- W4285491638 abstract "Copper slag is a kind of huge metallurgical residue with fayalite as the main phase. Due to the oxidation of fayalite to quartz and hematite during sintering process, quartz became the main phase of ceramics when it contained large proportion of copper slag. The internal stress in the ceramic formed due to the change of α to β increases the potential risk of cracks in the quartz cooling process. In this paper, in order to reduce the precipitation of quartz phase, natural diopside rich in CaO and MgO was introduced into the copper slag-based ceramics. A batch of ceramics were prepared with 50 wt.% copper slag and 5 ~ 25 wt.% diopside as raw materials at different sintering temperatures. Evolution of crystals and densification process for the ceramics were investigated through physical property tests, including XRF, XRD, SEM, EDS and FACTSAGE calculation. The results indicated that fayalite particles derived from the slag formed a core-shell structure during the oxidation process, with the inner core dominated by silica and the outer shell enriched by iron oxide. It was observed that MgO and Fe2O3 reacted outside the shell to form mafic spinel (Fe, Mg) Fe2O4, which greatly promoted the reaction of Ca2+ with SiO2 in the core areas to form anorthite. As the amount of diopside increased, more mafic spinel and anorthite formed, while less quartz appeared. The addition of diopside to the ceramic body did not change its initial sintering temperature at 1170°C but significantly improved its bending strength from 35.8 MPa to 50.3 MPa with 5 ~ 20 wt.% addition of diopside, and more diopside would result in excessive flux and over firing." @default.
- W4285491638 created "2022-07-15" @default.
- W4285491638 creator A5035064562 @default.
- W4285491638 creator A5064965235 @default.
- W4285491638 creator A5078428128 @default.
- W4285491638 date "2022-07-15" @default.
- W4285491638 modified "2023-10-17" @default.
- W4285491638 title "Evolution of crystals in SiO<sub>2</sub>-Fe<sub>2</sub>O<sub>3</sub>-Al<sub>2</sub>O<sub>3</sub> system ceramics derived from copper slag" @default.
- W4285491638 cites W1975780735 @default.
- W4285491638 cites W2081159965 @default.
- W4285491638 cites W2141815319 @default.
- W4285491638 cites W2161778026 @default.
- W4285491638 cites W2549389087 @default.
- W4285491638 doi "https://doi.org/10.1080/21870764.2022.2083476" @default.
- W4285491638 hasPublicationYear "2022" @default.
- W4285491638 type Work @default.
- W4285491638 citedByCount "0" @default.
- W4285491638 crossrefType "journal-article" @default.
- W4285491638 hasAuthorship W4285491638A5035064562 @default.
- W4285491638 hasAuthorship W4285491638A5064965235 @default.
- W4285491638 hasAuthorship W4285491638A5078428128 @default.
- W4285491638 hasBestOaLocation W42854916381 @default.
- W4285491638 hasConcept C127313418 @default.
- W4285491638 hasConcept C134132462 @default.
- W4285491638 hasConcept C151730666 @default.
- W4285491638 hasConcept C159048435 @default.
- W4285491638 hasConcept C191897082 @default.
- W4285491638 hasConcept C192562407 @default.
- W4285491638 hasConcept C199289684 @default.
- W4285491638 hasConcept C2776230739 @default.
- W4285491638 hasConcept C2776994862 @default.
- W4285491638 hasConcept C2777018398 @default.
- W4285491638 hasConcept C2777581544 @default.
- W4285491638 hasConcept C2778189432 @default.
- W4285491638 hasConcept C2778993962 @default.
- W4285491638 hasConcept C2779131772 @default.
- W4285491638 hasConcept C2779870107 @default.
- W4285491638 hasConcept C2780364934 @default.
- W4285491638 hasConcept C544778455 @default.
- W4285491638 hasConcept C67236022 @default.
- W4285491638 hasConcept C93746451 @default.
- W4285491638 hasConceptScore W4285491638C127313418 @default.
- W4285491638 hasConceptScore W4285491638C134132462 @default.
- W4285491638 hasConceptScore W4285491638C151730666 @default.
- W4285491638 hasConceptScore W4285491638C159048435 @default.
- W4285491638 hasConceptScore W4285491638C191897082 @default.
- W4285491638 hasConceptScore W4285491638C192562407 @default.
- W4285491638 hasConceptScore W4285491638C199289684 @default.
- W4285491638 hasConceptScore W4285491638C2776230739 @default.
- W4285491638 hasConceptScore W4285491638C2776994862 @default.
- W4285491638 hasConceptScore W4285491638C2777018398 @default.
- W4285491638 hasConceptScore W4285491638C2777581544 @default.
- W4285491638 hasConceptScore W4285491638C2778189432 @default.
- W4285491638 hasConceptScore W4285491638C2778993962 @default.
- W4285491638 hasConceptScore W4285491638C2779131772 @default.
- W4285491638 hasConceptScore W4285491638C2779870107 @default.
- W4285491638 hasConceptScore W4285491638C2780364934 @default.
- W4285491638 hasConceptScore W4285491638C544778455 @default.
- W4285491638 hasConceptScore W4285491638C67236022 @default.
- W4285491638 hasConceptScore W4285491638C93746451 @default.
- W4285491638 hasFunder F4320335960 @default.
- W4285491638 hasLocation W42854916381 @default.
- W4285491638 hasLocation W42854916382 @default.
- W4285491638 hasOpenAccess W4285491638 @default.
- W4285491638 hasPrimaryLocation W42854916381 @default.
- W4285491638 hasRelatedWork W11858928 @default.
- W4285491638 hasRelatedWork W1551111093 @default.
- W4285491638 hasRelatedWork W1971721424 @default.
- W4285491638 hasRelatedWork W218471242 @default.
- W4285491638 hasRelatedWork W2192256204 @default.
- W4285491638 hasRelatedWork W2586201822 @default.
- W4285491638 hasRelatedWork W2911090760 @default.
- W4285491638 hasRelatedWork W2968594016 @default.
- W4285491638 hasRelatedWork W3111387391 @default.
- W4285491638 hasRelatedWork W3145537587 @default.
- W4285491638 isParatext "false" @default.
- W4285491638 isRetracted "false" @default.
- W4285491638 workType "article" @default.