- W4225742955 endingPage "106218" @default.
- W4225742955 startingPage "106218" @default.
- W4225742955 abstract "The failure investigation of a thermocouple protective sheath tube made of UMCo-50 cobalt base alloy exposed to SO2-bearing hot gas in a sulfur refining furnace was systematically conducted. Various microstructural examination techniques were employed in order to clarify a root cause of failure. A tip portion of protective sheath tube remarkably revealed its severe material degradation after exposure to SO2-bearing hot gas in service for approximately 6 months. From the investigation, it turned out that the alloy was significantly prone to sulfidation attacks due to the formation of undesired chromium-rich carbides in its structure, which was accelerated by temperature fluctuation between 550 and 1100 °C during service. As a result, the protective sheath tube could not last for approximately 3 years as its design life." @default.
- W4225742955 created "2022-05-05" @default.
- W4225742955 creator A5005292271 @default.
- W4225742955 creator A5011407992 @default.
- W4225742955 creator A5087379854 @default.
- W4225742955 date "2022-08-01" @default.
- W4225742955 modified "2023-09-26" @default.
- W4225742955 title "Sulfidation failure of UMCo-50 protective sheath tube used for a temperature monitoring device exposed to sulfur dioxide bearing hot gas" @default.
- W4225742955 cites W1969617755 @default.
- W4225742955 cites W1974336038 @default.
- W4225742955 cites W1983047243 @default.
- W4225742955 cites W1988062304 @default.
- W4225742955 cites W2002663673 @default.
- W4225742955 cites W200520573 @default.
- W4225742955 cites W2041385976 @default.
- W4225742955 cites W2042877247 @default.
- W4225742955 cites W2043382584 @default.
- W4225742955 cites W2045104029 @default.
- W4225742955 cites W2046440846 @default.
- W4225742955 cites W2058550089 @default.
- W4225742955 cites W2079990289 @default.
- W4225742955 cites W2135187474 @default.
- W4225742955 cites W2147582307 @default.
- W4225742955 cites W2284242587 @default.
- W4225742955 cites W2541776042 @default.
- W4225742955 cites W2772445118 @default.
- W4225742955 cites W283591225 @default.
- W4225742955 cites W4213278840 @default.
- W4225742955 cites W4241412832 @default.
- W4225742955 cites W50736516 @default.
- W4225742955 doi "https://doi.org/10.1016/j.engfailanal.2022.106218" @default.
- W4225742955 hasPublicationYear "2022" @default.
- W4225742955 type Work @default.
- W4225742955 citedByCount "0" @default.
- W4225742955 crossrefType "journal-article" @default.
- W4225742955 hasAuthorship W4225742955A5005292271 @default.
- W4225742955 hasAuthorship W4225742955A5011407992 @default.
- W4225742955 hasAuthorship W4225742955A5087379854 @default.
- W4225742955 hasConcept C103208741 @default.
- W4225742955 hasConcept C127413603 @default.
- W4225742955 hasConcept C159985019 @default.
- W4225742955 hasConcept C168068576 @default.
- W4225742955 hasConcept C179104552 @default.
- W4225742955 hasConcept C185592680 @default.
- W4225742955 hasConcept C191897082 @default.
- W4225742955 hasConcept C192562407 @default.
- W4225742955 hasConcept C199978012 @default.
- W4225742955 hasConcept C205649164 @default.
- W4225742955 hasConcept C2777551473 @default.
- W4225742955 hasConcept C2778480967 @default.
- W4225742955 hasConcept C2780447027 @default.
- W4225742955 hasConcept C2781333061 @default.
- W4225742955 hasConcept C42360764 @default.
- W4225742955 hasConcept C511782168 @default.
- W4225742955 hasConcept C518881349 @default.
- W4225742955 hasConcept C5335593 @default.
- W4225742955 hasConcept C58640448 @default.
- W4225742955 hasConceptScore W4225742955C103208741 @default.
- W4225742955 hasConceptScore W4225742955C127413603 @default.
- W4225742955 hasConceptScore W4225742955C159985019 @default.
- W4225742955 hasConceptScore W4225742955C168068576 @default.
- W4225742955 hasConceptScore W4225742955C179104552 @default.
- W4225742955 hasConceptScore W4225742955C185592680 @default.
- W4225742955 hasConceptScore W4225742955C191897082 @default.
- W4225742955 hasConceptScore W4225742955C192562407 @default.
- W4225742955 hasConceptScore W4225742955C199978012 @default.
- W4225742955 hasConceptScore W4225742955C205649164 @default.
- W4225742955 hasConceptScore W4225742955C2777551473 @default.
- W4225742955 hasConceptScore W4225742955C2778480967 @default.
- W4225742955 hasConceptScore W4225742955C2780447027 @default.
- W4225742955 hasConceptScore W4225742955C2781333061 @default.
- W4225742955 hasConceptScore W4225742955C42360764 @default.
- W4225742955 hasConceptScore W4225742955C511782168 @default.
- W4225742955 hasConceptScore W4225742955C518881349 @default.
- W4225742955 hasConceptScore W4225742955C5335593 @default.
- W4225742955 hasConceptScore W4225742955C58640448 @default.
- W4225742955 hasFunder F4320324523 @default.
- W4225742955 hasLocation W42257429551 @default.
- W4225742955 hasOpenAccess W4225742955 @default.
- W4225742955 hasPrimaryLocation W42257429551 @default.
- W4225742955 hasRelatedWork W1515659654 @default.
- W4225742955 hasRelatedWork W1969459558 @default.
- W4225742955 hasRelatedWork W1983585095 @default.
- W4225742955 hasRelatedWork W1991670989 @default.
- W4225742955 hasRelatedWork W2071550242 @default.
- W4225742955 hasRelatedWork W2103275632 @default.
- W4225742955 hasRelatedWork W2353228182 @default.
- W4225742955 hasRelatedWork W2374000539 @default.
- W4225742955 hasRelatedWork W4256489876 @default.
- W4225742955 hasRelatedWork W4320525573 @default.
- W4225742955 hasVolume "138" @default.
- W4225742955 isParatext "false" @default.
- W4225742955 isRetracted "false" @default.
- W4225742955 workType "article" @default.