- W4230235114 abstract "Abstract Mechanical properties and transmission electron microscopy studies of single crystals of γ–Ti–54.5 at.% Al of various orientations for which ordinary slip occurs show that at the temperature T p of the peak stress of the yield stress anomaly (YSA) the critical resolved shear stresses (CRSSs) for ordinary slip on {110) and {111} are comparable, and that above T p, the CRSS on {110) decreases rapidly with increasing temperature. The glide loops on (110) are elongated along the [001] direction, indicating the low mobility of edge dislocations. Below T p, slip occurs on {111} and the screw dislocations are much less mobile than the edge dislocations, forming effectively long locks. Further slip (unlocking) is thought to occur by the generation and glide of edge superkinks along the screw direction. In the region of the YSA, before unlocking occurs, the screws bow out, mainly on {111} and partly on {110), the latter resulting in relatively immobile jogs which act as obstacles to slip on {111} and to the motion of the superkinks. Bowing on {110) has been observed in this work and by others. The YSA is considered to be due to increasing amounts of bowing on {110) with increasing temperature, and thus the formation of larger jogs on {110) in dislocations gliding on {111}. The driving forces for this mechanism are attributed to the screw dislocations having a minimum line tension on {110) and, except for alloys with less than about 54 at.% Al, to a lower resistance from the effect of short-range order associated with the Al5Ti3 phase for slip on {110) than on {111}. The large activation volumes observed below T p are thought to be associated with mechanisms controlling the generation and motion of edge superkinks. involving thermally activated processes including climb at small jogs, and various mechanisms of cross-slip. Above T p the rate-controlling process is considered to be thermally activated or climb-controlled glide of edge dislocations on {110) planes. The model for the YSA is discussed in the light of results from other studies." @default.
- W4230235114 created "2022-05-11" @default.
- W4230235114 creator A5035888386 @default.
- W4230235114 date "2001-01-01" @default.
- W4230235114 modified "2023-10-14" @default.
- W4230235114 title "Yield stress anomalies in single crystals of Ti-54.5 at.% Al III. Ordinary slip" @default.
- W4230235114 doi "https://doi.org/10.1080/014186101300012525" @default.
- W4230235114 hasPublicationYear "2001" @default.
- W4230235114 type Work @default.
- W4230235114 citedByCount "0" @default.
- W4230235114 crossrefType "journal-article" @default.
- W4230235114 hasAuthorship W4230235114A5035888386 @default.
- W4230235114 hasConcept C121332964 @default.
- W4230235114 hasConcept C127172972 @default.
- W4230235114 hasConcept C138885662 @default.
- W4230235114 hasConcept C146088050 @default.
- W4230235114 hasConcept C159122135 @default.
- W4230235114 hasConcept C159985019 @default.
- W4230235114 hasConcept C165682214 @default.
- W4230235114 hasConcept C171250308 @default.
- W4230235114 hasConcept C185592680 @default.
- W4230235114 hasConcept C192562407 @default.
- W4230235114 hasConcept C195268267 @default.
- W4230235114 hasConcept C207647181 @default.
- W4230235114 hasConcept C21141959 @default.
- W4230235114 hasConcept C26873012 @default.
- W4230235114 hasConcept C27206212 @default.
- W4230235114 hasConcept C2780787355 @default.
- W4230235114 hasConcept C30445746 @default.
- W4230235114 hasConcept C41234517 @default.
- W4230235114 hasConcept C8010536 @default.
- W4230235114 hasConcept C97355855 @default.
- W4230235114 hasConceptScore W4230235114C121332964 @default.
- W4230235114 hasConceptScore W4230235114C127172972 @default.
- W4230235114 hasConceptScore W4230235114C138885662 @default.
- W4230235114 hasConceptScore W4230235114C146088050 @default.
- W4230235114 hasConceptScore W4230235114C159122135 @default.
- W4230235114 hasConceptScore W4230235114C159985019 @default.
- W4230235114 hasConceptScore W4230235114C165682214 @default.
- W4230235114 hasConceptScore W4230235114C171250308 @default.
- W4230235114 hasConceptScore W4230235114C185592680 @default.
- W4230235114 hasConceptScore W4230235114C192562407 @default.
- W4230235114 hasConceptScore W4230235114C195268267 @default.
- W4230235114 hasConceptScore W4230235114C207647181 @default.
- W4230235114 hasConceptScore W4230235114C21141959 @default.
- W4230235114 hasConceptScore W4230235114C26873012 @default.
- W4230235114 hasConceptScore W4230235114C27206212 @default.
- W4230235114 hasConceptScore W4230235114C2780787355 @default.
- W4230235114 hasConceptScore W4230235114C30445746 @default.
- W4230235114 hasConceptScore W4230235114C41234517 @default.
- W4230235114 hasConceptScore W4230235114C8010536 @default.
- W4230235114 hasConceptScore W4230235114C97355855 @default.
- W4230235114 hasIssue "1" @default.
- W4230235114 hasLocation W42302351141 @default.
- W4230235114 hasOpenAccess W4230235114 @default.
- W4230235114 hasPrimaryLocation W42302351141 @default.
- W4230235114 hasRelatedWork W1987290081 @default.
- W4230235114 hasRelatedWork W1998280638 @default.
- W4230235114 hasRelatedWork W2062725923 @default.
- W4230235114 hasRelatedWork W2316074972 @default.
- W4230235114 hasRelatedWork W2384512752 @default.
- W4230235114 hasRelatedWork W2601835951 @default.
- W4230235114 hasRelatedWork W2756836630 @default.
- W4230235114 hasRelatedWork W3035732769 @default.
- W4230235114 hasRelatedWork W4238782173 @default.
- W4230235114 hasRelatedWork W434909130 @default.
- W4230235114 hasVolume "81" @default.
- W4230235114 isParatext "false" @default.
- W4230235114 isRetracted "false" @default.
- W4230235114 workType "article" @default.