @default.
- W4200344680 date "2022-03-01" @default.
- W4200344680 modified "2023-10-03" @default.
- W4200344680 title "Metallurgical analyses on Al-Mg alloy pop rivets used in the electric cabinet" @default.
- W4200344680 cites W1965879910 @default.
- W4200344680 cites W1980626998 @default.
- W4200344680 cites W1991698228 @default.
- W4200344680 cites W2017902242 @default.
- W4200344680 cites W2023540080 @default.
- W4200344680 cites W2031272504 @default.
- W4200344680 cites W2038211127 @default.
- W4200344680 cites W2084190973 @default.
- W4200344680 cites W2884878776 @default.
- W4200344680 cites W2897103829 @default.
- W4200344680 cites W2909061682 @default.
- W4200344680 cites W2927862187 @default.
- W4200344680 cites W2969800671 @default.
- W4200344680 cites W2970293338 @default.
- W4200344680 cites W2981271067 @default.
- W4200344680 cites W3005096977 @default.
- W4200344680 cites W3010325691 @default.
- W4200344680 cites W3015666999 @default.
- W4200344680 cites W3026938211 @default.
- W4200344680 cites W3041008126 @default.
- W4200344680 cites W3088551805 @default.
- W4200344680 cites W3088800024 @default.
- W4200344680 cites W3095263473 @default.
- W4200344680 cites W3112839006 @default.
- W4200344680 cites W3115365852 @default.
- W4200344680 doi "https://doi.org/10.1016/j.engfailanal.2021.106000" @default.
- W4200344680 hasPublicationYear "2022" @default.
- W4200344680 type Work @default.
- W4200344680 citedByCount "0" @default.
- W4200344680 crossrefType "journal-article" @default.
- W4200344680 hasAuthorship W4200344680A5005056208 @default.
- W4200344680 hasAuthorship W4200344680A5008397133 @default.
- W4200344680 hasAuthorship W4200344680A5010394179 @default.
- W4200344680 hasAuthorship W4200344680A5020921140 @default.
- W4200344680 hasAuthorship W4200344680A5038061233 @default.
- W4200344680 hasAuthorship W4200344680A5047277220 @default.
- W4200344680 hasAuthorship W4200344680A5052830364 @default.
- W4200344680 hasAuthorship W4200344680A5056273715 @default.
- W4200344680 hasAuthorship W4200344680A5070159436 @default.
- W4200344680 hasAuthorship W4200344680A5081869027 @default.
- W4200344680 hasConcept C131850400 @default.
- W4200344680 hasConcept C159985019 @default.
- W4200344680 hasConcept C191897082 @default.
- W4200344680 hasConcept C192562407 @default.
- W4200344680 hasConcept C2780026712 @default.
- W4200344680 hasConcept C43369102 @default.
- W4200344680 hasConcept C57769158 @default.
- W4200344680 hasConcept C58396970 @default.
- W4200344680 hasConceptScore W4200344680C131850400 @default.
- W4200344680 hasConceptScore W4200344680C159985019 @default.
- W4200344680 hasConceptScore W4200344680C191897082 @default.
- W4200344680 hasConceptScore W4200344680C192562407 @default.
- W4200344680 hasConceptScore W4200344680C2780026712 @default.
- W4200344680 hasConceptScore W4200344680C43369102 @default.
- W4200344680 hasConceptScore W4200344680C57769158 @default.
- W4200344680 hasConceptScore W4200344680C58396970 @default.
- W4200344680 hasLocation W42003446801 @default.
- W4200344680 hasOpenAccess W4200344680 @default.
- W4200344680 hasPrimaryLocation W42003446801 @default.
- W4200344680 hasRelatedWork W2045872900 @default.
- W4200344680 hasRelatedWork W2089251307 @default.
- W4200344680 hasRelatedWork W2137307547 @default.
- W4200344680 hasRelatedWork W2380293314 @default.
- W4200344680 hasRelatedWork W2943188944 @default.
- W4200344680 hasRelatedWork W2996358649 @default.
- W4200344680 hasRelatedWork W3082440218 @default.
- W4200344680 hasRelatedWork W3184073732 @default.
- W4200344680 hasRelatedWork W3190750232 @default.
- W4200344680 hasRelatedWork W4285802202 @default.
- W4200344680 hasVolume "133" @default.
- W4200344680 isParatext "false" @default.
- W4200344680 isRetracted "false" @default.
- W4200344680 workType "article" @default.