- W4221003461 endingPage "108059" @default.
- W4221003461 startingPage "108059" @default.
- W4221003461 abstract "This Data in Brief article presents crystallographic data collected along chloride-induced stress corrosion cracks (CISCC) in a gas tungsten arc welded (GTAW) austenitic stainless steel (AuSS) 304L. The experimental setup involved a welded stainless steel 304L coupon of dimensions 105 mm × 18.5 mm × 3 mm, loaded in a 4-point bending fixture with a maximum tensile stress of 380 MPa. The fixtured specimen was immersed in boiling magnesium chloride (MgCl2) solution until a through-crack was observed on the specimen surface after 17 hours of boiling. The cross-section was subsequently polished, and 37 cracks of interest in the heat affected zone (HAZ) and weld zone (WZ) were selected for crystallographic characterization. Scanning electron microscopy (SEM) based electron backscatter diffraction (EBSD) was used to map the grain orientations along and surrounding each crack path. The obtained orientation imaging microscopy (OIM) datasets were post-processed using EDAX OIM V8 proprietary software to generate inverse pole figures (IPF), image quality (IQ) figures, detector signal (SEM) images, and to determine the Taylor factor and Schmid factor of mapped grains. This dataset can be used to understand CISCC crack initiation, propagation, and termination behaviors, as has been reported in the accompanying original research article. This data article providing the raw EBSD OIM datasets and processed images formatted for accessibility in future studies. This comprehensive EBSD dataset can further be used to extract grain boundary misorientation information; benchmark comparative studies of SCC/CISCC in AuSS and other Fe or Ni alloys; and provide critical validation data on grain morphology, misorientation, and crystallography for GTAW and CISCC models." @default.
- W4221003461 created "2022-04-03" @default.
- W4221003461 creator A5016022039 @default.
- W4221003461 creator A5077063025 @default.
- W4221003461 date "2022-06-01" @default.
- W4221003461 modified "2023-10-14" @default.
- W4221003461 title "Crystallographic orientation data from chloride-induced stress corrosion crack (CISCC) paths in gas tungsten arc welded (GTAW) austenitic stainless steel 304L" @default.
- W4221003461 cites W2908626277 @default.
- W4221003461 cites W4239366181 @default.
- W4221003461 doi "https://doi.org/10.1016/j.dib.2022.108059" @default.
- W4221003461 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/35345845" @default.
- W4221003461 hasPublicationYear "2022" @default.
- W4221003461 type Work @default.
- W4221003461 citedByCount "3" @default.
- W4221003461 countsByYear W42210034612022 @default.
- W4221003461 crossrefType "journal-article" @default.
- W4221003461 hasAuthorship W4221003461A5016022039 @default.
- W4221003461 hasAuthorship W4221003461A5077063025 @default.
- W4221003461 hasBestOaLocation W42210034611 @default.
- W4221003461 hasConcept C159985019 @default.
- W4221003461 hasConcept C191897082 @default.
- W4221003461 hasConcept C192562407 @default.
- W4221003461 hasConcept C19474535 @default.
- W4221003461 hasConcept C20480867 @default.
- W4221003461 hasConcept C20625102 @default.
- W4221003461 hasConcept C26771246 @default.
- W4221003461 hasConcept C2778117898 @default.
- W4221003461 hasConcept C2778760603 @default.
- W4221003461 hasConcept C2779229422 @default.
- W4221003461 hasConcept C27805521 @default.
- W4221003461 hasConcept C3450827 @default.
- W4221003461 hasConcept C47908070 @default.
- W4221003461 hasConcept C87976508 @default.
- W4221003461 hasConceptScore W4221003461C159985019 @default.
- W4221003461 hasConceptScore W4221003461C191897082 @default.
- W4221003461 hasConceptScore W4221003461C192562407 @default.
- W4221003461 hasConceptScore W4221003461C19474535 @default.
- W4221003461 hasConceptScore W4221003461C20480867 @default.
- W4221003461 hasConceptScore W4221003461C20625102 @default.
- W4221003461 hasConceptScore W4221003461C26771246 @default.
- W4221003461 hasConceptScore W4221003461C2778117898 @default.
- W4221003461 hasConceptScore W4221003461C2778760603 @default.
- W4221003461 hasConceptScore W4221003461C2779229422 @default.
- W4221003461 hasConceptScore W4221003461C27805521 @default.
- W4221003461 hasConceptScore W4221003461C3450827 @default.
- W4221003461 hasConceptScore W4221003461C47908070 @default.
- W4221003461 hasConceptScore W4221003461C87976508 @default.
- W4221003461 hasFunder F4320306084 @default.
- W4221003461 hasFunder F4320332364 @default.
- W4221003461 hasLocation W42210034611 @default.
- W4221003461 hasLocation W42210034612 @default.
- W4221003461 hasLocation W42210034613 @default.
- W4221003461 hasLocation W42210034614 @default.
- W4221003461 hasOpenAccess W4221003461 @default.
- W4221003461 hasPrimaryLocation W42210034611 @default.
- W4221003461 hasRelatedWork W1983338805 @default.
- W4221003461 hasRelatedWork W2035573963 @default.
- W4221003461 hasRelatedWork W2135581715 @default.
- W4221003461 hasRelatedWork W2287929894 @default.
- W4221003461 hasRelatedWork W2313687183 @default.
- W4221003461 hasRelatedWork W2378773533 @default.
- W4221003461 hasRelatedWork W2386890856 @default.
- W4221003461 hasRelatedWork W2389453758 @default.
- W4221003461 hasRelatedWork W2901588016 @default.
- W4221003461 hasRelatedWork W1537097370 @default.
- W4221003461 hasVolume "42" @default.
- W4221003461 isParatext "false" @default.
- W4221003461 isRetracted "false" @default.
- W4221003461 workType "article" @default.