- W4243445692 abstract "The copolymerization of 6-caprolactam with 12-dodecanelactam with 2 mol-% 6-aminocaproic acid as the initiator was investigated at 260°C within a broad concentration range of both comonomers. With increasing content of 12-dodecanelactam in the initial mixture the equilibrium content of the copolymer increased and the rate of copolymerization decreased. In the initial stage of copolymerization 12-dodecanelactam disappeared very quickly from the initial mixture; it was not incorporated into the copolymer directly, but through oligomers, probably through a cyclic dimer. The effect of temperature on the copolymerization process was examined for an equimolar composition of the initial mixture. It was demonstrated that starting with the polymerization temperature of 260°C, the copolymers underwent degradation on long-termin heating. At 280°C, degradation occured already after 50 h of polymerization. The apparent activation energy of copolymerization, 62 kJ/mol, was calculated from the temperature dependence. Es wurde die Copolymerisation von 6-Caprolactam und 12-Dodecanlactam, initiiert durch 2 mol-% der 6-Aminocapronsäure bei 260°C in einem breiten Konzentrationsbereich beider Comonomerer verfolgt. Mit steigendem Anteil des 12-Dodecanlactams im Ausgangsgemisch steigt der Gleichgewichtsgehalt an Copolymeren und zugleich sinkt die Copolymerisationsgeschwindigkeit. In der Anfangsphase der Copolymerisation nimmt der Gehalt an 12-Dodecanlactam im Reaktionsgemisch schnell ab, es wird jedoch nicht in das Copolymere direkt eingebaut, sondern über Oligomere, wahrscheinlich über ein cyclisches Dimeres. Für die äquimolare Zusammensetzung des Ausgangsgemisches wurde der Einfluß der Temperatur auf den Verlauf der Copolymerisation verfolgt. Es wurde festgestellt, daß die Copolymeren ab einer Polymerisationstemperatur von 260°C bei langfristigem Erhitzen abbauen, bei Temperaturen über 280°C stellt sich ein Abbau schon nach 50 h ein. Aus der Temperaturabhängigkeit wurde die scheinbare Aktivierungsenergie der Copolymerisation zu 62 kJ/mol ermittelt." @default.
- W4243445692 created "2022-05-12" @default.
- W4243445692 creator A5040028455 @default.
- W4243445692 creator A5081189405 @default.
- W4243445692 creator A5082540831 @default.
- W4243445692 creator A5084261149 @default.
- W4243445692 date "1982-03-17" @default.
- W4243445692 modified "2023-10-17" @default.
- W4243445692 doi "https://doi.org/10.1002/apmc.1982.051030109" @default.
- W4243445692 hasPublicationYear "1982" @default.
- W4243445692 type Work @default.
- W4243445692 citedByCount "1" @default.
- W4243445692 crossrefType "journal-article" @default.
- W4243445692 hasAuthorship W4243445692A5040028455 @default.
- W4243445692 hasAuthorship W4243445692A5081189405 @default.
- W4243445692 hasAuthorship W4243445692A5082540831 @default.
- W4243445692 hasAuthorship W4243445692A5084261149 @default.
- W4243445692 hasConcept C15920480 @default.
- W4243445692 hasConcept C178790620 @default.
- W4243445692 hasConcept C185592680 @default.
- W4243445692 hasConcept C188027245 @default.
- W4243445692 hasConcept C2779537395 @default.
- W4243445692 hasConcept C2779546866 @default.
- W4243445692 hasConcept C44228677 @default.
- W4243445692 hasConcept C521977710 @default.
- W4243445692 hasConcept C95121573 @default.
- W4243445692 hasConceptScore W4243445692C15920480 @default.
- W4243445692 hasConceptScore W4243445692C178790620 @default.
- W4243445692 hasConceptScore W4243445692C185592680 @default.
- W4243445692 hasConceptScore W4243445692C188027245 @default.
- W4243445692 hasConceptScore W4243445692C2779537395 @default.
- W4243445692 hasConceptScore W4243445692C2779546866 @default.
- W4243445692 hasConceptScore W4243445692C44228677 @default.
- W4243445692 hasConceptScore W4243445692C521977710 @default.
- W4243445692 hasConceptScore W4243445692C95121573 @default.
- W4243445692 hasIssue "1" @default.
- W4243445692 hasLocation W42434456921 @default.
- W4243445692 hasOpenAccess W4243445692 @default.
- W4243445692 hasPrimaryLocation W42434456921 @default.
- W4243445692 hasRelatedWork W1517987100 @default.
- W4243445692 hasRelatedWork W1944937360 @default.
- W4243445692 hasRelatedWork W1953528074 @default.
- W4243445692 hasRelatedWork W2056566734 @default.
- W4243445692 hasRelatedWork W2126688278 @default.
- W4243445692 hasRelatedWork W2155965899 @default.
- W4243445692 hasRelatedWork W2322310161 @default.
- W4243445692 hasRelatedWork W2392360665 @default.
- W4243445692 hasRelatedWork W2925275839 @default.
- W4243445692 hasRelatedWork W2949663163 @default.
- W4243445692 hasVolume "103" @default.
- W4243445692 isParatext "false" @default.
- W4243445692 isRetracted "false" @default.
- W4243445692 workType "article" @default.