- W4281776369 abstract "In dental clinics, it is common to perform small fitting adjustments in dentures using a micro-grinding tool after testing them in the patient's mouth. This procedure increases local roughness and can lead to formation of microcracks on the prosthesis surface. This study aimed to investigate the benefits of a post-finishing heat treatment to surface roughness and crack healing and its effect on the flexural strength of lithium disilicate (LD) dental glass-ceramics. Commercially available lithium metasilicate, Li2SiO3, samples were heat treated at 840 °C for 7 min to induce the phase transformation into LD, Li2Si2O5. The LD samples were characterized by X-ray Diffraction, Scanning Electron Microscopy, Vickers hardness, Young’s modulus, and fracture toughness. One of the surfaces of the LD samples was sanded aiming to simulate the denture fitting adjustments performed in the dentist’s laboratory, generating a rough surface, Group 1. Half of the LD samples had their biaxial flexural strength evaluated by the piston-on-three-ball test (P–3B) and the other half were submitted to a second short-term heat treatment (840 °C - 5 min), Group 2, and later assessed by the P–3B. Roughness parameters in both groups were measured by 3D optical profilometry. After the crystallization heat treatment, formation of elongated LD crystals, Li2Si2O5, 35% amorphous phase, and residual Li3PO4 was observed. In addition, the following mechanical property values were obtained: Vickers hardness = 5.8 ± 0.1 GPa, fracture toughness = 2.2 ± 0.1 MPa m1/2, and Young’s modulus = 100.3 ± 0.3 GPa. The samples in Group 1 showed bending strength of 206 ± 30 MPa and the following roughness parameters: Ra = 0.45 ± 0.16 μm, Rz = 22.7 ± 6.7 μm, and PV = 27.7 ± 7.1 μm. In the samples in Group 2, the Ra, Rz and PV roughness parameters were 0.31 ± 0.12 μm, 5.2 ± 2.5 μm, and 9.2 ± 4.7 μm, respectively. With this decrease in roughness, the bending strength increased by 62%, with a mean value of 331 ± 59 MPa. In the need for machine finishing of LD-based glass-ceramic dental prostheses, the use of a second short-term heat treatment at 840 °C for 5 min generates considerable gains in bending strength, increasing the lifecycle of the prosthesis as a result of reduced surface roughness caused by softening of the remaining amorphous phase in the glass-ceramic. These conditions can be adapted to each chemical and crystallographic composition of the glass-ceramic under study." @default.
- W4281776369 created "2022-06-13" @default.
- W4281776369 creator A5002710873 @default.
- W4281776369 creator A5021332992 @default.
- W4281776369 creator A5046050500 @default.
- W4281776369 creator A5050201402 @default.
- W4281776369 creator A5064372256 @default.
- W4281776369 creator A5067278246 @default.
- W4281776369 date "2022-09-01" @default.
- W4281776369 modified "2023-10-12" @default.
- W4281776369 title "Effect of heat treatment on the roughness and mechanical properties of dental lithium disilicate glass-ceramics" @default.
- W4281776369 cites W1773950446 @default.
- W4281776369 cites W2016059534 @default.
- W4281776369 cites W2021652256 @default.
- W4281776369 cites W2032780914 @default.
- W4281776369 cites W2033303770 @default.
- W4281776369 cites W2045885437 @default.
- W4281776369 cites W2047400738 @default.
- W4281776369 cites W2055955464 @default.
- W4281776369 cites W2067618681 @default.
- W4281776369 cites W2087071170 @default.
- W4281776369 cites W2103242919 @default.
- W4281776369 cites W2104224578 @default.
- W4281776369 cites W2107220262 @default.
- W4281776369 cites W2142238393 @default.
- W4281776369 cites W2168745915 @default.
- W4281776369 cites W2175050105 @default.
- W4281776369 cites W2341383816 @default.
- W4281776369 cites W2511112452 @default.
- W4281776369 cites W2518583786 @default.
- W4281776369 cites W2555905352 @default.
- W4281776369 cites W2742586944 @default.
- W4281776369 cites W2791557063 @default.
- W4281776369 cites W2810245783 @default.
- W4281776369 cites W2897049770 @default.
- W4281776369 cites W2900822981 @default.
- W4281776369 cites W2921191046 @default.
- W4281776369 cites W2925247217 @default.
- W4281776369 cites W2952609200 @default.
- W4281776369 cites W2954118719 @default.
- W4281776369 cites W2973763114 @default.
- W4281776369 cites W2974821120 @default.
- W4281776369 cites W2977909593 @default.
- W4281776369 cites W3000428212 @default.
- W4281776369 cites W3004291752 @default.
- W4281776369 cites W3007998507 @default.
- W4281776369 cites W3110978917 @default.
- W4281776369 cites W3111322643 @default.
- W4281776369 cites W3173541782 @default.
- W4281776369 cites W3197399291 @default.
- W4281776369 cites W4200248336 @default.
- W4281776369 doi "https://doi.org/10.1016/j.ceramint.2022.05.314" @default.
- W4281776369 hasPublicationYear "2022" @default.
- W4281776369 type Work @default.
- W4281776369 citedByCount "2" @default.
- W4281776369 countsByYear W42817763692022 @default.
- W4281776369 countsByYear W42817763692023 @default.
- W4281776369 crossrefType "journal-article" @default.
- W4281776369 hasAuthorship W4281776369A5002710873 @default.
- W4281776369 hasAuthorship W4281776369A5021332992 @default.
- W4281776369 hasAuthorship W4281776369A5046050500 @default.
- W4281776369 hasAuthorship W4281776369A5050201402 @default.
- W4281776369 hasAuthorship W4281776369A5064372256 @default.
- W4281776369 hasAuthorship W4281776369A5067278246 @default.
- W4281776369 hasConcept C107365816 @default.
- W4281776369 hasConcept C133392424 @default.
- W4281776369 hasConcept C134132462 @default.
- W4281776369 hasConcept C159985019 @default.
- W4281776369 hasConcept C178405089 @default.
- W4281776369 hasConcept C192562407 @default.
- W4281776369 hasConcept C26771246 @default.
- W4281776369 hasConcept C2779989610 @default.
- W4281776369 hasConcept C43486711 @default.
- W4281776369 hasConcept C71039073 @default.
- W4281776369 hasConcept C87976508 @default.
- W4281776369 hasConcept C97549433 @default.
- W4281776369 hasConceptScore W4281776369C107365816 @default.
- W4281776369 hasConceptScore W4281776369C133392424 @default.
- W4281776369 hasConceptScore W4281776369C134132462 @default.
- W4281776369 hasConceptScore W4281776369C159985019 @default.
- W4281776369 hasConceptScore W4281776369C178405089 @default.
- W4281776369 hasConceptScore W4281776369C192562407 @default.
- W4281776369 hasConceptScore W4281776369C26771246 @default.
- W4281776369 hasConceptScore W4281776369C2779989610 @default.
- W4281776369 hasConceptScore W4281776369C43486711 @default.
- W4281776369 hasConceptScore W4281776369C71039073 @default.
- W4281776369 hasConceptScore W4281776369C87976508 @default.
- W4281776369 hasConceptScore W4281776369C97549433 @default.
- W4281776369 hasFunder F4320321868 @default.
- W4281776369 hasFunder F4320322025 @default.
- W4281776369 hasFunder F4320322749 @default.
- W4281776369 hasFunder F4320334779 @default.
- W4281776369 hasFunder F4320335322 @default.
- W4281776369 hasIssue "18" @default.
- W4281776369 hasLocation W42817763691 @default.
- W4281776369 hasOpenAccess W4281776369 @default.
- W4281776369 hasPrimaryLocation W42817763691 @default.
- W4281776369 hasRelatedWork W1841368884 @default.