- W4212855650 abstract "Face-centered-cubic (FCC) Fe40Mn20Cr20Ni20 high-entropy alloys (HEAs) with a weigh of 50 Kg were fabricated by industrialized vacuum-induction melting. This alloy consists of a tetragonal σ phase and minority M23C6 carbides embedded in the continuous FCC matrix after thermomechanical treatments. A heterogeneous structure composed of a phase distribution and grain size is formed. The yield strength and ultimate tensile strength are increased from 398 MPa to 679 MPa at 10−4 s−1 to 743 MPa and 1412 MPa at 3000 s−1, respectively. Meanwhile, the elongation is slightly improved as the strain rate rises. The strain rate sensitivity under quasi-static tension is 0.0172, in contrast to 0.3978 under dynamic deformation. Upon dynamic tension, the simultaneous enhancements of both strength and ductility are attributed to the joint activation of multiple strengthening mechanisms. Deformation-induced twinning further improves the strain-hardening ability of the alloy. Besides, short range order may seriously hinder the dislocation movement, especially when the thermal activation of dislocations gradually fails at high strain rates, which limit the dislocation slip to a smaller scale and result in deformed sub-grains. In contrast, under quasi-static tension, only dislocation slip dominates, accompanied by dislocation entanglement and massive pile-ups. Moreover, a typical Johnson-Cook model was employed to predict the dynamic-flow behavior. This study sheds lights on the mechanical performance superiority from heterogeneous HEAs under dynamic tension and might open new insights for developing high-performance HEAs to resist dynamic impacts." @default.
- W4212855650 created "2022-02-24" @default.
- W4212855650 creator A5009305334 @default.
- W4212855650 creator A5011905020 @default.
- W4212855650 creator A5015719512 @default.
- W4212855650 creator A5027297848 @default.
- W4212855650 creator A5033713425 @default.
- W4212855650 creator A5036956998 @default.
- W4212855650 creator A5045616202 @default.
- W4212855650 creator A5068940266 @default.
- W4212855650 date "2022-04-01" @default.
- W4212855650 modified "2023-10-14" @default.
- W4212855650 title "Dynamic tension and constitutive model in Fe40Mn20Cr20Ni20 high-entropy alloys with a heterogeneous structure" @default.
- W4212855650 cites W1965617158 @default.
- W4212855650 cites W1968985108 @default.
- W4212855650 cites W1972490279 @default.
- W4212855650 cites W1979766176 @default.
- W4212855650 cites W1981789628 @default.
- W4212855650 cites W1993506931 @default.
- W4212855650 cites W1996413252 @default.
- W4212855650 cites W2003975937 @default.
- W4212855650 cites W2022723071 @default.
- W4212855650 cites W2023668998 @default.
- W4212855650 cites W2039061417 @default.
- W4212855650 cites W2040096310 @default.
- W4212855650 cites W2054293435 @default.
- W4212855650 cites W2058085399 @default.
- W4212855650 cites W2065251521 @default.
- W4212855650 cites W2066578528 @default.
- W4212855650 cites W2075098688 @default.
- W4212855650 cites W2078492700 @default.
- W4212855650 cites W2086827153 @default.
- W4212855650 cites W2090989574 @default.
- W4212855650 cites W2093974253 @default.
- W4212855650 cites W2096810472 @default.
- W4212855650 cites W2111613810 @default.
- W4212855650 cites W2113247183 @default.
- W4212855650 cites W2169281412 @default.
- W4212855650 cites W2195577347 @default.
- W4212855650 cites W2299593614 @default.
- W4212855650 cites W2408247608 @default.
- W4212855650 cites W2494516016 @default.
- W4212855650 cites W2507397129 @default.
- W4212855650 cites W2518946889 @default.
- W4212855650 cites W2534691303 @default.
- W4212855650 cites W2551931795 @default.
- W4212855650 cites W2557572537 @default.
- W4212855650 cites W2588418573 @default.
- W4212855650 cites W2590213398 @default.
- W4212855650 cites W2590620339 @default.
- W4212855650 cites W2605865700 @default.
- W4212855650 cites W2614756363 @default.
- W4212855650 cites W2615755808 @default.
- W4212855650 cites W2622849719 @default.
- W4212855650 cites W2726887920 @default.
- W4212855650 cites W2734956595 @default.
- W4212855650 cites W2766778477 @default.
- W4212855650 cites W2771236453 @default.
- W4212855650 cites W2782516741 @default.
- W4212855650 cites W2791121806 @default.
- W4212855650 cites W2791485504 @default.
- W4212855650 cites W2792232135 @default.
- W4212855650 cites W2795755990 @default.
- W4212855650 cites W2798115165 @default.
- W4212855650 cites W2799328146 @default.
- W4212855650 cites W2801320419 @default.
- W4212855650 cites W2889738569 @default.
- W4212855650 cites W2898966069 @default.
- W4212855650 cites W2919922616 @default.
- W4212855650 cites W2944127423 @default.
- W4212855650 cites W2945676487 @default.
- W4212855650 cites W2969543315 @default.
- W4212855650 cites W2971042528 @default.
- W4212855650 cites W2995569610 @default.
- W4212855650 cites W3002389536 @default.
- W4212855650 cites W3024509282 @default.
- W4212855650 cites W3033000340 @default.
- W4212855650 cites W3036119466 @default.
- W4212855650 cites W3036260226 @default.
- W4212855650 cites W3041645345 @default.
- W4212855650 cites W3045464332 @default.
- W4212855650 cites W3076296969 @default.
- W4212855650 cites W3080112152 @default.
- W4212855650 cites W3080505970 @default.
- W4212855650 cites W3081393111 @default.
- W4212855650 cites W3082372182 @default.
- W4212855650 cites W3086876396 @default.
- W4212855650 cites W3098243865 @default.
- W4212855650 cites W3114426413 @default.
- W4212855650 cites W3120842599 @default.
- W4212855650 cites W3138774688 @default.
- W4212855650 cites W3189991032 @default.
- W4212855650 cites W3194272510 @default.
- W4212855650 cites W4200314593 @default.
- W4212855650 doi "https://doi.org/10.1016/j.msea.2022.142837" @default.
- W4212855650 hasPublicationYear "2022" @default.
- W4212855650 type Work @default.
- W4212855650 citedByCount "13" @default.