- W4225544983 abstract "The purpose of the present study is to track the formation of the intermetallic phases that form in the binary Al-Mg system and investigate their orientation relationships to the parent Al and Mg elements. Therefore, two compositions Al60Mg40 and Al40Mg60 (wt%), which are very suitable for studying the diffusion of Al in Mg and Mg in Al were heated from room temperature up to elevated temperatures below the melting point. Powder metallurgy, including cold extrusion was used to create a large interface between the Al and Mg, which facilitates fast reaction kinetics. In order to observe the phase formation during heating and analyze the crystal structures, X-ray diffraction using synchrotron radiation was used. The use of high energy X-ray was extremely helpful, enabling the detection of small phase fractions and information on the orientation relationships between the Al and Mg and the intermetallic phases that formed. The γ-Al12Mg17phase was the first phase formed in both alloy compositions on annealing. Subsequently, the β-Al3Mg2phase was formed. After annealing at 400 ºC for 2 h, the Al40Mg60 composition consisted of a very high amount of Al12Mg17 and a small amount of Mg phase while the Al60Mg40 composition consisted of mainly Al3Mg2 and a small fraction of Al12Mg17, indicating that thermodynamic equilibrium has been approximated. On further annealing at 400 ºC for 12 h, both compositions formed only one phase, namely the Al12Mg17 phase in the Al40Mg60 composition and the Al3Mg2 phase in the Al60Mg40 composition. In this condition, a Pitsch-Schrader orientation relationship was found between the Mg and the γ-Al12Mg17 phase, the occurrence of which is discussed within the framework of literature models. No orientation relationship between either the Al or the Mg with the Al3Mg2 phase was found." @default.
- W4225544983 created "2022-05-05" @default.
- W4225544983 creator A5007489330 @default.
- W4225544983 creator A5012749248 @default.
- W4225544983 creator A5026699674 @default.
- W4225544983 date "2022-08-01" @default.
- W4225544983 modified "2023-10-18" @default.
- W4225544983 title "Formation of the intermetallic phases Al12Mg17 and Al3Mg2 during heating of elemental Al-Mg composites studied by high-energy X-ray diffraction" @default.
- W4225544983 cites W1576261241 @default.
- W4225544983 cites W1586764493 @default.
- W4225544983 cites W1629916531 @default.
- W4225544983 cites W188801585 @default.
- W4225544983 cites W1949615099 @default.
- W4225544983 cites W1966350606 @default.
- W4225544983 cites W1967091917 @default.
- W4225544983 cites W1971955525 @default.
- W4225544983 cites W1973504237 @default.
- W4225544983 cites W1973642582 @default.
- W4225544983 cites W1976429604 @default.
- W4225544983 cites W1978445581 @default.
- W4225544983 cites W1980580865 @default.
- W4225544983 cites W1983425573 @default.
- W4225544983 cites W1986862346 @default.
- W4225544983 cites W1993254642 @default.
- W4225544983 cites W1998829816 @default.
- W4225544983 cites W2001091777 @default.
- W4225544983 cites W2014690755 @default.
- W4225544983 cites W2016260972 @default.
- W4225544983 cites W2032152569 @default.
- W4225544983 cites W2046878793 @default.
- W4225544983 cites W2050220304 @default.
- W4225544983 cites W2050692007 @default.
- W4225544983 cites W2058341071 @default.
- W4225544983 cites W2061281673 @default.
- W4225544983 cites W2061812654 @default.
- W4225544983 cites W2062088581 @default.
- W4225544983 cites W2068065633 @default.
- W4225544983 cites W2069657514 @default.
- W4225544983 cites W2069710604 @default.
- W4225544983 cites W2071262716 @default.
- W4225544983 cites W2089396978 @default.
- W4225544983 cites W2108439616 @default.
- W4225544983 cites W2115068143 @default.
- W4225544983 cites W2121707484 @default.
- W4225544983 cites W2133782191 @default.
- W4225544983 cites W2145900101 @default.
- W4225544983 cites W2164993505 @default.
- W4225544983 cites W2232493493 @default.
- W4225544983 cites W2561861479 @default.
- W4225544983 cites W2587356893 @default.
- W4225544983 cites W2911675981 @default.
- W4225544983 cites W3037918056 @default.
- W4225544983 cites W4235341129 @default.
- W4225544983 cites W4251263555 @default.
- W4225544983 doi "https://doi.org/10.1016/j.jallcom.2022.165114" @default.
- W4225544983 hasPublicationYear "2022" @default.
- W4225544983 type Work @default.
- W4225544983 citedByCount "4" @default.
- W4225544983 countsByYear W42255449832022 @default.
- W4225544983 countsByYear W42255449832023 @default.
- W4225544983 crossrefType "journal-article" @default.
- W4225544983 hasAuthorship W4225544983A5007489330 @default.
- W4225544983 hasAuthorship W4225544983A5012749248 @default.
- W4225544983 hasAuthorship W4225544983A5026699674 @default.
- W4225544983 hasConcept C113196181 @default.
- W4225544983 hasConcept C178790620 @default.
- W4225544983 hasConcept C185592680 @default.
- W4225544983 hasConcept C191897082 @default.
- W4225544983 hasConcept C192562407 @default.
- W4225544983 hasConcept C27501479 @default.
- W4225544983 hasConcept C2777855556 @default.
- W4225544983 hasConcept C2780026712 @default.
- W4225544983 hasConcept C44280652 @default.
- W4225544983 hasConcept C8010536 @default.
- W4225544983 hasConceptScore W4225544983C113196181 @default.
- W4225544983 hasConceptScore W4225544983C178790620 @default.
- W4225544983 hasConceptScore W4225544983C185592680 @default.
- W4225544983 hasConceptScore W4225544983C191897082 @default.
- W4225544983 hasConceptScore W4225544983C192562407 @default.
- W4225544983 hasConceptScore W4225544983C27501479 @default.
- W4225544983 hasConceptScore W4225544983C2777855556 @default.
- W4225544983 hasConceptScore W4225544983C2780026712 @default.
- W4225544983 hasConceptScore W4225544983C44280652 @default.
- W4225544983 hasConceptScore W4225544983C8010536 @default.
- W4225544983 hasLocation W42255449831 @default.
- W4225544983 hasOpenAccess W4225544983 @default.
- W4225544983 hasPrimaryLocation W42255449831 @default.
- W4225544983 hasRelatedWork W1963767451 @default.
- W4225544983 hasRelatedWork W1999552040 @default.
- W4225544983 hasRelatedWork W2046330920 @default.
- W4225544983 hasRelatedWork W2075616172 @default.
- W4225544983 hasRelatedWork W2089251307 @default.
- W4225544983 hasRelatedWork W2109470534 @default.
- W4225544983 hasRelatedWork W2316597249 @default.
- W4225544983 hasRelatedWork W2766515653 @default.
- W4225544983 hasRelatedWork W2970076452 @default.
- W4225544983 hasRelatedWork W3094239684 @default.
- W4225544983 hasVolume "911" @default.