- W4240051629 abstract "1. Introduction Different Pt‐Pd nanoalloys were prepared from organic precursors in solution. Their nucleation and growth in the liquid was in situ studied in a graphene oxide liquid cell by the direct reduction in the electron beam [1‐3]. Then, the morphological evolution of the nanoalloys under gas pressure was in situ studied in an environmental sample holder [4] by standard TEM. 2. Pt@Pd core shell NPs Increasing amounts of Pt could be deposited on Pd nanocubes cubes by sequential reduction, with a resulting concave shape as seen in fig. 1. Fig.2 is a set of images during the Pt growth around the same Pd cube, during 20 mn. The operating conditions (magnification 800 K, electron density 3. 10 5 A/m 2 ) corresponds to an increasing electron dose. During this time, the variation of liquid quantity in the drop was not visible. From the set of images, it seems that the Pt layer has an homogeneous thickness during the growth, so that the final concave shape results from other steps in the preparation process. Then, the morphology of Pt@Pd nanocubes was in situ observed during oxido reduction cycles in a few mbar of pure O 2 and H 2 . Fig. 3 clearly shows that the Pd@Pt nanocubes have concave shapes in pure H 2 . In pure O 2, they are much rounded at the corners and the (110) facets are extended compared to the same samples in H 2 , as the anisotropy ratio between the surface free energies of (001) and (110) faces, increases from 0.7 in H 2 to 0.8 in O 2 . 3. Properties A maximal reactivity in gas has been found for an equivalent thickness of 0.4 atomic Pt layers on the Pd nanocubes. For this thickness the core‐shell particles are more active than pure Pd cubes or similar Pt cubes reported in literature. This behavior is explained by a decrease of the adsorption energy of molecules, due a compressive strain, induced by the misfit between the two metal bulk lattices and by a ligand effect due to the modification of the electronic structure of Pt atoms in contact with Pd atoms. A similar qualitative evolution as a function of thickness of the Pt layer was already observed in electrocatalysis and was also explained by the decrease of the strength of adsorbed species." @default.
- W4240051629 created "2022-05-12" @default.
- W4240051629 creator A5006113905 @default.
- W4240051629 creator A5044189805 @default.
- W4240051629 creator A5045475004 @default.
- W4240051629 creator A5070618042 @default.
- W4240051629 date "2016-12-20" @default.
- W4240051629 modified "2023-10-04" @default.
- W4240051629 title "In situ TEM study of nanoalloys in solution" @default.
- W4240051629 cites W2046312837 @default.
- W4240051629 cites W2071794968 @default.
- W4240051629 cites W2316977051 @default.
- W4240051629 doi "https://doi.org/10.1002/9783527808465.emc2016.5744" @default.
- W4240051629 hasPublicationYear "2016" @default.
- W4240051629 type Work @default.
- W4240051629 citedByCount "0" @default.
- W4240051629 crossrefType "other" @default.
- W4240051629 hasAuthorship W4240051629A5006113905 @default.
- W4240051629 hasAuthorship W4240051629A5044189805 @default.
- W4240051629 hasAuthorship W4240051629A5045475004 @default.
- W4240051629 hasAuthorship W4240051629A5070618042 @default.
- W4240051629 hasBestOaLocation W42400516291 @default.
- W4240051629 hasConcept C113196181 @default.
- W4240051629 hasConcept C120665830 @default.
- W4240051629 hasConcept C121332964 @default.
- W4240051629 hasConcept C146088050 @default.
- W4240051629 hasConcept C171250308 @default.
- W4240051629 hasConcept C178790620 @default.
- W4240051629 hasConcept C185592680 @default.
- W4240051629 hasConcept C191897082 @default.
- W4240051629 hasConcept C192562407 @default.
- W4240051629 hasConcept C2524010 @default.
- W4240051629 hasConcept C2777822432 @default.
- W4240051629 hasConcept C2779851234 @default.
- W4240051629 hasConcept C33923547 @default.
- W4240051629 hasConcept C43617362 @default.
- W4240051629 hasConcept C499950583 @default.
- W4240051629 hasConcept C53051483 @default.
- W4240051629 hasConcept C54355233 @default.
- W4240051629 hasConcept C61048295 @default.
- W4240051629 hasConcept C66882249 @default.
- W4240051629 hasConcept C8010536 @default.
- W4240051629 hasConcept C85725439 @default.
- W4240051629 hasConcept C86803240 @default.
- W4240051629 hasConcept C97355855 @default.
- W4240051629 hasConceptScore W4240051629C113196181 @default.
- W4240051629 hasConceptScore W4240051629C120665830 @default.
- W4240051629 hasConceptScore W4240051629C121332964 @default.
- W4240051629 hasConceptScore W4240051629C146088050 @default.
- W4240051629 hasConceptScore W4240051629C171250308 @default.
- W4240051629 hasConceptScore W4240051629C178790620 @default.
- W4240051629 hasConceptScore W4240051629C185592680 @default.
- W4240051629 hasConceptScore W4240051629C191897082 @default.
- W4240051629 hasConceptScore W4240051629C192562407 @default.
- W4240051629 hasConceptScore W4240051629C2524010 @default.
- W4240051629 hasConceptScore W4240051629C2777822432 @default.
- W4240051629 hasConceptScore W4240051629C2779851234 @default.
- W4240051629 hasConceptScore W4240051629C33923547 @default.
- W4240051629 hasConceptScore W4240051629C43617362 @default.
- W4240051629 hasConceptScore W4240051629C499950583 @default.
- W4240051629 hasConceptScore W4240051629C53051483 @default.
- W4240051629 hasConceptScore W4240051629C54355233 @default.
- W4240051629 hasConceptScore W4240051629C61048295 @default.
- W4240051629 hasConceptScore W4240051629C66882249 @default.
- W4240051629 hasConceptScore W4240051629C8010536 @default.
- W4240051629 hasConceptScore W4240051629C85725439 @default.
- W4240051629 hasConceptScore W4240051629C86803240 @default.
- W4240051629 hasConceptScore W4240051629C97355855 @default.
- W4240051629 hasLocation W42400516291 @default.
- W4240051629 hasOpenAccess W4240051629 @default.
- W4240051629 hasPrimaryLocation W42400516291 @default.
- W4240051629 hasRelatedWork W1979612817 @default.
- W4240051629 hasRelatedWork W1994722349 @default.
- W4240051629 hasRelatedWork W2032060173 @default.
- W4240051629 hasRelatedWork W2075750484 @default.
- W4240051629 hasRelatedWork W2087566651 @default.
- W4240051629 hasRelatedWork W2601453644 @default.
- W4240051629 hasRelatedWork W2847744229 @default.
- W4240051629 hasRelatedWork W2899084033 @default.
- W4240051629 hasRelatedWork W2912159860 @default.
- W4240051629 hasRelatedWork W3084171500 @default.
- W4240051629 isParatext "false" @default.
- W4240051629 isRetracted "false" @default.
- W4240051629 workType "other" @default.