- W4245582893 endingPage "535" @default.
- W4245582893 startingPage "535" @default.
- W4245582893 abstract "High frequency (80 Hz) fatigue tests have been conducted at ∼22°C on aged 8090 AlLi alloy plate in the as-received T8771 condition. Single edge notched specimens were used with a T-L orientation. Crack propagation rates were studied at an R-ratio of 0.5, under rising ΔK conditions, while testing in desiccated air and three freely corroding aqueous environments; distilled water, 0.6 M NaCl, and 1.0 M AlCl3. Particular attention was directed towards behavior near the cyclic crack rate threshold and in stage 1. The fatigue tests were supplemented by electrochemical potential studies and detailed fractographic observations using optical microscopy and scanning electron microscopy techniques. The major role of the aqueous environments was to promote S-L splitting (delamination) at grain boundaries, with a subsequent effect on the stress state at the crack tip. The lowestΔKth, 1.05MPa m12, was obtained in the AlCl3 solution and this environment caused sufficient splitting at the threshold that plane stress conditions played an important role in events at the crack tip. In all the other test environments, the ΔKth was ∼1.7 MPa m12, no splitting was present at the threshold and the crack tip was under plane strain conditions. Increasing the ΔK affected splitting in all the aqueous environments, producing a peak in the number of splits between 5 MPa m12and 6 MPa m12, and causing a sufficient amount of splitting that the crack tip was placed under plane stress conditions throughout Stage 2. Consistent with this, Stage 2 cyclic crack rates, da/dN, were very similar in all the aqueous environments, where they obeyed a power law relationship, da/dN∝(ΔK)4. In contrast, splitting effects were insignificant in desiccated air and the crack tip remained under plane strain conditions throughout the test, leading to out of plane cracking and ridge formation in the mid-thickness of the specimen, and resulting in severe growth retardation at ΔK values above ∼3.0 MPa m12. Analysis of the observations led to the conclusion that the S-L splitting phenomenon is associated with both localized anodic dissolution processes and hydrogen embrittlement effects, with solute segregation probably playing a contributory role." @default.
- W4245582893 created "2022-05-12" @default.
- W4245582893 date "1993-11-01" @default.
- W4245582893 modified "2023-09-25" @default.
- W4245582893 title "Effect of cycle mean strain on small crack growth in Alloy 718 at elevated temperatures" @default.
- W4245582893 doi "https://doi.org/10.1016/0142-1123(93)90364-v" @default.
- W4245582893 hasPublicationYear "1993" @default.
- W4245582893 type Work @default.
- W4245582893 citedByCount "0" @default.
- W4245582893 crossrefType "journal-article" @default.
- W4245582893 hasConcept C127313418 @default.
- W4245582893 hasConcept C138885662 @default.
- W4245582893 hasConcept C147789679 @default.
- W4245582893 hasConcept C151730666 @default.
- W4245582893 hasConcept C159985019 @default.
- W4245582893 hasConcept C162307627 @default.
- W4245582893 hasConcept C184651966 @default.
- W4245582893 hasConcept C185592680 @default.
- W4245582893 hasConcept C192562407 @default.
- W4245582893 hasConcept C21036866 @default.
- W4245582893 hasConcept C26771246 @default.
- W4245582893 hasConcept C2779429693 @default.
- W4245582893 hasConcept C2780026712 @default.
- W4245582893 hasConcept C28539199 @default.
- W4245582893 hasConcept C30239060 @default.
- W4245582893 hasConcept C41008148 @default.
- W4245582893 hasConcept C41895202 @default.
- W4245582893 hasConcept C43617362 @default.
- W4245582893 hasConcept C58097730 @default.
- W4245582893 hasConcept C59085676 @default.
- W4245582893 hasConcept C61039299 @default.
- W4245582893 hasConcept C75512024 @default.
- W4245582893 hasConcept C76155785 @default.
- W4245582893 hasConcept C77017923 @default.
- W4245582893 hasConcept C77928131 @default.
- W4245582893 hasConceptScore W4245582893C127313418 @default.
- W4245582893 hasConceptScore W4245582893C138885662 @default.
- W4245582893 hasConceptScore W4245582893C147789679 @default.
- W4245582893 hasConceptScore W4245582893C151730666 @default.
- W4245582893 hasConceptScore W4245582893C159985019 @default.
- W4245582893 hasConceptScore W4245582893C162307627 @default.
- W4245582893 hasConceptScore W4245582893C184651966 @default.
- W4245582893 hasConceptScore W4245582893C185592680 @default.
- W4245582893 hasConceptScore W4245582893C192562407 @default.
- W4245582893 hasConceptScore W4245582893C21036866 @default.
- W4245582893 hasConceptScore W4245582893C26771246 @default.
- W4245582893 hasConceptScore W4245582893C2779429693 @default.
- W4245582893 hasConceptScore W4245582893C2780026712 @default.
- W4245582893 hasConceptScore W4245582893C28539199 @default.
- W4245582893 hasConceptScore W4245582893C30239060 @default.
- W4245582893 hasConceptScore W4245582893C41008148 @default.
- W4245582893 hasConceptScore W4245582893C41895202 @default.
- W4245582893 hasConceptScore W4245582893C43617362 @default.
- W4245582893 hasConceptScore W4245582893C58097730 @default.
- W4245582893 hasConceptScore W4245582893C59085676 @default.
- W4245582893 hasConceptScore W4245582893C61039299 @default.
- W4245582893 hasConceptScore W4245582893C75512024 @default.
- W4245582893 hasConceptScore W4245582893C76155785 @default.
- W4245582893 hasConceptScore W4245582893C77017923 @default.
- W4245582893 hasConceptScore W4245582893C77928131 @default.
- W4245582893 hasIssue "6" @default.
- W4245582893 hasLocation W42455828931 @default.
- W4245582893 hasOpenAccess W4245582893 @default.
- W4245582893 hasPrimaryLocation W42455828931 @default.
- W4245582893 hasRelatedWork W2113653656 @default.
- W4245582893 hasRelatedWork W2126953240 @default.
- W4245582893 hasRelatedWork W226213227 @default.
- W4245582893 hasRelatedWork W2331523553 @default.
- W4245582893 hasRelatedWork W2389191516 @default.
- W4245582893 hasRelatedWork W2488669787 @default.
- W4245582893 hasRelatedWork W2548998242 @default.
- W4245582893 hasRelatedWork W2785225543 @default.
- W4245582893 hasRelatedWork W3010340056 @default.
- W4245582893 hasRelatedWork W2050670933 @default.
- W4245582893 hasVolume "15" @default.
- W4245582893 isParatext "false" @default.
- W4245582893 isRetracted "false" @default.
- W4245582893 workType "article" @default.