- W4255626552 abstract "Ni-Co alloy deposits were obtained by electroless plating from an acetate bath using dimethyl-amine borane at a rate of about 7μm/h at 60°C. Thallous nitrate was employed as a stabilizer of the bath. Under these conditions, both thallium and boron were co-deposited into Ni-Co alloys. It was, however, confirmed that boron content in the alloy deposit decreased significantly with an increase of thallous nitrate in the bath. Internal stress, electrical resistance and hardness of the alloy deposits were discussed on the basis of the composition of Ni-Co alloys. The internal stress of the Ni-Co alloy deposits seemed to decrease with a decrease in boron content of the alloys. The specific resistance of the Ni-Co alloy deposits as-plated was found to be 60-80μΩcm. However, it decreased to about 20μΩcm upon heat treatment at 400-600°C in vacuum. The hardness of the alloy deposits heat-treated at 400°C depended on boron content in the alloys; the higher boron content gave rise to the higher hardness of the alloy deposits up to that of hard chromium coatings." @default.
- W4255626552 created "2022-05-12" @default.
- W4255626552 creator A5024548415 @default.
- W4255626552 creator A5074770744 @default.
- W4255626552 creator A5086181386 @default.
- W4255626552 date "1980-01-01" @default.
- W4255626552 modified "2023-10-18" @default.
- W4255626552 doi "https://doi.org/10.4139/sfj1950.31.567" @default.
- W4255626552 hasPublicationYear "1980" @default.
- W4255626552 type Work @default.
- W4255626552 citedByCount "2" @default.
- W4255626552 crossrefType "journal-article" @default.
- W4255626552 hasAuthorship W4255626552A5024548415 @default.
- W4255626552 hasAuthorship W4255626552A5074770744 @default.
- W4255626552 hasAuthorship W4255626552A5086181386 @default.
- W4255626552 hasBestOaLocation W42556265521 @default.
- W4255626552 hasConcept C127313418 @default.
- W4255626552 hasConcept C178790620 @default.
- W4255626552 hasConcept C185592680 @default.
- W4255626552 hasConcept C191897082 @default.
- W4255626552 hasConcept C192562407 @default.
- W4255626552 hasConcept C2776985018 @default.
- W4255626552 hasConcept C2780026712 @default.
- W4255626552 hasConcept C501308230 @default.
- W4255626552 hasConcept C511782168 @default.
- W4255626552 hasConcept C8058405 @default.
- W4255626552 hasConceptScore W4255626552C127313418 @default.
- W4255626552 hasConceptScore W4255626552C178790620 @default.
- W4255626552 hasConceptScore W4255626552C185592680 @default.
- W4255626552 hasConceptScore W4255626552C191897082 @default.
- W4255626552 hasConceptScore W4255626552C192562407 @default.
- W4255626552 hasConceptScore W4255626552C2776985018 @default.
- W4255626552 hasConceptScore W4255626552C2780026712 @default.
- W4255626552 hasConceptScore W4255626552C501308230 @default.
- W4255626552 hasConceptScore W4255626552C511782168 @default.
- W4255626552 hasConceptScore W4255626552C8058405 @default.
- W4255626552 hasIssue "10" @default.
- W4255626552 hasLocation W42556265521 @default.
- W4255626552 hasOpenAccess W4255626552 @default.
- W4255626552 hasPrimaryLocation W42556265521 @default.
- W4255626552 hasRelatedWork W1989365426 @default.
- W4255626552 hasRelatedWork W1996331863 @default.
- W4255626552 hasRelatedWork W1999962534 @default.
- W4255626552 hasRelatedWork W2008100320 @default.
- W4255626552 hasRelatedWork W2323937902 @default.
- W4255626552 hasRelatedWork W2332122029 @default.
- W4255626552 hasRelatedWork W2371771324 @default.
- W4255626552 hasRelatedWork W2391593496 @default.
- W4255626552 hasRelatedWork W2811035334 @default.
- W4255626552 hasRelatedWork W4320525573 @default.
- W4255626552 hasVolume "31" @default.
- W4255626552 isParatext "false" @default.
- W4255626552 isRetracted "false" @default.
- W4255626552 workType "article" @default.