- W4206203464 abstract "The main aim of this study was to apply high-energy longer mechanical milling and spark plasma sintering (SPS) techniques to produce in-situ α-Ti/TiO 2 /TiC hybrid composites from commercially pure-Ti (CP–Ti, HCP structure) powders. The CP-Ti powders were subjected to different milling times (0, 20, 40, 60, 80, 100, and 120 h). The results showed that the powder samples milled for 120 h produced Ti, Ti 3 O 5 , TiO, TiO 2 phases, and dissolved C atoms from the process control agent (toluene) which were then converted to α-Ti, TiO 2 , and TiC phases (formed in-situ composites) through spark plasma sintering. This was expected due to more reactivity in the 120 h sample as longer milling introduces severe and robust structural refinements. Structural evaluations with increasing milling time were carried out using XRD, HRSEM, and HRTEM. The synthesized powders were then consolidated by SPS at pressures of 50 MPa and 1323 K for 6 min. The micro-hardness results have shown that the hardness was started to increase from 1.40 GPa to 5.56 GPa with increasing milling time due to more dislocation and pinning effect produced by grain refinement and formed TiO 2 /TiC intermetallic particles enhancing the strength of α-Ti matrix. The α-Ti/TiO 2 /TiC in-situ hybrid composite bulk sample yielded an ultimate compressive strength of 1.594 GPa." @default.
- W4206203464 created "2022-01-25" @default.
- W4206203464 creator A5004612216 @default.
- W4206203464 creator A5007178745 @default.
- W4206203464 creator A5015077863 @default.
- W4206203464 creator A5015589616 @default.
- W4206203464 creator A5037143859 @default.
- W4206203464 creator A5038384234 @default.
- W4206203464 date "2022-04-01" @default.
- W4206203464 modified "2023-09-29" @default.
- W4206203464 title "Structure and mechanical properties of in-situ synthesized α-Ti/TiO2/TiC hybrid composites through mechanical milling and spark plasma sintering" @default.
- W4206203464 cites W1966703141 @default.
- W4206203464 cites W1976381624 @default.
- W4206203464 cites W1979101213 @default.
- W4206203464 cites W1991242908 @default.
- W4206203464 cites W1995555140 @default.
- W4206203464 cites W1996289405 @default.
- W4206203464 cites W2000382684 @default.
- W4206203464 cites W2001315817 @default.
- W4206203464 cites W2004437627 @default.
- W4206203464 cites W2006496782 @default.
- W4206203464 cites W2009185243 @default.
- W4206203464 cites W2011897787 @default.
- W4206203464 cites W2034622538 @default.
- W4206203464 cites W2037018094 @default.
- W4206203464 cites W2038743815 @default.
- W4206203464 cites W2048972573 @default.
- W4206203464 cites W2061325240 @default.
- W4206203464 cites W2062656478 @default.
- W4206203464 cites W2078889254 @default.
- W4206203464 cites W2092447005 @default.
- W4206203464 cites W2112630646 @default.
- W4206203464 cites W2136108667 @default.
- W4206203464 cites W2169492727 @default.
- W4206203464 cites W2414741983 @default.
- W4206203464 cites W2612097623 @default.
- W4206203464 cites W2743724331 @default.
- W4206203464 cites W2790735483 @default.
- W4206203464 cites W2809492233 @default.
- W4206203464 cites W2889506916 @default.
- W4206203464 cites W2916046182 @default.
- W4206203464 cites W3000626214 @default.
- W4206203464 cites W3082289275 @default.
- W4206203464 cites W3108210607 @default.
- W4206203464 cites W3154762627 @default.
- W4206203464 cites W3157952219 @default.
- W4206203464 cites W3170123887 @default.
- W4206203464 doi "https://doi.org/10.1016/j.ceramint.2021.12.342" @default.
- W4206203464 hasPublicationYear "2022" @default.
- W4206203464 type Work @default.
- W4206203464 citedByCount "10" @default.
- W4206203464 countsByYear W42062034642022 @default.
- W4206203464 countsByYear W42062034642023 @default.
- W4206203464 crossrefType "journal-article" @default.
- W4206203464 hasAuthorship W4206203464A5004612216 @default.
- W4206203464 hasAuthorship W4206203464A5007178745 @default.
- W4206203464 hasAuthorship W4206203464A5015077863 @default.
- W4206203464 hasAuthorship W4206203464A5015589616 @default.
- W4206203464 hasAuthorship W4206203464A5037143859 @default.
- W4206203464 hasAuthorship W4206203464A5038384234 @default.
- W4206203464 hasConcept C104779481 @default.
- W4206203464 hasConcept C159985019 @default.
- W4206203464 hasConcept C191897082 @default.
- W4206203464 hasConcept C192562407 @default.
- W4206203464 hasConcept C27501479 @default.
- W4206203464 hasConcept C2776014600 @default.
- W4206203464 hasConcept C2777581544 @default.
- W4206203464 hasConcept C2780026712 @default.
- W4206203464 hasConceptScore W4206203464C104779481 @default.
- W4206203464 hasConceptScore W4206203464C159985019 @default.
- W4206203464 hasConceptScore W4206203464C191897082 @default.
- W4206203464 hasConceptScore W4206203464C192562407 @default.
- W4206203464 hasConceptScore W4206203464C27501479 @default.
- W4206203464 hasConceptScore W4206203464C2776014600 @default.
- W4206203464 hasConceptScore W4206203464C2777581544 @default.
- W4206203464 hasConceptScore W4206203464C2780026712 @default.
- W4206203464 hasFunder F4320334771 @default.
- W4206203464 hasIssue "8" @default.
- W4206203464 hasLocation W42062034641 @default.
- W4206203464 hasOpenAccess W4206203464 @default.
- W4206203464 hasPrimaryLocation W42062034641 @default.
- W4206203464 hasRelatedWork W1997220521 @default.
- W4206203464 hasRelatedWork W2013673174 @default.
- W4206203464 hasRelatedWork W2015253347 @default.
- W4206203464 hasRelatedWork W2062064674 @default.
- W4206203464 hasRelatedWork W2066820123 @default.
- W4206203464 hasRelatedWork W2097829472 @default.
- W4206203464 hasRelatedWork W2245602275 @default.
- W4206203464 hasRelatedWork W2371912931 @default.
- W4206203464 hasRelatedWork W2547539111 @default.
- W4206203464 hasRelatedWork W4234037745 @default.
- W4206203464 hasVolume "48" @default.
- W4206203464 isParatext "false" @default.
- W4206203464 isRetracted "false" @default.
- W4206203464 workType "article" @default.