• W4280533933 abstract "The present work examined the influence of anion type on incorporating WO3 into the MgO layer produced via plasma electrolytic oxidation of AZ31 Mg alloy. Here, three different anions, such as aluminate (AlO2-), silicate (SiO32-), and phosphate (PO43-) were added separately into an alkaline electrolyte containing WO3 nanoparticles. The microstructural observations revealed that the incorporation of the WO3 nanoparticles is affected by the diameter of discharge channels associated with the type of anion added into the electrolyte. The sample produced from phosphate electrolytes had higher thickness but was more porous than those obtained in aluminate or silicate electrolytes. Regardless of anion type, the amounts of WO3 nanoparticles incorporated into the inner layer of PEO coating were more significant than those incorporated into the outer layer, where a WO3-rich inner layer was obtained in the case sample coated in electrolyte with silicate anions. The electrochemical measurements in a 3.5 wt% NaCl solution indicated that the corrosion resistance of the sample coated in silicate electrolyte was superior to other samples in which the sample coated in phosphate electrolyte exhibited the lowest corrosion resistance. This behavior is explained by a mechanism in which every anion produces its microstructural defects under the influence of discharge types, such as type-A, B, C, D, and E, thus, affecting the physical incorporation of WO3 into the MgO layer under plasma conditions." @default.
• W4280533933 created "2022-05-22" @default.
• W4280533933 creator A5006178080 @default.
• W4280533933 creator A5038971083 @default.
• W4280533933 creator A5049914952 @default.
• W4280533933 creator A5066918761 @default.
• W4280533933 creator A5070991414 @default.
• W4280533933 date "2022-09-01" @default.
• W4280533933 modified "2023-10-14" @default.
• W4280533933 title "Anionic assisted incorporation of WO3 nanoparticles for enhanced electrochemical properties of AZ31 Mg alloy coated via plasma electrolytic oxidation" @default.
• W4280533933 cites W1032395513 @default.
• W4280533933 cites W1984507607 @default.
• W4280533933 cites W2002984481 @default.
• W4280533933 cites W2007640445 @default.
• W4280533933 cites W2021612473 @default.
• W4280533933 cites W2022239886 @default.
• W4280533933 cites W2025116324 @default.
• W4280533933 cites W2049813294 @default.
• W4280533933 cites W2053864041 @default.
• W4280533933 cites W2053961256 @default.
• W4280533933 cites W2054393528 @default.
• W4280533933 cites W2083820617 @default.
• W4280533933 cites W2083919560 @default.
• W4280533933 cites W2091915471 @default.
• W4280533933 cites W2125804417 @default.
• W4280533933 cites W2298448213 @default.
• W4280533933 cites W2382726662 @default.
• W4280533933 cites W2439416609 @default.
• W4280533933 cites W2460729179 @default.
• W4280533933 cites W2517559575 @default.
• W4280533933 cites W2595237959 @default.
• W4280533933 cites W2615265211 @default.
• W4280533933 cites W2615990324 @default.
• W4280533933 cites W2722191726 @default.
• W4280533933 cites W2765243974 @default.
• W4280533933 cites W2903931082 @default.
• W4280533933 cites W2914696640 @default.
• W4280533933 cites W2943509548 @default.
• W4280533933 cites W2966185806 @default.
• W4280533933 cites W2999017188 @default.
• W4280533933 cites W3016893620 @default.
• W4280533933 cites W3026702211 @default.
• W4280533933 cites W3030663352 @default.
• W4280533933 cites W3035433222 @default.
• W4280533933 cites W3035643075 @default.
• W4280533933 cites W3048026772 @default.
• W4280533933 cites W3083010249 @default.
• W4280533933 cites W3087969441 @default.
• W4280533933 cites W3091188732 @default.
• W4280533933 cites W3093521648 @default.
• W4280533933 cites W3115755887 @default.
• W4280533933 cites W3135539911 @default.
• W4280533933 cites W3138310734 @default.
• W4280533933 cites W3158465803 @default.
• W4280533933 cites W3159524638 @default.
• W4280533933 cites W3165745957 @default.
• W4280533933 cites W3184465545 @default.
• W4280533933 cites W3184886784 @default.
• W4280533933 cites W3194591260 @default.
• W4280533933 cites W4200170574 @default.
• W4280533933 cites W4205554486 @default.
• W4280533933 cites W4206182806 @default.
• W4280533933 cites W4210733292 @default.
• W4280533933 cites W4213425735 @default.
• W4280533933 cites W4220883365 @default.
• W4280533933 cites W4224280383 @default.
• W4280533933 doi "https://doi.org/10.1016/j.jallcom.2022.165445" @default.
• W4280533933 hasPublicationYear "2022" @default.
• W4280533933 type Work @default.
• W4280533933 citedByCount "22" @default.
• W4280533933 countsByYear W42805339332022 @default.
• W4280533933 countsByYear W42805339332023 @default.
• W4280533933 crossrefType "journal-article" @default.
• W4280533933 hasAuthorship W4280533933A5006178080 @default.
• W4280533933 hasAuthorship W4280533933A5038971083 @default.
• W4280533933 hasAuthorship W4280533933A5049914952 @default.
• W4280533933 hasAuthorship W4280533933A5066918761 @default.
• W4280533933 hasAuthorship W4280533933A5070991414 @default.
• W4280533933 hasConcept C127413603 @default.
• W4280533933 hasConcept C147789679 @default.
• W4280533933 hasConcept C155672457 @default.
• W4280533933 hasConcept C171250308 @default.
• W4280533933 hasConcept C17525397 @default.
• W4280533933 hasConcept C179104552 @default.
• W4280533933 hasConcept C185592680 @default.
• W4280533933 hasConcept C191897082 @default.
• W4280533933 hasConcept C192562407 @default.
• W4280533933 hasConcept C20625102 @default.
• W4280533933 hasConcept C2777335606 @default.
• W4280533933 hasConcept C2777387946 @default.
• W4280533933 hasConcept C2777578362 @default.
• W4280533933 hasConcept C2779227376 @default.
• W4280533933 hasConcept C2780026712 @default.
• W4280533933 hasConcept C2781448156 @default.
• W4280533933 hasConcept C42360764 @default.
• W4280533933 hasConcept C523993062 @default.
• W4280533933 hasConcept C52859227 @default.
• W4280533933 hasConcept C68801617 @default.

• next