- W4231704722 endingPage "543" @default.
- W4231704722 startingPage "526" @default.
- W4231704722 abstract "A programme of tests has been conducted to characterise the strength reduction of three GRP composite materials as a function of temperature and testing environment. The GRP materials and testing environments were selected to be of maximum relevance to the offshore industry. The materials were E-glass fibre reinforcement in matrices of three resins: two epoxies and phenolic. The testing environments were sea water and crude oil condensate. The temperature range tested was ambient to 150°C. The tests were performed on coupon specimens laminated using fibres in the form of woven mat. The fibres were aligned so as to allow testing in both fibre dominated and resin dominated failure modes. A novel environmental tensile testing facility was developed for this work, and this is described briefly. Results are presented for the strength of the three materials as a function of temperature in each failure mode when tested dry. These are then compared with equivalent results for the specimens tested in the liquid environments. This is the first reported measurement of GRP strength in liquid environments at these very high temperatures. It is demonstrated from the results that strength reduction is exhibited predominantly in the matrix dominated failure mode, though a small but significant strength reduction is also seen in the fibre dominated mode. Causes for these strength reductions are identified as lowered glass transition temperature and degradation of the glass and glass/resin interfaces respectively. The strength reductions for each combination of material and environment are quantified. Finally, appropriate limits to operating temperature are suggested for each material when used in an offshore environment." @default.
- W4231704722 created "2022-05-12" @default.
- W4231704722 creator A5001679220 @default.
- W4231704722 creator A5075772937 @default.
- W4231704722 date "1998-03-01" @default.
- W4231704722 modified "2023-09-27" @default.
- W4231704722 title "Coupon Tests of Fibre Reinforced Plastics at Elevated Temperatures in Offshore Processing Environments" @default.
- W4231704722 cites W1975030247 @default.
- W4231704722 cites W1975674733 @default.
- W4231704722 cites W1989401028 @default.
- W4231704722 cites W2000705094 @default.
- W4231704722 cites W2027242113 @default.
- W4231704722 cites W2063699664 @default.
- W4231704722 cites W2069746236 @default.
- W4231704722 cites W2136043247 @default.
- W4231704722 cites W2273130837 @default.
- W4231704722 cites W2504703180 @default.
- W4231704722 doi "https://doi.org/10.1177/002199839803200602" @default.
- W4231704722 hasPublicationYear "1998" @default.
- W4231704722 type Work @default.
- W4231704722 citedByCount "7" @default.
- W4231704722 countsByYear W42317047222015 @default.
- W4231704722 countsByYear W42317047222020 @default.
- W4231704722 countsByYear W42317047222023 @default.
- W4231704722 crossrefType "journal-article" @default.
- W4231704722 hasAuthorship W4231704722A5001679220 @default.
- W4231704722 hasAuthorship W4231704722A5075772937 @default.
- W4231704722 hasConcept C102267420 @default.
- W4231704722 hasConcept C112950240 @default.
- W4231704722 hasConcept C123453687 @default.
- W4231704722 hasConcept C127413603 @default.
- W4231704722 hasConcept C135628077 @default.
- W4231704722 hasConcept C151730666 @default.
- W4231704722 hasConcept C159985019 @default.
- W4231704722 hasConcept C166595027 @default.
- W4231704722 hasConcept C177229083 @default.
- W4231704722 hasConcept C192562407 @default.
- W4231704722 hasConcept C30239060 @default.
- W4231704722 hasConcept C58097730 @default.
- W4231704722 hasConcept C66283442 @default.
- W4231704722 hasConcept C66938386 @default.
- W4231704722 hasConcept C77928131 @default.
- W4231704722 hasConcept C86803240 @default.
- W4231704722 hasConceptScore W4231704722C102267420 @default.
- W4231704722 hasConceptScore W4231704722C112950240 @default.
- W4231704722 hasConceptScore W4231704722C123453687 @default.
- W4231704722 hasConceptScore W4231704722C127413603 @default.
- W4231704722 hasConceptScore W4231704722C135628077 @default.
- W4231704722 hasConceptScore W4231704722C151730666 @default.
- W4231704722 hasConceptScore W4231704722C159985019 @default.
- W4231704722 hasConceptScore W4231704722C166595027 @default.
- W4231704722 hasConceptScore W4231704722C177229083 @default.
- W4231704722 hasConceptScore W4231704722C192562407 @default.
- W4231704722 hasConceptScore W4231704722C30239060 @default.
- W4231704722 hasConceptScore W4231704722C58097730 @default.
- W4231704722 hasConceptScore W4231704722C66283442 @default.
- W4231704722 hasConceptScore W4231704722C66938386 @default.
- W4231704722 hasConceptScore W4231704722C77928131 @default.
- W4231704722 hasConceptScore W4231704722C86803240 @default.
- W4231704722 hasIssue "6" @default.
- W4231704722 hasLocation W42317047221 @default.
- W4231704722 hasOpenAccess W4231704722 @default.
- W4231704722 hasPrimaryLocation W42317047221 @default.
- W4231704722 hasRelatedWork W1975608897 @default.
- W4231704722 hasRelatedWork W2072775309 @default.
- W4231704722 hasRelatedWork W2136458310 @default.
- W4231704722 hasRelatedWork W2413437261 @default.
- W4231704722 hasRelatedWork W2766317656 @default.
- W4231704722 hasRelatedWork W2766828284 @default.
- W4231704722 hasRelatedWork W3035815745 @default.
- W4231704722 hasRelatedWork W3139794476 @default.
- W4231704722 hasRelatedWork W4231704722 @default.
- W4231704722 hasRelatedWork W4285731133 @default.
- W4231704722 hasVolume "32" @default.
- W4231704722 isParatext "false" @default.
- W4231704722 isRetracted "false" @default.
- W4231704722 workType "article" @default.