- W4283017889 abstract "Over recent years, renewable energy technologies have focused on increasing performance and efficiency, and on the reduction of maintenance costs. In this work, thermal-sprayed Inconel 625 coatings have been studied as an alternative for concentrated solar power plants receivers. A low-power compact plasma spray system was used to deposit coatings onto two substrates: grade 22 ferritic steel and AISI 316 L austenitic steel. This system may be used for in-situ maintenance or repair purposes. The coatings were heat-treated at two temperatures: 520 °C and 800 °C, at different exposure times. The aim of this work was to evaluate the effect of this treatment on the adherence and solar absorptivity of the Inconel 625 coatings. The results showed that, at higher temperatures and longer exposure times, better adherence and absorptivity are achieved. Adherence values above 60 MPa were obtained due to diffusion in the coating-substrate interface. Additionally, absorptivity values above 93% were measured due to oxide formation on the coating surface during heat treatment. Furthermore, the highest temperature of the oxidized treatment reported the highest values of absorptivity. These results show that the developed Inconel 625 coatings could be considered as a possible alternative to improve the performance of concentrated solar power plants." @default.
- W4283017889 created "2022-06-18" @default.
- W4283017889 creator A5000504317 @default.
- W4283017889 creator A5007343997 @default.
- W4283017889 creator A5016072828 @default.
- W4283017889 creator A5082616080 @default.
- W4283017889 date "2022-09-01" @default.
- W4283017889 modified "2023-10-02" @default.
- W4283017889 title "Alternative low-power plasma-sprayed inconel 625 coatings for thermal solar receivers: Effects of high temperature exposure on adhesion and solar absorptivity" @default.
- W4283017889 cites W1482003025 @default.
- W4283017889 cites W1599526235 @default.
- W4283017889 cites W1765578890 @default.
- W4283017889 cites W1966368201 @default.
- W4283017889 cites W1967254160 @default.
- W4283017889 cites W1967627023 @default.
- W4283017889 cites W1979067849 @default.
- W4283017889 cites W1982258628 @default.
- W4283017889 cites W1985063637 @default.
- W4283017889 cites W1990617369 @default.
- W4283017889 cites W1991910199 @default.
- W4283017889 cites W2003246219 @default.
- W4283017889 cites W2017061536 @default.
- W4283017889 cites W203318023 @default.
- W4283017889 cites W2033363923 @default.
- W4283017889 cites W2038240860 @default.
- W4283017889 cites W2043719482 @default.
- W4283017889 cites W2054212529 @default.
- W4283017889 cites W2066947166 @default.
- W4283017889 cites W2084388468 @default.
- W4283017889 cites W2087475847 @default.
- W4283017889 cites W2108806206 @default.
- W4283017889 cites W2130715736 @default.
- W4283017889 cites W2144529492 @default.
- W4283017889 cites W2395755065 @default.
- W4283017889 cites W2517102336 @default.
- W4283017889 cites W2549290261 @default.
- W4283017889 cites W2551944653 @default.
- W4283017889 cites W2560405131 @default.
- W4283017889 cites W2599976895 @default.
- W4283017889 cites W2730958767 @default.
- W4283017889 cites W2744175552 @default.
- W4283017889 cites W2763133679 @default.
- W4283017889 cites W2792463320 @default.
- W4283017889 cites W2890617269 @default.
- W4283017889 cites W2907203607 @default.
- W4283017889 cites W2910057465 @default.
- W4283017889 cites W2940731362 @default.
- W4283017889 cites W2964431951 @default.
- W4283017889 cites W2965187498 @default.
- W4283017889 cites W2969734455 @default.
- W4283017889 cites W2987196329 @default.
- W4283017889 cites W3001039166 @default.
- W4283017889 cites W3003122306 @default.
- W4283017889 cites W3004606795 @default.
- W4283017889 cites W3008200312 @default.
- W4283017889 cites W3010930974 @default.
- W4283017889 cites W3012402311 @default.
- W4283017889 cites W3016679000 @default.
- W4283017889 cites W3082564117 @default.
- W4283017889 cites W3087046616 @default.
- W4283017889 cites W3096154121 @default.
- W4283017889 cites W3111070636 @default.
- W4283017889 cites W3133001369 @default.
- W4283017889 cites W3153287210 @default.
- W4283017889 cites W3198711663 @default.
- W4283017889 cites W3217407082 @default.
- W4283017889 cites W4206442632 @default.
- W4283017889 doi "https://doi.org/10.1016/j.solmat.2022.111839" @default.
- W4283017889 hasPublicationYear "2022" @default.
- W4283017889 type Work @default.
- W4283017889 citedByCount "6" @default.
- W4283017889 countsByYear W42830178892022 @default.
- W4283017889 countsByYear W42830178892023 @default.
- W4283017889 crossrefType "journal-article" @default.
- W4283017889 hasAuthorship W4283017889A5000504317 @default.
- W4283017889 hasAuthorship W4283017889A5007343997 @default.
- W4283017889 hasAuthorship W4283017889A5016072828 @default.
- W4283017889 hasAuthorship W4283017889A5082616080 @default.
- W4283017889 hasConcept C119599485 @default.
- W4283017889 hasConcept C120665830 @default.
- W4283017889 hasConcept C121332964 @default.
- W4283017889 hasConcept C127413603 @default.
- W4283017889 hasConcept C149669645 @default.
- W4283017889 hasConcept C159985019 @default.
- W4283017889 hasConcept C188573790 @default.
- W4283017889 hasConcept C191897082 @default.
- W4283017889 hasConcept C192562407 @default.
- W4283017889 hasConcept C20625102 @default.
- W4283017889 hasConcept C2776020425 @default.
- W4283017889 hasConcept C2778703219 @default.
- W4283017889 hasConcept C2779229422 @default.
- W4283017889 hasConcept C2780026712 @default.
- W4283017889 hasConcept C2781448156 @default.
- W4283017889 hasConcept C41291067 @default.
- W4283017889 hasConcept C541104983 @default.
- W4283017889 hasConcept C76046532 @default.
- W4283017889 hasConceptScore W4283017889C119599485 @default.
- W4283017889 hasConceptScore W4283017889C120665830 @default.