- W4206724263 abstract "This study investigated the effect of heat generation during friction stir welding (FSW) on dissimilar aluminium alloy plates AA6061 and AA5052 using process variables such as tool rotational speed, feed rate and temperature distribution. Temperature distributions on the workpiece were recorded at advancing side and receding side during welding by using thermocouples and revealed that temperatures on the advancing side are greater than those on the receding side. The FSW process was simulated at the tool speed of 1000, 1200 and 1400 rpm, feed rate of 20, 40, 60 mm/min. A Taguchi OA has been used for designed the experiments. The findings of the micro hardness test at the welded zone analysed using Vickers’s tester. Microstructure analysis of AA6061 identical welds reveals that grains are slightly reduced at HAZ, while analysis of AA5052 and AA6061 dissimilar welds reveals that grain are significantly enlarged at weldment than base metal. It also found that, the tool speed increases while maintaining a steady feed rate, increased the amount of heat generated in weld zones. On the other hand, increasing feed rate while maintaining constant tool rotational speeds results in a decrease in the amount of heat created in weld zones. Analysis of variance (ANOVA) revealed, the optimal condition of temperature distribution and heat generation is T3F1 (i.e., tool speed of 1400 rpm and feed rate of 20 mm/min). A model of the workpiece and tool was developed using Deform-3D Software for friction stir welding, and thermal analysis was performed to analyse the temperature distribution." @default.
- W4206724263 created "2022-01-25" @default.
- W4206724263 creator A5006614151 @default.
- W4206724263 creator A5045192948 @default.
- W4206724263 creator A5050907307 @default.
- W4206724263 creator A5069246539 @default.
- W4206724263 date "2022-01-01" @default.
- W4206724263 modified "2023-09-30" @default.
- W4206724263 title "Temperature and strain distribution during friction stir welding of AA6061 and AA5052 aluminum alloy using deform 3D" @default.
- W4206724263 cites W1997461014 @default.
- W4206724263 cites W2473893475 @default.
- W4206724263 cites W2607974993 @default.
- W4206724263 cites W2790915573 @default.
- W4206724263 cites W2980837237 @default.
- W4206724263 cites W2999909766 @default.
- W4206724263 cites W3016889180 @default.
- W4206724263 doi "https://doi.org/10.1016/j.matpr.2021.12.085" @default.
- W4206724263 hasPublicationYear "2022" @default.
- W4206724263 type Work @default.
- W4206724263 citedByCount "4" @default.
- W4206724263 countsByYear W42067242632023 @default.
- W4206724263 crossrefType "journal-article" @default.
- W4206724263 hasAuthorship W4206724263A5006614151 @default.
- W4206724263 hasAuthorship W4206724263A5045192948 @default.
- W4206724263 hasAuthorship W4206724263A5050907307 @default.
- W4206724263 hasAuthorship W4206724263A5069246539 @default.
- W4206724263 hasConcept C127413603 @default.
- W4206724263 hasConcept C149342994 @default.
- W4206724263 hasConcept C159985019 @default.
- W4206724263 hasConcept C168068576 @default.
- W4206724263 hasConcept C191897082 @default.
- W4206724263 hasConcept C192562407 @default.
- W4206724263 hasConcept C19474535 @default.
- W4206724263 hasConcept C2779821118 @default.
- W4206724263 hasConcept C2780026712 @default.
- W4206724263 hasConcept C40241539 @default.
- W4206724263 hasConcept C40367268 @default.
- W4206724263 hasConcept C513153333 @default.
- W4206724263 hasConcept C78519656 @default.
- W4206724263 hasConcept C81063470 @default.
- W4206724263 hasConcept C83469408 @default.
- W4206724263 hasConcept C87976508 @default.
- W4206724263 hasConceptScore W4206724263C127413603 @default.
- W4206724263 hasConceptScore W4206724263C149342994 @default.
- W4206724263 hasConceptScore W4206724263C159985019 @default.
- W4206724263 hasConceptScore W4206724263C168068576 @default.
- W4206724263 hasConceptScore W4206724263C191897082 @default.
- W4206724263 hasConceptScore W4206724263C192562407 @default.
- W4206724263 hasConceptScore W4206724263C19474535 @default.
- W4206724263 hasConceptScore W4206724263C2779821118 @default.
- W4206724263 hasConceptScore W4206724263C2780026712 @default.
- W4206724263 hasConceptScore W4206724263C40241539 @default.
- W4206724263 hasConceptScore W4206724263C40367268 @default.
- W4206724263 hasConceptScore W4206724263C513153333 @default.
- W4206724263 hasConceptScore W4206724263C78519656 @default.
- W4206724263 hasConceptScore W4206724263C81063470 @default.
- W4206724263 hasConceptScore W4206724263C83469408 @default.
- W4206724263 hasConceptScore W4206724263C87976508 @default.
- W4206724263 hasLocation W42067242631 @default.
- W4206724263 hasOpenAccess W4206724263 @default.
- W4206724263 hasPrimaryLocation W42067242631 @default.
- W4206724263 hasRelatedWork W1972584411 @default.
- W4206724263 hasRelatedWork W2031790272 @default.
- W4206724263 hasRelatedWork W2185500352 @default.
- W4206724263 hasRelatedWork W2383746349 @default.
- W4206724263 hasRelatedWork W2514511647 @default.
- W4206724263 hasRelatedWork W2766262532 @default.
- W4206724263 hasRelatedWork W2791263920 @default.
- W4206724263 hasRelatedWork W2938539780 @default.
- W4206724263 hasRelatedWork W2944952013 @default.
- W4206724263 hasRelatedWork W4323538766 @default.
- W4206724263 hasVolume "59" @default.
- W4206724263 isParatext "false" @default.
- W4206724263 isRetracted "false" @default.
- W4206724263 workType "article" @default.